【摘要】：通過熔鹽向Al-4.5%Cu引入足量的鈉,研究鈉在Al-Cu合金中的存在形式以及對合金顯微組織和抗拉性能的影響。結果表明:鈉以單質形式存在于合金晶界中,這種鈉降低了基體和CuAl_2相之間的結合力。T6時效處理后,鈉導致了微觀裂紋的產生和CuAl_2相的殘留�？估瓕嶒灥慕Y果顯示鈉使得合金的斷裂方式由韌窩斷裂向晶間斷裂轉變,這導致了合金性能的急劇降低。
[Abstract]:The existence form of sodium in Al-Cu alloy and its effect on microstructure and tensile properties of Al-Cu alloy were studied by introducing sufficient amount of sodium into Al-4.5%Cu by molten salt. The results show that sodium exists in the grain boundary of the alloy in the form of single substance, which reduces the binding force between the matrix and CuAl_2 phase. After aging treatment with T6, sodium leads to the formation of microcracks and the residue of CuAl_2 phase. The results of tensile test show that the fracture mode of the alloy is changed from dimple fracture to intergranular fracture, which leads to a sharp decrease in the properties of the alloy.
【作者單位】： 山東大學材料液固結構演變與加工教育部重點實驗室;
【分類號】：TG146.21

【參考文獻】

相關期刊論文 前1條

1 孫寶德,丁文江,疏達,周堯和;Purification technology of molten aluminum[J];Journal of Central South University of Technology(English Edition);2004年02期

【相似文獻】

相關期刊論文 前10條

1 石德珂,劉軍海;高錳鋼的斷裂特性[J];兵器材料科學與工程;1989年10期

2 閻立珠;氣伐鋼的新熱處理法[J];熱加工工藝;1978年06期

3 ;"330"葉片生產技術總結 六、討論意見[J];大型鑄鍛件;1980年01期

4 張帆;趙建平;;內聚力單元在Voronoi元胞的晶間斷裂模擬中的應用[J];組合機床與自動化加工技術;2013年11期

5 R.J.Acuna;李溪濱;;6063鋁合金的斷裂行為——化學成分和時效狀態(tài)的影響[J];輕金屬;1985年04期

6 吳波;魏悅廣;譚建松;王建平;;納米晶Ni晶間斷裂的數(shù)值模擬[J];金屬學報;2009年09期

7 H.科迪埃;趙小兵;;可焊A1-Zn-Mg合金的顯微組織和晶間斷裂[J];國外艦船技術(材料類);1981年02期

8 陳升媛;;微量元素對鎳鉻鈰合金延性和斷裂的影響[J];上海金屬.有色分冊;1988年02期

9 朱彥生;;基于有限元模擬的納米晶Ni的晶間斷裂分析[J];鑄造技術;2014年07期

10 齊蕓馨，王玉忠，，夏建國，王改蓮;電渣熔鑄35CrNi3MoV鋼枝晶間斷裂的俄歇分析[J];鋼鐵;1996年06期

相關會議論文 前1條

1 劉新權;吳德振;楊恩超;蘇化冰;闞繼友;;熱處理工藝對X20Cr13葉片用鋼FATT_(50)和晶間斷裂的影響[A];中國動力工程學會透平專業(yè)委員會2012年學術研討會論文集[C];2012年

本文編號：2444743