【摘要】：采用溫軋加等溫?zé)崽幚砉に囍苽浼{米貝氏體鋼,研究了形變溫度對(duì)納米貝氏體相變速率的影響。結(jié)果表明,形變過冷奧氏體在503 K的貝氏體等溫轉(zhuǎn)變時(shí)間由常規(guī)等溫淬火的50 h縮短至20 h,納米貝氏體鋼的抗拉強(qiáng)度為2127 MPa、延伸率為4%。在實(shí)驗(yàn)溫度范圍內(nèi)進(jìn)行的過冷奧氏體形變均能促進(jìn)納米貝氏體相變,相變速率隨著形變溫度的降低而提高。過冷奧氏體形變量大于30%后殘余奧氏體組織明顯細(xì)化,塊狀殘余奧氏體全部轉(zhuǎn)變?yōu)楸∧�。溫軋工藝可在不惡化其它力學(xué)性能的前提下加速低溫貝氏體相變,從而縮短熱處理時(shí)間使生產(chǎn)成本降低。
[Abstract]:Nano-bainite steel was prepared by warm rolling plus isothermal heat treatment. The effect of deformation temperature on the transformation rate of nano-bainite was studied. The results show that the isothermal transformation time of deformed supercooled austenite at 503K is shortened from 50 h to 20 h, and the tensile strength of nano-bainite steel is 2127 MPa, elongation 4%. The supercooled austenite deformation in the experimental temperature range can promote the nano-bainite transformation, and the transformation rate increases with the decrease of the deformation temperature. After the supercooled austenite shape variable is more than 30%, the microstructure of retained austenite is refined obviously, and the bulk retained austenite is transformed into thin film shape. The warm rolling process can accelerate the transformation of bainite at low temperature without deterioration of other mechanical properties, thus shorten the heat treatment time and reduce the production cost.
【作者單位】： 北京科技大學(xué)冶金工程研究院;現(xiàn)代交通金屬材料與加工技術(shù)北京實(shí)驗(yàn)室;中國電力科學(xué)研究院;
【基金】：國家自然科學(xué)基金51271035和51371032資助項(xiàng)目~~
【分類號(hào)】：TG142.1;TG335

【參考文獻(xiàn)】

相關(guān)期刊論文 前1條

1 Yao Huang;Ai-min Zhao;Jian-guo He;Xiao-pei Wang;Zhi-gang Wang;Liang Qi;;Microstructure,crystallography and nucleation mechanism of NANOBAIN steel[J];International Journal of Minerals Metallurgy and Materials;2013年12期

【共引文獻(xiàn)】

相關(guān)期刊論文 前7條

1 易紅亮;陳蓬;王國棟;馬鳴圖;;δ-TRIP鋼的物理與力學(xué)冶金[J];中國工程科學(xué);2014年02期

2 任勇強(qiáng);陳二虎;宋婷婷;袁勝福;尚成嘉;;高延伸膨脹管用鋼的力學(xué)性能及微觀組織[J];鋼鐵;2014年04期

3 王長軍;雍岐龍;孫新軍;梁劍雄;;強(qiáng)塑積大于30 GPa·%的熱軋中碳TRIP鋼組織及性能研究[J];材料科學(xué)與工藝;2014年02期

4 Jing-jing Yang;Run Wu;Wen Liang;Meng-xia Tang;;Effect of nano-sized precipitates on the crystallography of ferrite in high-strength strip steel[J];International Journal of Minerals Metallurgy and Materials;2014年05期

5 劉慶鎖;袁連杰;高斌;楊巍巍;孟亮;;奧氏體化溫度對(duì)高碳含硅鋼等溫轉(zhuǎn)變的影響[J];鋼鐵;2014年07期

6 胡海江;徐光;劉峰;;超級(jí)貝氏體鋼相變的原位觀察研究[J];材料科學(xué)與工藝;2014年05期

7 吳化;張翠翠;梁言;劉云旭;;低合金超級(jí)貝氏體鋼組織形態(tài)的研究[J];材料科學(xué)與工藝;2014年05期

【二級(jí)參考文獻(xiàn)】

相關(guān)期刊論文 前5條

1 ;Precipitation and stability of reversed austenite in 9Ni steel[J];International Journal of Minerals Metallurgy and Materials;2010年05期

2 ;Grain refinement in the coarse-grained region of the heat-affected zone in low-carbon high-strength microalloyed steels[J];International Journal of Minerals Metallurgy and Materials;2010年06期

3 ;Effects of Si on the stability of retained austenite and temper embrittlement of ultrahigh strength steels[J];International Journal of Minerals Metallurgy and Materials;2011年05期

4 ;Microstructures and mechanical properties of C-Mn-Cr-Nb and C-Mn-Si-Nb ultra-high strength dual-phase steels[J];International Journal of Minerals Metallurgy and Materials;2012年10期

5 Ming Chang;Hao Yu;;Kinetics of bainite-to-austenite transformation during continuous reheating in low carbon microalloyed steel[J];International Journal of Minerals Metallurgy and Materials;2013年05期

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 趙四新;王巍;毛大立;;鋼中貝氏體相變研究新進(jìn)展[J];材料熱處理學(xué)報(bào);2006年04期

2 孟祥康，武小雷，，楊延清，張喜燕，康沫狂;貝氏體相變研究的某些進(jìn)展[J];金屬熱處理學(xué)報(bào);1995年01期

3 劉曉,鐘凡;貝氏體相變理論──兩個(gè)一級(jí)相變耦合的模型[J];金屬學(xué)報(bào);1999年11期

4 劉宗昌;鋼中貝氏體相變的論爭及前景[J];包頭鋼鐵學(xué)院學(xué)報(bào);2003年01期

5 劉宗昌;王海燕;任慧平;李文學(xué);;貝氏體相變特點(diǎn)的研究[J];材料熱處理學(xué)報(bào);2007年S1期

6 劉宗昌;計(jì)云萍;任慧平;;貝氏體相變理論研究新進(jìn)展[J];內(nèi)蒙古科技大學(xué)學(xué)報(bào);2012年01期

7 徐祖耀;貝氏體相變機(jī)制[J];材料科學(xué)進(jìn)展;1988年03期

8 徐祖耀;貝氏體相變研究的進(jìn)展[J];兵器材料科學(xué)與工程;1989年08期

9 徐祖耀;;鋼中貝氏體相變的先期效應(yīng)[J];上海金屬;1991年03期

10 孟祥康;康沫狂;楊延清;劉東慧;洪建明;劉治國;;β′→α_1型貝氏體相變初期的切變行為[J];自然科學(xué)進(jìn)展;1993年03期

相關(guān)會(huì)議論文 前2條

1 劉宗昌;王海燕;任慧平;李文學(xué);;貝氏體相變特點(diǎn)的研究[A];第九次全國熱處理大會(huì)論文集（二）[C];2007年

2 渠秀娟;李維娟;巨東英;;壓應(yīng)力對(duì)Cr-Mo鋼連續(xù)冷卻貝氏體相變的影響[A];第九次全國熱處理大會(huì)論文集（二）[C];2007年

相關(guān)碩士學(xué)位論文 前4條

1 段寶玉;鋼中貝氏體相變機(jī)理的研究[D];內(nèi)蒙古科技大學(xué);2009年

2 翟進(jìn)坡;Cr-Mo-V鋼形變奧氏體冷卻轉(zhuǎn)變及高壓下的貝氏體相變[D];燕山大學(xué);2009年

3 何p芾

本文編號(hào)：2461030