本文選題：泡沫炭 + 酚醛樹脂��； 參考：《華東理工大學學報(自然科學版)》2017年04期

【摘要】：以高軟化點瀝青為原料,采用自發(fā)泡法制備泡沫炭,將其用作生物污水處理固菌載體材料,并通過添加適量的酚醛樹脂以提高泡沫炭的開孔率,進而提高其生物掛膜量。研究結(jié)果表明:當在高軟化點瀝青中添加酚醛樹脂的質(zhì)量分數(shù)為30%時,所制泡沫炭的開孔率高達100%,生物掛膜量(質(zhì)量分數(shù))達5.4%;當酚醛樹脂的添加質(zhì)量分數(shù)為40%時,所制泡沫炭的壓縮強度達5.2MPa,但其開孔率較低,孔結(jié)構(gòu)的均一性較差。
[Abstract]:Foamed carbon was prepared from asphalt with high softening point by spontaneous bubble method. It was used as the carrier material for biological wastewater treatment. By adding appropriate amount of phenolic resin, the open porosity of foamed carbon was increased and the amount of biofilm was increased. The results show that when the mass fraction of phenolic resin is 30, the porosity of foamed carbon is up to 100, and the amount of biofilm (mass fraction) reaches 5.4%, and when the added mass fraction of phenolic resin is 40? The compressive strength of the foamed carbon is 5.2 MPA, but the porosity is low and the homogeneity of pore structure is poor.
【作者單位】： 華東理工大學化學工程國家重點實驗室上海市多相結(jié)構(gòu)材料化學工程重點實驗室特種功能高分子材料及相關(guān)技術(shù)教育部重點實驗室;
【基金】：國家自然科學基金(51472086,51002051) 上海市自然科學基金(12ZR1407200)
【分類號】：TB383.4;TQ127.11

【相似文獻】

相關(guān)期刊論文 前10條

1 吳錫琪;;用氣體激光自動測定玻璃的軟化點[J];玻璃;1979年02期

2 ;科技簡訊[J];林化科技通訊;1982年02期

3 ;以α—蒎烯為原料的高軟化點聚萜烯(中試)通過鑒定[J];廣東化工;1982年01期

4 伍宏標;玻璃軟化點溫度的計算方法[J];玻璃;1988年01期

5 Т.Л.Молокова;由寶娣;;高軟化點瀝青基炭制品焙燒的研究[J];炭素技術(shù);1983年05期

6 霍華林;;縮短瀝青熬制周期[J];氯堿工業(yè);1982年06期

7 劉光彬;用玻璃物性配合化學分析控制成分和密度變化[J];玻璃;1992年03期

8 呂景文,郭國棟;L~2MCP可溶芯玻璃的研究[J];長春光學精密機械學院學報;1989年01期

9 伍洪標;玻璃軟化點溫度的簡易計算方法[J];玻璃與搪瓷;2004年04期

10 丁時炳;;關(guān)于炭素制品生產(chǎn)用瀝青[J];炭素技術(shù);1983年04期

，

本文編號：1950545