【摘要】：以聚乙烯吡咯烷酮(PVP)作為成孔劑,丙酮和N,N-二甲基乙酰胺(DMAc)為溶劑,采用溶液相轉(zhuǎn)化法制備了皮層超薄且支撐層具有大量孔隙結(jié)構(gòu)的醋酸纖維素(CA)非均質(zhì)平板膜。對(duì)膜的純水通量、染料截留吸附性能進(jìn)行了考察,并通過(guò)場(chǎng)發(fā)射掃描電子顯微鏡對(duì)膜形貌進(jìn)行了表征,討論了成孔劑的含量對(duì)CA平板膜結(jié)構(gòu)與性能的影響。結(jié)果表明,當(dāng)CA質(zhì)量分?jǐn)?shù)8%,m(PVP)/m(CA)=23/100,V(溶劑丙酮)∶V(DMAc)=1∶1時(shí),制備的CA膜具有200nm的皮層結(jié)構(gòu),其純水通量可達(dá)230.75L/(m2·h),對(duì)染料截留率保持在97%以上。
[Abstract]:Using polyvinylpyrrolidone (PVP) as pore forming agent acetone and N-dimethyl acetamide (DMAC) as solvent a thin and porous cellulose acetate (CA) heterogeneous flat film was prepared by solution phase inversion method. The pure water flux and dye retention and adsorption properties of the membrane were investigated. The morphology of the membrane was characterized by field emission scanning electron microscope (SEM). The effect of the content of pore-forming agent on the structure and properties of CA flat membrane was discussed. The results show that when the CA mass fraction is 8%, the CA membrane has the cortical structure of 200nm, the pure water flux is up to 230.75L/(m2 HN, and the dye rejection rate is over 97%.
【作者單位】： 常州大學(xué)石油化工學(xué)院;
【基金】：國(guó)家自然科學(xué)基金青年基金資助項(xiàng)目(21404016;51103016) 生態(tài)紡織教育部重點(diǎn)實(shí)驗(yàn)室(江南大學(xué))(KLET1304) 江蘇省高校自然科學(xué)研究面上項(xiàng)目(15KJB430003)
【分類號(hào)】：TQ051.893

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 張亞彬;高小元;肖長(zhǎng)發(fā);;浸沒(méi)沉淀相轉(zhuǎn)化/燒結(jié)法制備鈉鈣硅玻璃平板膜[J];稀有金屬材料與工程;2013年S1期

2 劉桂香,栗廣勇,徐仁賢;用于分離 N_2-H_2的聚砜平板膜性能和結(jié)構(gòu)研究[J];膜科學(xué)與技術(shù);1991年Z1期

3 陸茵,胡少媚,顧熙棠,王剛明;科研用平板刮膜機(jī)[J];膜科學(xué)與技術(shù);2002年02期

4 ;[J];;年期

相關(guān)會(huì)議論文 前1條

1 張亞彬;高小元;肖長(zhǎng)發(fā);;煅燒對(duì)鈉鈣硅玻璃平板膜物相及微觀結(jié)構(gòu)的影響[A];第十七屆全國(guó)高技術(shù)陶瓷學(xué)術(shù)年會(huì)摘要集[C];2012年

，

本文編號(hào)：1854888