本文選題：集束拉拔技術(shù)　切入點(diǎn)：Nb管　出處：《稀有金屬材料與工程》2015年04期 　論文類型：期刊論文

【摘要】：采用集束拉拔技術(shù)制備出高強(qiáng)高導(dǎo)Nb管增強(qiáng)Cu-Nb多芯復(fù)合線材,樣品直徑為Φ2.5 mm時(shí),強(qiáng)度接近1.1 GPa,導(dǎo)電率達(dá)到74%IACS。選取不同尺寸線徑(Φ3.0 mm、Φ2.7 mm、Φ2.5 mm)的復(fù)合線材,通過場(chǎng)發(fā)射掃描電鏡測(cè)試手段表征了不同尺寸線材的芯絲形貌、Cu-Nb界面的微觀結(jié)構(gòu),探討了多尺寸條件下芯絲和界面微觀組織的演變規(guī)律及特性,最后結(jié)合σ-ε曲線圖和R-T曲線圖,詳細(xì)分析了尺寸變化所引起線材性能的演變機(jī)理。
[Abstract]:The high strength and high conductivity NB tube reinforced Cu-Nb multi-core composite wire was prepared by cluster drawing technique. When the diameter of the sample was 桅 2.5 mm, the strength was close to 1.1 GPa.The conductivity reached 74IACS.The composite wire with different sizes (桅 3.0 mm, 桅 2.7 mm, 桅 2.5 mm) was selected. The microstructure of Cu-Nb interface was characterized by means of field emission scanning electron microscopy (SEM). The evolution and characteristics of the microstructure of core wire and interface were discussed under multi-dimension conditions. Finally, the 蟽-蔚 curve and R-T curve were combined. The evolution mechanism of wire properties caused by dimension change is analyzed in detail.
【作者單位】： 西北有色金屬研究院;
【基金】：國(guó)家自然科學(xué)基金資助(51031002)
【分類號(hào)】：TG359

【參考文獻(xiàn)】

相關(guān)期刊論文 前4條

1 寧遠(yuǎn)濤;張曉輝;張婕;;大變形Cu-10Ag原位納米纖維復(fù)合材料[J];稀有金屬材料與工程;2005年12期

2 梁明;陳自力;盧亞鋒;李成山;閆果;李金山;張平祥;;高強(qiáng)高導(dǎo)銅鈮微觀復(fù)合材料的微觀結(jié)構(gòu)與性能[J];稀有金屬材料與工程;2009年10期

3 劉瑞蕊;周海濤;周嘯;陸德平;劉克明;彭謙之;彭勇;鐘芳華;;高強(qiáng)高導(dǎo)銅合金的研究現(xiàn)狀及發(fā)展趨勢(shì)[J];材料導(dǎo)報(bào);2012年19期

4 李春廣;孫霞光;鄧勝濤;管軍強(qiáng);肖成舉;萬曉波;朱思華;李建峰;杜社軍;王天成;張豐收;劉向宏;馮勇;;高場(chǎng)磁體用RRPNb_3Sn股線的研制[J];稀有金屬材料與工程;2012年08期

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 耿永紅;郭迎春;張吉明;劉方方;管偉明;張昆華;;大塑性變形金屬基納米纖維復(fù)合材料制備工藝與研究現(xiàn)狀[J];材料導(dǎo)報(bào);2007年08期

2 畢莉明;劉平;陳小紅;劉新寬;;形變銅基原位復(fù)合材料強(qiáng)化機(jī)理的研究進(jìn)展[J];材料導(dǎo)報(bào);2011年23期

3 寧遠(yuǎn)濤;張曉輝;吳躍軍;;Cu-Ag合金原位纖維復(fù)合材料的沉淀強(qiáng)化效應(yīng)[J];稀有金屬材料與工程;2007年10期

4 耿永紅;郭迎春;畢s，

本文編號(hào)：1636800