  本文選題：纖維增強水泥基復(fù)合材料 + 多縫開裂　； 參考：《公路工程》2014年03期

【摘要】：通過匯總和分析大量國內(nèi)外相關(guān)文獻(xiàn),對纖維增強水泥基復(fù)合材料開裂模型的發(fā)展進(jìn)行了綜述,并采用實測數(shù)據(jù)對J積分模型進(jìn)行了檢驗。結(jié)果表明,J積分法的推論與試驗測試結(jié)果基本一致,其推薦的兩個最小性能指標(biāo)可為高性能纖維增強水泥基復(fù)合材料的設(shè)計提供有效的指導(dǎo)。在未來的研究過程中還應(yīng)再建立一個反映裂縫飽和程度的指標(biāo),從而在設(shè)計階段就能對多縫開裂進(jìn)行全面控制。
[Abstract]:The development of crack model of fiber reinforced cement matrix composites was summarized by summarizing and analyzing a large number of related literatures at home and abroad. The J integral model was tested by the measured data. The results show that the corollary of the J integral method is basically consistent with the test results, and the two minimum performance indexes recommended by this method can provide effective guidance for the design of high performance fiber reinforced cement matrix composites. In the process of future research, a new index reflecting the degree of fracture saturation should be established, so that the multi-joint cracking can be controlled comprehensively in the design stage.
【作者單位】： 越秀(中國)交通基建投資有限公司;
【分類號】：U414

【參考文獻(xiàn)】

相關(guān)期刊論文 前3條

1 王曉剛;Folker.H.Wittmann;趙鐵軍;;優(yōu)化設(shè)計水泥基復(fù)合材料應(yīng)變硬化性能研究[J];混凝土與水泥制品;2006年03期

2 徐世p，

本文編號：2101126