【摘要】：背景:近來,氧化鋯陶瓷種植體開始被報道應用于臨床。為了促進種植體的骨結合,提高成功率,學者們對其表面處理作了很多研究,但目前尚無公認的氧化鋯種植體表面處理技術。目的:總結介紹氧化鋯種植體表面處理技術的研究進展。方法:由第一作者用計算機檢索相關期刊論文(CNKI:2000年1月至2016年10月),Pub Med和Web of Science數據庫(2000年1月至2016年10月),檢索詞為:氧化鋯、氧化鋯種植體、表面處理"和e treatment"zirconia or zirconium,implant,surfac",語言分別設定為中文和英文。對氧化鋯種植體表面處理的技術進行總結,對氧化鋯種植體的性質、表面處理技術和商品化情況等方面進行介紹。結果與結論:共納入23篇文章。結果表明,目前常見的氧化鋯種植體的表面處理技術有噴砂、酸蝕、噴砂酸蝕、選擇性滲透酸蝕、激光、紫外線和表面涂層處理,均都能一定程度地提高種植體表面活性,增大粗糙度,促進骨結合。但由于氧化鋯種植體的研究很有限,仍需要大量的實驗來探究最適宜的表面處理技術。
[Abstract]:Background: recently, zirconia ceramic implants have been reported for clinical use. In order to promote the bone bonding and improve the success rate, many scholars have done a lot of research on the surface treatment of the implant, but there is no recognized surface treatment technology of zirconia implant. Objective: to summarize the research progress of zirconia implant surface treatment. Methods: the full text databases of Chinese periodicals (CNKI: January 2000 to October 2016) were searched by the first author with the keywords of Zirconia, Zirconia implants, and the databases of Pub Med and Web of Science (January 2000 to October 2016). Surface treatment "and e treatment" zirconia or zirconia implantsurfac ", language set as Chinese and English, respectively." The surface treatment technology of zirconia implant was summarized. The properties, surface treatment technology and commercialization of zirconia implant were introduced. Results & conclusion: 23 articles were included. The results showed that the surface treatment techniques of zirconia implants, such as sand blasting, acid etching, sand blasting acid erosion, selective permeation acid etching, laser, ultraviolet radiation and surface coating treatment, could improve the surface activity of the implant to a certain extent. Increase roughness and promote bone bonding. However, due to the limited research of zirconia implants, a large number of experiments are needed to explore the most suitable surface treatment technology.
【作者單位】： 廣西醫(yī)科大學附屬口腔醫(yī)學院;
【基金】：國家自然科學基金資助項目(81260170) 廣西自然科學基金資助項目(604197919071)~~
【分類號】：R783

【相似文獻】

相關期刊論文 前8條

1 孟玉坤,王航;滲透陶瓷的表面處理與粘接[J];國外醫(yī)學.口腔醫(yī)學分冊;1998年04期

2 焦艷軍;王玨;潘福勤;;鈦及鈦合金種植體的兩種表面處理對細菌黏附能力的影響[J];中國藥物與臨床;2008年11期

3 程靜濤;牙科鈦鑄件的表面處理[J];生物醫(yī)學工程學雜志;1998年04期

4 趙永康;王秋旭;劉維賢;鄭彩云;李述軍;;氧化加堿處理Ti-24Nb-4Zr-7.9Sn合金表面的生物相容性研究[J];東南大學學報(醫(yī)學版);2007年04期

5 余粵海;翁達龍;邱小燕;張新薇;;不同表面處理的Br，

本文編號：2086428