本文選題：YBCO高溫超導(dǎo)線圈 + 熱應(yīng)力��； 參考：《低溫與超導(dǎo)》2017年09期

【摘要】：主要研究由液氮與線圈溫差產(chǎn)生的熱應(yīng)力是否會破壞YBCO高溫超導(dǎo)線圈,從而為實際操作過程中線圈受力損壞的來源提供一定的參考。將多種環(huán)氧材料熱膨脹系數(shù)測試的結(jié)果用于仿真計算后,與相應(yīng)的YBCO帶材臨界應(yīng)力測試結(jié)果相比較,發(fā)現(xiàn)經(jīng)配置的環(huán)氧樹脂浸漬處理的線圈、液氮冷卻過程中產(chǎn)生的熱應(yīng)力不會破壞線圈。
[Abstract]:This paper mainly studies whether the thermal stress caused by the temperature difference between liquid nitrogen and coil will destroy YBCO high temperature superconducting coil, thus providing a certain reference for the source of coil force damage in practical operation. The test results of thermal expansion coefficient of various epoxy materials were applied to the simulation calculation, and compared with the results of the corresponding YBCO strip critical stress test, it was found that the collocated epoxy resin impregnated coil was found. The thermal stress generated during liquid nitrogen cooling does not destroy the coil.
【作者單位】： 中國科學(xué)院電工研究所;中國科學(xué)院大學(xué);中國科學(xué)院應(yīng)用超導(dǎo)重點實驗室;
【分類號】：TM26

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 玉燕;二硼化鎂超導(dǎo)線圈制造成功[J];金屬功能材料;2002年05期

2 ;大型鈮-鋁合金超導(dǎo)線圈在日本研制成功[J];國際電力;2003年01期

3 邵惠民,顏家烈;超導(dǎo)線圈中線材的磁化及其產(chǎn)生的影響[J];低溫與超導(dǎo);1984年02期

4 吳全興;純鈦管用于試驗超導(dǎo)線圈的開發(fā)[J];鈦工業(yè)進(jìn)展;2002年06期

5 李蘭凱;馮忠奎;程軍勝;倪志鵬;王秋良;;超導(dǎo)線圈的等效熱膨脹系數(shù)的理論與實驗研究[J];低溫工程;2013年02期

6 汪京榮;高溫超導(dǎo)線圈及在日本的應(yīng)用研究[J];稀有金屬快報;2000年05期

7 王曉磊;許皆平;崔健;;一種基于矢量變頻技術(shù)的超導(dǎo)線圈專用恒張力繞線機[J];低溫與超導(dǎo);2010年04期

8 李蘭凱;王厚生;倪志鵬;程軍勝;王秋良;;超導(dǎo)線圈繞制過程的力學(xué)行為研究[J];物理學(xué)報;2013年05期

9 張國民,林良真,肖立業(yè),宋乃浩,陳敏,余運佳;高溫超導(dǎo)線圈的交流損耗[J];低溫物理學(xué)報;2003年S1期

10 吳林濤;張軍朋;;超導(dǎo)線圈中的感應(yīng)電流[J];物理通報;2012年04期

相關(guān)博士學(xué)位論文 前1條

1 賴凌峰;高溫超導(dǎo)線圈穩(wěn)定性研究[D];清華大學(xué);2015年

相關(guān)碩士學(xué)位論文 前3條

1 任小龍;超導(dǎo)重力儀器中超導(dǎo)線圈有效電感與間距關(guān)系的研究[D];華中科技大學(xué);2016年

2 趙穎;高溫超導(dǎo)線圈交流損耗的分析與研究[D];北京交通大學(xué);2011年

3 李盼;Bi-2223超導(dǎo)線圈的設(shè)計研究[D];東北大學(xué);2012年

，

本文編號：2094498