【摘要】：對S30408奧氏體不銹鋼進行室溫應變強化,在深冷溫區(qū)(77K~4.2K)進一步時效處理,利用金相顯微鏡、X射線衍射儀(XRD)和透射電子顯微鏡(TEM)研究了應變誘發(fā)和熱誘發(fā)馬氏體相變的微觀特征,探討了馬氏體相變的微觀機理。結果表明:馬氏體相變的含量、微觀形貌、形核特征和位錯組態(tài)隨著預應變量的增加和溫度的降低而改變,且應變強化比溫度對相變的影響要大。誘發(fā)馬氏體與母相奧氏體的位相關系符合K-S關系,其相變的微觀機理為γ(fcc)→ε(hcp)、γ(fcc)→α'(bcc)、γ(fcc)→ε(hcp)→α'(bcc)、γ(fcc)→形變孿晶→α'(bcc)。
[Abstract]:S30408 austenitic stainless steel was strengthened by strain at room temperature. The microcosmic characteristics of strain induced and thermally induced martensite transformation were studied by means of metallographic microscope X-ray diffractometer (XRD) and transmission electron microscope (TEM). The microscopic mechanism of martensitic transformation was discussed. The results show that the content, morphology, nucleation characteristics and dislocation configuration of martensitic transformation change with the increase of prestrain variables and the decrease of temperature, and the effect of strain strengthening temperature is greater than that of temperature. The phase relationship between induced martensite and parent austenite accords with K-S relation. The microscopic mechanism of the phase transformation is 緯 (fcc) 蔚 (hcp), 緯 (fcc) 偽'(bcc), 緯 (fcc) 蔚 (hcp) 偽'(bcc), 緯 (fcc) Twin 偽'(bcc).
【作者單位】： 合肥工業(yè)大學材料科學與工程學院;合肥通用機械研究院國家壓力容器與管道安全工程技術研究中心安徽省壓力容器與管道安全技術重點實驗室;
【基金】：安徽省自然科學基金項目(1308085ME69) 安徽省重大科學儀器設備開發(fā)專項(1310115194) 合肥通用機械研究院青年科技基金(2013010646)
【分類號】：TG142.71

【參考文獻】

相關期刊論文 前1條

1 劉偉;李志斌;王翔;鄒驊;王立新;;應變速率對奧氏體不銹鋼應變誘發(fā)α′-馬氏體轉變和力學行為的影響[J];金屬學報;2009年03期

相關博士學位論文 前1條

1 韓豫;應變強化奧氏體不銹鋼制壓力容器工藝研究及其在典型介質環(huán)境中的性能評價[D];合肥工業(yè)大學;2012年

【共引文獻】

相關期刊論文 前10條

1 周勇;佘敏捷;劉家闊;;304不銹鋼馬氏體組織轉變探討[J];鋼鐵研究;2012年04期

2 宋仁伯;項建英;侯東坡;;316L不銹鋼冷變形加工硬化機制及組織特征[J];北京科技大學學報;2013年01期

3 李志峰;麻永林;馮巖;宮美娜;邢淑清;;神經(jīng)網(wǎng)絡在冷軋301S不銹鋼極薄帶材表面硬度預測中的應用[J];鋼鐵;2014年05期

4 史志剛;董紅年;李益民;王弘U，

本文編號：2229529