本文選題：正畸　切入點(diǎn)：粘結(jié)劑　出處：《浙江大學(xué)》2014年碩士論文

【摘要】：目的： 比較使用六種不同粘結(jié)劑在模擬口腔環(huán)境的體外實(shí)驗(yàn)中的抗剪切力的大小及粘結(jié)劑的牙表面殘余量。分析各種粘結(jié)劑的優(yōu)缺點(diǎn),為臨床正畸治療中粘結(jié)劑的選擇做參考。 方法： 選擇健康前磨牙60顆,隨機(jī)分為六組,分別使用Transbond XT光固化型樹(shù)脂粘結(jié)劑(美國(guó),3M)；非調(diào)拌型牙釉質(zhì)粘合樹(shù)脂(中國(guó),西湖巴爾)；光固化型牙釉質(zhì)粘合樹(shù)脂(中國(guó),西湖巴爾)；GC光固化型玻璃離子粘結(jié)劑(日本,富士)；Medicept光固化型樹(shù)脂粘結(jié)劑(英國(guó),Medicept); Prime-Dent光固化型樹(shù)脂粘結(jié)劑(美國(guó),Prime-Dent)等六種粘結(jié)劑嚴(yán)格按說(shuō)明書(shū)操作粘結(jié)托槽,置于37℃的人工唾液中24小時(shí)后,用測(cè)力儀以lmm/min的速度剪切下托槽,記錄最大力值算出粘結(jié)劑的抗剪切力強(qiáng)度,將所得數(shù)據(jù)用SPSS17.0統(tǒng)計(jì)軟件進(jìn)行分析,將卸載了托槽的牙面在10倍放大鏡下觀察殘留在牙釉質(zhì)上的粘結(jié)劑量,并進(jìn)行ARI評(píng)分,將結(jié)果進(jìn)行Kruskall-wallis H檢驗(yàn)。 結(jié)果： 單因素方差分析顯示各組間的粘結(jié)強(qiáng)度有顯著性差異(P0.05)；以TransbondXT光固化型樹(shù)脂粘結(jié)劑組為經(jīng)典標(biāo)準(zhǔn)參照,則GC光固化型玻璃離子粘結(jié)劑組和Prime-Dent光固化型樹(shù)脂粘結(jié)劑組與之存在顯著性差異(P0.05),粘結(jié)強(qiáng)度明顯不足,其余三組與之無(wú)顯著性差異；ARI評(píng)分結(jié)果進(jìn)行Kruskall-wallis H檢驗(yàn)顯示各組間無(wú)顯著性差異(P0.05) 結(jié)論： 雖然六種正畸粘結(jié)劑的粘結(jié)強(qiáng)度存在差異,但基本都能夠滿(mǎn)足正畸臨床工作的需要。Transbond XT光固化型樹(shù)脂粘結(jié)劑是穩(wěn)定可靠的正畸粘結(jié)劑。西湖巴爾非調(diào)拌型牙釉質(zhì)粘合樹(shù)脂及光固化型牙釉質(zhì)粘合樹(shù)脂粘結(jié)強(qiáng)度高,值得臨床推廣使用。
[Abstract]:Objective:The magnitude of shear stress and the residual amount of tooth surface of six different binders in simulated oral environment were compared.The advantages and disadvantages of various binders were analyzed to provide references for the selection of binders in orthodontic treatment.Methods:60 healthy premolars were randomly divided into six groups and treated with Transbond XT photocurable resin binder (USA), unmixed enamel adhesive resin (Xihu Barr, China), and light-cured enamel adhesive resin (China, China, China).Six kinds of glass-ion binders, such as Prime-Dent photocurable resin binder (Japan, Japan, Medicept photocurable resin binder), and Prime-Dent light-curable resin binder (Prime-Dent), are operated strictly according to instructions.After being placed in artificial saliva at 37 鈩，

本文編號(hào)：1719128