【摘要】：對(duì)固溶時(shí)效處理后的高強(qiáng)高韌鈦合金初生α相的體積分?jǐn)?shù)、尺寸,次生α相的體積分?jǐn)?shù)和αs/β相界面密度等顯微組織特征進(jìn)行了定量表征和統(tǒng)計(jì)分析,探討了隨著固溶溫度的變化,高強(qiáng)高韌鈦合金顯微組織與其力學(xué)性能間的相關(guān)性.結(jié)果表明:在α+β兩相區(qū)固溶時(shí)效處理,隨著固溶溫度的升高,合金初生α相的體積分?jǐn)?shù)降低,相尺寸先降低后略有升高,次生α相的體積分?jǐn)?shù)升高,αs/β相界面密度先升高后降低.初生α相的體積分?jǐn)?shù)與伸長(zhǎng)率、靜力韌度和裂紋形成功正相關(guān),αs/β相界面密度與合金屈服強(qiáng)度成正相關(guān).
[Abstract]:The volume fraction and size of primary 偽 phase, volume fraction of secondary 偽 phase and interface density of 偽 s / 尾 phase of high strength and high toughness titanium alloy treated by solution aging treatment were quantitatively characterized and statistically analyzed. The correlation between microstructure and mechanical properties of high strength and high toughness titanium alloy was discussed with the change of solution temperature. The results show that the volume fraction of the primary 偽 phase decreases with the increase of the solution temperature, and the phase size decreases at first and then increases slightly after the aging treatment in the 偽 尾 two-phase region. The volume fraction of secondary 偽 phase increased and the interface density of 偽 s / 尾 phase increased first and then decreased. The volume fraction of primary 偽 phase is positively correlated with elongation, static toughness and crack shape, and the interface density of 偽 s / 尾 phase is positively correlated with the yield strength of the alloy.
【作者單位】： 上海飛機(jī)設(shè)計(jì)研究院;北京航空航天大學(xué)材料科學(xué)與工程學(xué)院;北京航空材料研究院;
【基金】：航空科學(xué)基金(2012ZEL056) 教育部長(zhǎng)江學(xué)者和創(chuàng)新團(tuán)隊(duì)發(fā)展計(jì)劃(IRT0805)
【分類(lèi)號(hào)】：TG166.5;TG146.23

【參考文獻(xiàn)】

相關(guān)期刊論文 前5條

1 王凱旋;曾衛(wèi)東;邵一濤;趙永慶;周義剛;;基于體視學(xué)原理的鈦合金顯微組織定量分析[J];稀有金屬材料與工程;2009年03期

2 曹春曉;;一代材料技術(shù),一代大型飛機(jī)[J];航空學(xué)報(bào);2008年03期

3 付艷艷;宋月清;惠松驍;米緒軍;葉文君;;熱處理對(duì)VST55531鈦合金的組織和拉伸性能的影響[J];稀有金屬;2008年04期

4 楊冬雨;付艷艷;惠松驍;葉文君;于洋;梁恩泉;;高強(qiáng)高韌鈦合金研究與應(yīng)用進(jìn)展[J];稀有金屬;2011年04期

5 付艷艷;惠松驍;葉文君;米緒軍;于洋;;冷卻速度對(duì)VST55531鈦合金的顯微組織和力學(xué)性能的影響[J];中國(guó)有色金屬學(xué)報(bào);2010年S1期

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 ;Application of the titanium alloy in civil aviation[J];Baosteel Technical Research;2011年04期

2 韓棟;張鵬省;毛小南;盧亞鋒;奚正平;楊建朝;;BT22鈦合金及其大型鍛件的研究進(jìn)展[J];材料導(dǎo)報(bào);2010年03期

3 鄒田春;馮振宇;陳兆晨;楊倩;;民機(jī)復(fù)合材料結(jié)構(gòu)適航審定現(xiàn)狀[J];材料導(dǎo)報(bào);2010年21期

4 邵暉;趙永慶;葛鵬;曾衛(wèi)東;楊義;王凱旋;單迪;;鍛造溫度場(chǎng)和應(yīng)變場(chǎng)對(duì)TC21鈦合金顯微組織的影響[J];材料導(dǎo)報(bào);2011年12期

5 秦冬陽(yáng);盧亞鋒;劉茜;周廉;;近β馬氏體鈦合金中的β→ω相變[J];材料導(dǎo)報(bào);2012年05期

6 張紀(jì)奎;程小全;酈正能;;基于損傷容限設(shè)計(jì)的機(jī)體金屬材料力學(xué)性能綜合表征與評(píng)價(jià)[J];材料工程;2010年07期

7 王凱旋;曾衛(wèi)東;趙永慶;邵一濤;周建華;王曉英;周義剛;;鈦合金片層α相在熱加工過(guò)程中演變規(guī)律的定量研究(英文)[J];稀有金屬材料與工程;2010年04期

8 商國(guó)強(qiáng);寇宏超;費(fèi)躍;常輝;朱知壽;王新南;張豐收;李金山;;時(shí)效工藝對(duì)Ti-10V-2Fe-3Al合金顯微組織和力學(xué)性能的影響[J];稀有金屬材料與工程;2010年06期

9 邵一濤;曾衛(wèi)東;韓遠(yuǎn)飛;周建華;王曉英;周義剛;;基于BP人工神經(jīng)網(wǎng)絡(luò)的TC17鈦合金顯微組織-力學(xué)性能關(guān)系預(yù)測(cè)[J];稀有金屬材料與工程;2011年02期

10 陳威;孫巧艷;肖林;孫軍;葛鵬;;時(shí)效工藝對(duì)Ti1023合金微觀組織和力學(xué)性能的影響[J];稀有金屬材料與工程;2011年04期

相關(guān)會(huì)議論文 前10條

1 付艷艷;惠松驍;葉文君;米緒軍;于洋;;用正交試驗(yàn)法優(yōu)化Ti-5Al-5Mo-5V-3Cr鈦合金的熱處理工藝[A];中國(guó)有色金屬學(xué)會(huì)第十四屆材料科學(xué)與合金加工學(xué)術(shù)年會(huì)論文集[C];2011年

2 張義長(zhǎng);楊加明;;黏彈性復(fù)合材料結(jié)構(gòu)阻尼性能優(yōu)化設(shè)計(jì)[A];經(jīng)濟(jì)發(fā)展方式轉(zhuǎn)變與自主創(chuàng)新——第十二屆中國(guó)科學(xué)技術(shù)協(xié)會(huì)年會(huì)（第二卷）[C];2010年

3 徐鋒;計(jì)波;朱益藩;羅月新;龐克昌;;加工工藝對(duì)Ti5553合金等溫鍛件力學(xué)性能和顯微組織的影響[A];第十四屆全國(guó)鈦及鈦合金學(xué)術(shù)交流會(huì)論文集（上冊(cè)）[C];2010年

4 雷力明;黃旭;黃利軍;曹春曉;;鑄態(tài)TB6鈦合金熱變形行為及本構(gòu)關(guān)系[A];第十四屆全國(guó)鈦及鈦合金學(xué)術(shù)交流會(huì)論文集（上冊(cè)）[C];2010年

5 王凱旋;曾衛(wèi)東;趙永慶;徐斌;田飛;朱艷春;張堯武;周義剛;;TC17鈦合金片層組織動(dòng)態(tài)球化的神經(jīng)網(wǎng)絡(luò)預(yù)測(cè)模型[A];第十四屆全國(guó)鈦及鈦合金學(xué)術(shù)交流會(huì)論文集（上冊(cè)）[C];2010年

6 曾衛(wèi)東;王凱旋;趙永慶;周建華;王曉英;徐斌;周義剛;;(α+β)兩相鈦合金顯微組織的定量分析和表征[A];第十四屆全國(guó)鈦及鈦合金學(xué)術(shù)交流會(huì)論文集（上冊(cè)）[C];2010年

7 劉翠云;李煥喜;馬朝利;;TC18鈦合金耳片的斷口形貌及疲勞性能[A];第十四屆全國(guó)鈦及鈦合金學(xué)術(shù)交流會(huì)論文集（下冊(cè)）[C];2010年

8 Linlin Li;Guoqing Wu;Changxu Liu;Aixue Sha;;Relationships between Spring-back and Microstructure of Ti-15V-3Cr-3Sn-3Al Titanium Alloy Sheet during Bending Process[A];中國(guó)材料大會(huì)2012第20分會(huì)場(chǎng)：先進(jìn)鈦合金材料技術(shù)與應(yīng)用論文集[C];2012年

9 Qiong Hui;Xiangyi Xue;Hongchao Kou;Minjie Lai;Bin Tang;Jinshan Li;;Phase Transformation and Microstructure Evolution in Near- β Ti-7333 Titanium Alloy During Aging[A];中國(guó)材料大會(huì)2012第20分會(huì)場(chǎng)：先進(jìn)鈦合金材料技術(shù)與應(yīng)用論文集[C];2012年

10 Xinnan Wang;Yue Fei;Xiaohu Zhou;Zhishou Zhu;Jun Li;Guoqiang Shang;Liwei Zhu;;Microstructure and Property of a New Metastable β Titanium Alloy[A];中國(guó)材料大會(huì)2012第20分會(huì)場(chǎng)：先進(jìn)鈦合金材料技術(shù)與應(yīng)用論文集[C];2012年

相關(guān)博士學(xué)位論文 前10條

1 李培躍;7050合金淬火敏感性及其機(jī)理研究[D];北京有色金屬研究總院;2011年

2 還大軍;復(fù)合材料自動(dòng)鋪放CAD/CAM關(guān)鍵技術(shù)研究[D];南京航空航天大學(xué);2010年

3 歐陽(yáng)德來(lái);TB6和TA15鈦合金β鍛組織演變及動(dòng)態(tài)再結(jié)晶行為研究[D];南京航空航天大學(xué);2011年

4 李友生;硬質(zhì)合金刀具與Ti-6Al-4V鈦合金的化學(xué)性能匹配研究[D];山東大學(xué);2010年

5 盧敏;復(fù)合材料構(gòu)件自動(dòng)鋪絲成型中的路徑生成算法研究[D];南京航空航天大學(xué);2011年

6 李成林;[D];北京有色金屬研究總院;2013年

7 宮新勇;激光熔覆沉積修復(fù)TC11鈦合金葉片的基礎(chǔ)問(wèn)題研究[D];北京有色金屬研究總院;2014年

8 李偉;鈦合金表面B_4C/G激光合金化層的組織與耐磨性研究[D];山東大學(xué);2014年

9 肖麗;熱連軋Ti-6Al-4V合金的力學(xué)、蠕變行為及微觀結(jié)構(gòu)表征[D];沈陽(yáng)工業(yè)大學(xué);2014年

10 宋奎晶;TA15鈦合金TIG焊熱影響區(qū)組織模擬及力學(xué)本構(gòu)關(guān)系研究[D];哈爾濱工業(yè)大學(xué);2014年

相關(guān)碩士學(xué)位論文 前10條

1 張選龍;碳纖維復(fù)合材料/鈦合金疊層裝配制孔技術(shù)研究[D];大連理工大學(xué);2010年

2 楊濤;高強(qiáng)鋁合金T型接頭激光焊接技術(shù)研究[D];武漢理工大學(xué);2011年

3 廖國(guó)防;航空接頭精密等溫鍛壓工藝仿真與實(shí)驗(yàn)研究[D];中南大學(xué);2011年

4 陳學(xué)海;7085鋁合金熱變形行為及加工圖研究[D];中南大學(xué);2011年

5 王志輝;Ti62421s高溫鈦合金組織性能的研究[D];中南大學(xué);2010年

6 寧勇;TC4鈦合金激光焊接焊縫預(yù)測(cè)與成形質(zhì)量分析[D];北京工業(yè)大學(xué);2011年

7 李紹淵;纖維金屬層壓板的應(yīng)力集中與疲勞裂紋擴(kuò)展研究[D];南京航空航天大學(xué);2011年

8 賈百芳;熱處理對(duì)TC18鈦合金顯微組織參數(shù)及力學(xué)性能的影響[D];西安建筑科技大學(xué);2011年

9 陳國(guó)珠;ZL114A鋁合金激光-電弧復(fù)合焊接頭組織分布與性能研究[D];華中科技大學(xué);2011年

10 趙穎;鈦合金蒙皮骨架激光焊接工藝與接頭性能研究[D];上海交通大學(xué);2012年

【二級(jí)參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 韓棟;張鵬省;毛小南;盧亞鋒;奚正平;楊建朝;;BT22鈦合金及其大型鍛件的研究進(jìn)展[J];材料導(dǎo)報(bào);2010年03期

2 陳慧琴;林好轉(zhuǎn);郭靈;曹春曉;;鈦合金熱變形機(jī)制及微觀組織演變規(guī)律的研究進(jìn)展[J];材料工程;2007年01期

3 賀金宇;李德富;陳海珊;沈建;趙云豪;;TB2合金鍛造工藝與組織性能的研究[J];稀有金屬材料與工程;2006年S2期

4 陳亞莉;;開(kāi)創(chuàng)復(fù)合材料應(yīng)用新時(shí)代——波音787飛機(jī)復(fù)合材料選材和制造工藝[J];國(guó)際航空;2007年08期

5 張紀(jì)奎;酈正能;程小全;王軍;;復(fù)合材料整體結(jié)構(gòu)在大型民機(jī)上的應(yīng)用[J];航空制造技術(shù);2007年09期

6 徐建林,陳超;材料顯微組織分析的研究[J];計(jì)量學(xué)報(bào);2004年04期

7 付艷艷;宋月清;惠松驍;米緒軍;;用正交試驗(yàn)法優(yōu)化VST55531鈦合金的熱處理工藝[J];金屬熱處理;2008年07期

8 Jéróme Pora;A380結(jié)構(gòu)的先進(jìn)材料和技術(shù)——未來(lái)發(fā)展的技術(shù)平臺(tái)[J];航空維修與工程;2003年06期

9 李文平;鈦合金的應(yīng)用現(xiàn)狀及發(fā)展前景[J];輕金屬;2002年05期

10 汪建林;高強(qiáng)度β鈦合金的發(fā)展和應(yīng)用[J];上海鋼研;2001年02期

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 剛建偉;韓小磊;李志輝;朱寶宏;張永安;;固溶時(shí)效處理對(duì)Al-6.6Zn-2.3Mg-2.1Cu-0.12Zr合金組織性能的影響[J];稀有金屬;2012年04期

2 賈玉鑫;黃金亮;馮劍;;固溶時(shí)效處理對(duì)軋制態(tài)Mg-12Li-2Al-1Zn合金組織與性能的影響[J];金屬熱處理;2014年01期

3 劉勁松;蒲玉興;;塑料模具鋼固溶時(shí)效處理及應(yīng)用[J];模具工業(yè);2009年08期

4 高紅選;古文全;吳建;郭光平;;固溶時(shí)效處理對(duì)鋁合金電阻率及力學(xué)性能的影響[J];熱加工工藝;2014年12期

5 張榮紅;蘭艷，

本文編號(hào)：2235330