本文選題：冷卻速率 + 力學(xué)性能　； 參考：《稀有金屬材料與工程》2015年08期

【摘要】：采用銅模吸鑄法制備了直徑分別為2、4、6 mm的Zr44Cu40Al8Ag8塊體非晶合金。利用X射線衍射儀(XRD)、光學(xué)顯微鏡(OM)、掃描電子顯微鏡(SEM)、透射電子顯微鏡(TEM)、同步示差掃描量熱儀(DSC)等手段對(duì)試樣的顯微結(jié)構(gòu)進(jìn)行了分析,采用單軸壓縮試驗(yàn)測(cè)試了試樣的力學(xué)性能。實(shí)驗(yàn)結(jié)果表明:試樣的力學(xué)性能受自由體積和析出晶體相數(shù)量影響。當(dāng)冷卻速率降低時(shí),試樣塑性因自由體積減少而變小,同時(shí)強(qiáng)度因Al3Zr析出相增多而降低。
[Abstract]:Zr44Cu40Al8Ag8 bulk amorphous alloy with a diameter of 2 ~ 4 ~ 6 mm was prepared by copper mould suction casting method. The microstructure of the samples was analyzed by means of X-ray diffractometer, optical microscope, scanning electron microscope (SEM), transmission electron microscope (TEM) and synchronous differential scanning calorimeter (DSCS). The mechanical properties of the samples were tested by uniaxial compression test. The experimental results show that the mechanical properties of the samples are affected by the free volume and the number of precipitated crystal phases. When the cooling rate decreases, the plasticity of the specimen decreases with the decrease of free volume, and the strength decreases with the increase of Al _ 3Zr precipitated phase.
【作者單位】： 蘭州理工大學(xué);
【基金】：國家自然科學(xué)基金資助(51061008)
【分類號(hào)】：TG139.8

【參考文獻(xiàn)】

相關(guān)期刊論文 前7條

1 楊英俊;邢大偉;王剛;孫劍飛;魏思東;沈軍;;銅基大塊非晶合金的壓縮斷裂行為[J];稀有金屬材料與工程;2007年06期

2 袁子洲;姚林;包石磊;王英君;;熔體冷速對(duì)Co_(48)Cr_(15)Mo_(14)C_(15)B_6Er_2塊體非晶合金晶化及磁性能的影響[J];稀有金屬材料與工程;2009年06期

3 張翠梅;惠希東;劉雄軍;陳國良;;高Cu高強(qiáng)Zr基塊體非晶合金的制備與力學(xué)性能(英文)[J];稀有金屬材料與工程;2008年02期

4 李杳奇;宋e，

本文編號(hào)：2008677