【摘要】：目的:觀察生物交聯(lián)劑京尼平預(yù)處理對牙本質(zhì)-樹脂粘結(jié)面即刻和老化后粘結(jié)強度的影響。方法:分別以蒸餾水、無水乙醇、無水丙酮液作為溶劑配置含京尼平濃度為0.05、0.10、0.15 mg/mL的預(yù)處理劑,并以純?nèi)軇┳鳛榭瞻讓φ?分別對酸蝕后的牙本質(zhì)粘結(jié)面進行預(yù)處理;然后用Z350納米復(fù)合樹脂制備牙本質(zhì)-樹脂粘結(jié)試件,用萬能測試機檢測各組牙本質(zhì)-樹脂粘結(jié)面的即刻和冷熱循環(huán)老化處理后的微拉伸粘結(jié)強度。結(jié)果:牙本質(zhì)粘結(jié)面經(jīng)不同溶劑配置的不同濃度京尼平預(yù)處理劑處理后,其牙本質(zhì)-樹脂粘結(jié)面的即刻微拉伸粘結(jié)強度(除0.05 mg/mL組外),均顯著高于相應(yīng)的溶劑對照組(P0.05),并且呈濃度依賴性增加;經(jīng)冷熱循環(huán)老化后,仍以0.1 mg/mL和0.15 mg/mL濃度的京尼平預(yù)處理組的微拉伸粘結(jié)強度顯著高于相應(yīng)的溶劑對照組(P0.05),各組老化后的微拉伸粘結(jié)強度均明顯低于其未經(jīng)老化處理的相應(yīng)組(P0.05)。結(jié)論:京尼平預(yù)處理可有效保護牙本質(zhì)-樹脂粘結(jié)界面,并能減緩其老化過程。
[Abstract]:Aim: to observe the effect of genipin pretreatment on the bonding strength of dentin-resin adhesive surface immediately and after aging. Methods: distilled water, anhydrous ethanol and anhydrous acetone solution were used as solvent to prepare the pretreatment agent containing 0. 05% 0. 1010 mg/mL of geniapine, and pure solvent was used as blank control. The dentin bonding surface after acid etching was pretreated respectively. Then the dentin-resin bonding specimens were prepared with Z350 nano-composite resin. The microtensile bond strength of each group of dentin-resin bonding surfaces was measured by universal testing machine. Results: after the dentin bonding surface was treated with different concentrations of genipin pretreatment with different solvents, the bonding strength of the dentin-resin bonding surface was immediately slightly tensile (except for 0.05 mg/mL group). All of them were significantly higher than the corresponding solvent control group (P0.05), and increased in a dose-dependent manner. The microtensile bond strength of the pretreatment group with 0. 1 mg/mL and 0. 15 mg/mL concentration was significantly higher than that of the solvent control group (P0.05). The microtensile bond strength of each group after aging was significantly lower than that of the corresponding group without aging (P0.05). Conclusion: geniapine pretreatment can effectively protect dentin-resin bonding interface and slow down the aging process.
【作者單位】： 第四軍醫(yī)大學(xué)口腔醫(yī)學(xué)院
【基金】：陜西省中醫(yī)藥管理局中醫(yī)藥課題(Lc71)
【分類號】：R783

【參考文獻】

相關(guān)期刊論文 前1條

1 金勛杰;閆景龍;周磊;姬燁;楊顯生;徐公平;;京尼平交聯(lián)明膠特性隨時間變化的研究[J];生物醫(yī)學(xué)工程學(xué)雜志;2008年01期

【共引文獻】

相關(guān)期刊論文 前3條

1 韓釗;劉興炎;厲孟;高秋明;李旭升;;載骨髓間充質(zhì)干細(xì)胞明膠微球的制備[J];軍醫(yī)進修學(xué)院學(xué)報;2012年05期

2 厲孟;劉旭東;劉興炎;;京尼平與戊二醛交聯(lián)明膠微球的性能比較[J];中國修復(fù)重建外科雜志;2009年01期

3 沙鑫家;王玉睿;周三玲;李娜;劉瑞瑞;;京尼平預(yù)處理對脫礦牙本質(zhì)膠原機械性能的影響[J];牙體牙髓牙周病學(xué)雜志;2014年08期

相關(guān)博士學(xué)位論文 前1條

1 厲孟;新型多孔自固化人工骨治療骨質(zhì)疏松骨缺損的實驗研究[D];第四軍醫(yī)大學(xué);2009年

相關(guān)碩士學(xué)位論文 前7條

1 李杰;明膠與改性明膠吸附/解吸水分的動力學(xué)研究[D];鄭州大學(xué);2010年

2 王莉莉;PP無紡布上功能分子的固定及其吸附性能研究[D];昆明理工大學(xué);2010年

3 占英英;可控制釋放微膠囊的制備和釋放性能研究[D];東北農(nóng)業(yè)大學(xué);2010年

4 韓釗;載骨髓間充質(zhì)干細(xì)胞磷酸鈣骨水泥的制備[D];第四軍醫(yī)大學(xué);2012年

5 馮瀚洲;兩種抗結(jié)核藥物的緩釋制劑研究與評價[D];北京協(xié)和醫(yī)學(xué)院;2012年

6 趙，

本文編號：2300432