【摘要】：Al-Zn-Mg-Cu合金密度小,比強(qiáng)度高,具有良好的加工性能,是現(xiàn)代航空航天武器裝備等領(lǐng)域發(fā)展的關(guān)鍵結(jié)構(gòu)材料。但是對于大型結(jié)構(gòu)件,該系鋁合金表現(xiàn)出一定的淬火敏感性。綜述了Al-Zn-Mg-Cu合金淬透性研究方法和影響該系鋁合金淬透性的因素。其中淬透性研究方法包括:端淬-硬度試驗(yàn)法測定鋁合金淬透層深度、TTP曲線、CCT曲線、TTT曲線、理論計(jì)算法以及計(jì)算機(jī)數(shù)值模擬法。并且從合金的化學(xué)成分、軋制制度、均勻化制度、淬火制度、時(shí)效制度和幾何尺寸等方面分析了影響淬透性的因素。
[Abstract]:Al-Zn-Mg-Cu alloys with low density, high specific strength and good processing properties are the key structural materials for the development of modern aerospace weapons and equipment. However, for large structural parts, the aluminum alloy shows a certain quenching sensitivity. The research methods of hardenability of Al-Zn-Mg-Cu alloy and the factors affecting the hardenability of the alloy are reviewed. The research methods of hardenability include the depth of quenched layer, TTP curve, CCT curve, TTT curve, theoretical calculation method and computer numerical simulation method. The factors affecting hardenability were analyzed from the aspects of chemical composition, rolling schedule, homogenization system, quenching system, aging system and geometric size of the alloy.
【作者單位】： 長沙理工大學(xué)汽車與機(jī)械工程學(xué)院;長沙理工大學(xué)工程車輛輕量化與可靠性技術(shù)重點(diǎn)實(shí)驗(yàn)室;
【基金】：湖南省自然科學(xué)基金(12JJ2023)
【分類號】：TG146.21

【參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 劉勝膽;張新明;黃振寶;;淬火速率對7055鋁合金組織和力學(xué)性能的影響[J];材料科學(xué)與工藝;2008年05期

2 趙中魁,周鐵濤,劉培英,陳昌麒;Al-Zn-Mg-Cu-Li-Er合金時(shí)效組織中Er相的TEM觀察[J];稀有金屬材料與工程;2004年10期

3 劉勝膽;張新明;游江海;張小艷;;微量鋯對7055型鋁合金淬火敏感性的影響[J];稀有金屬材料與工程;2007年04期

4 陳志國;楊文玲;王詩勇;舒軍;;微合金化鋁合金的研究進(jìn)展[J];稀有金屬材料與工程;2010年08期

5 李克生 ,田進(jìn)安;一種新型淬火介質(zhì)的應(yīng)用研究[J];國外金屬熱處理;2004年02期

6 張新明;歐陽惠;劉勝膽;吳澤政;王雷;周志樂;;固溶處理對Al-7.9Zn-2.5Mg-1.0Cu合金淬火敏感性的影響[J];材料研究學(xué)報(bào);2013年02期

7 張新明;余翠娟;劉勝膽;劉星興;張盼;王瑩瑩;;Fe和Si雜質(zhì)對Al-Zn-Mg-Cu合金淬火敏感性的影響[J];材料工程;2013年10期

8 劉勝膽;張新明;游江海;張小艷;張，

本文編號：2416924