【摘要】：采用恒流模式,通過單變量實驗改變電解液中乙酸鈣、六偏磷酸鈉和磷酸二氫鈉等鈣磷組分的濃度,在AZ31鎂合金表面制備微弧氧化生物陶瓷膜,觀察分析膜層微觀組織結(jié)構(gòu),測定膜層表面Ca/P比、耐蝕性等,探討鈣磷組分及其濃度對膜層組織和性能的影響,進而對電解液進行優(yōu)化,并對優(yōu)化后的膜層性能進行觀察和分析。結(jié)果表明:乙酸鈣、六偏磷酸鈉、磷酸二氫鈉對膜層Ca、P元素含量及Ca/P比值有決定作用;乙酸鈣濃度越高,膜層厚度越小,但是均一性越好;六偏磷酸鈉濃度對膜層表面形貌和厚度幾乎無影響,其濃度越高,膜層中P元素含量越高;磷酸二氫鈉濃度越高,Ca/P比值越小。電解液優(yōu)化后,制備的膜層較為平整致密,表面均勻分布10.7μm左右的微孔,但存在微裂紋;膜層主要由MgO、Mg和少量Ca2P2O7、SiO2等物相組成,使硬度和耐蝕性比鎂合金基體有明顯提高;膜層粗糙度Ra=0.45μm,潤濕角為42.65°,有利于細胞的附著與生長。
[Abstract]:The microarc oxidized bioceramic films were prepared on the surface of AZ31 magnesium alloys by changing the concentration of calcium acetate, sodium hexametaphosphate and sodium dihydrogen phosphate in the electrolyte by single variable experiment in constant current mode. The microstructure of the coatings was observed and analyzed. The surface Ca/P ratio and corrosion resistance of the film were measured. The effects of calcium and phosphorus components and their concentration on the structure and properties of the film were discussed. The electrolyte was optimized and the properties of the optimized film were observed and analyzed. The results showed that calcium acetate, sodium hexametaphosphate and sodium dihydrogen phosphate had a decisive effect on the content of Ca,P and the ratio of Ca/P, the higher the concentration of calcium acetate was, the smaller the thickness of the film was, but the better the uniformity was. The concentration of sodium hexametaphosphate had little effect on the surface morphology and thickness of the film. The higher the concentration of sodium hexametaphosphate was, the higher the content of P in the film was, and the higher the concentration of sodium dihydrogen phosphate was, the smaller the ratio of Ca/P was. After the electrolyte was optimized, the film was smooth and compact, and the surface of the film was evenly distributed about 10.7 渭 m of micropores, but there were microcracks. The hardness and corrosion resistance of the coating are mainly composed of MgO,Mg and a small amount of Ca2P2O7,SiO2. The roughness of the coating is Ra=0.45 渭 m and the wetting angle is 42.65 擄, which is beneficial to cell adhesion and growth.
【作者單位】： 江蘇科技大學(xué);
【基金】：江蘇高校優(yōu)勢學(xué)科建設(shè)工程資助項目(蘇政辦[2011]6) 江蘇省先進焊接技術(shù)重點實驗室資助項目(JSAWT-11) 江蘇省高校研究生科研創(chuàng)新計劃資助項目(2014-1081)
【分類號】：TG174.4

【參考文獻】

相關(guān)期刊論文 前10條

1 劉亮;郭鋒;李鵬飛;婭婭;;鈦生物種植體表面微弧氧化膜制備的電解液研究[J];表面技術(shù);2009年03期

2 劉亞萍;段良輝;潘俊德;崔彩娥;繆強;徐重;;鎂合金微弧氧化陶瓷膜的微觀結(jié)構(gòu)、相成分和耐腐蝕性能[J];材料保護;2006年02期

3 黃晶晶;楊柯;;鎂合金的生物醫(yī)用研究[J];材料導(dǎo)報;2006年04期

4 葛淑萍;王貴學(xué);沈陽;張勤;賈東煜;;鎂基合金應(yīng)用于生物醫(yī)用材料的研究進展[J];材料導(dǎo)報;2010年05期

5 張利;李玉寶;呂國玉;石浦江;;氧化鋅對納米羥基磷灰石/殼聚糖復(fù)合骨水泥理化性能的影響[J];功能材料;2006年12期

6 黃曉艷,周宏;21世紀綠色工程材料——Mg合金[J];南方金屬;2004年03期

7 王永偉;張永紅;;骨組織工程支架材料研究進展[J];山西醫(yī)藥雜志(下半月刊);2007年06期

8 馬威,時惠英,劉寶林,魏建華,封興華;成骨細胞在微弧氧化處理后純鈦表面的附著、增殖及ALP活性[J];實用口腔醫(yī)學(xué)雜志;2005年01期

9 張佳;宗陽;付彭懷;袁廣銀;丁文江;;鎂合金在生物醫(yī)用材料領(lǐng)域的應(yīng)用及發(fā)展前景[J];中國組織工程研究與臨床康復(fù);2009年29期

10 張榮發(fā);單大勇;陳榮石;韓恩厚;;電參數(shù)對鎂合金微弧氧化膜厚度的影響[J];中國有色金屬學(xué)報;2007年10期

【共引文獻】

相關(guān)期刊論文 前10條

1 王淑艷;夏永平;陸正萍;彭贊瑜;胡芮;;電解液組分對AZ91D鎂合金微弧氧化膜層耐蝕性的影響[J];中國表面工程;2011年05期

2 李勇;牛麗媛;高光亮;林繼興;劉蘭云;;微弧氧化工藝及封孔處理對鎂合金耐蝕性能的影響[J];表面技術(shù);2008年06期

3 閆鳳英;石玉龍;莫偉言;;氧化時間對鈦表面微弧氧化膜層的影響[J];表面技術(shù);2010年04期

4 章志友;趙晴;陳寧;;鎂合金微弧氧化膜相組成及結(jié)構(gòu)分析[J];材料保護;2008年03期

5 宋雨來;王文琴;劉耀輝;;鎂合金微弧氧化電解液體系及其添加劑的研究現(xiàn)狀與展望[J];材料保護;2010年11期

6 華e，

本文編號：2352475