【摘要】：針對(duì)中國(guó)先進(jìn)研究堆(CARR)的特殊性,以靜態(tài)掛片實(shí)驗(yàn)與動(dòng)態(tài)模擬實(shí)驗(yàn)相結(jié)合,采用掛片失重的方法計(jì)算腐蝕速率,著重從Cl-、SO2-4、Mg2+和Ca2+濃縮比,pH值,緩蝕阻垢劑濃度等方面開展了碳鋼腐蝕影響因素的分析與研究。結(jié)果表明,在CARR二回路中,Cl-、SO2-4、Mg2+和Ca2+的濃縮比為2~3,pH值為8.0~8.5,緩釋阻垢劑LJ-301的濃度為0.12g/L左右的水質(zhì)為最佳狀態(tài),經(jīng)24h浸泡或循環(huán)水沖擊下,20#碳鋼的防腐效果明顯。
[Abstract]:In view of the particularity of (CARR) of China Advanced Research reactor, the corrosion rate is calculated by using the method of weightlessness of hanging sheet combined with static hanging sheet experiment and dynamic simulation experiment, especially from the pH value of Cl-,SO2-4,Mg2 and Ca2 concentration ratio. The factors affecting corrosion of carbon steel were analyzed and studied in the aspects of corrosion and scale inhibitor concentration. The results show that in the secondary loop of CARR, the concentration ratio of Cl-so _ 2-SO _ 4H _ 2mg _ 2 and Ca2 is 2 ~ (3) O ~ (3) pH = 8.0 ~ 8.5, and the best condition is that the concentration of LJ-301 is about 0.12g/L. The anticorrosive effect of 20 # carbon steel is obvious after 24 h immersion or circulatory water impact.
【作者單位】： 中國(guó)原子能科學(xué)研究院反應(yīng)堆工程研究設(shè)計(jì)所;
【分類號(hào)】：TL411;TG174

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 ;第47屆國(guó)際水會(huì)議(IWC)論文摘要[J];工業(yè)水處理;1989年03期

相關(guān)會(huì)議論文 前4條

1 馬娜;劉桂良;;FAC的研究歷程與工程應(yīng)對(duì)策略[A];中國(guó)核動(dòng)力研究設(shè)計(jì)院科學(xué)技術(shù)年報(bào)（2009）[C];2011年

2 王勇;周培德;楊勇;張強(qiáng);;池式鈉冷快堆二回路鈉比活度研究[A];中國(guó)原子能科學(xué)研究院年報(bào) 2009[C];2010年

3 趙亮;胡建群;吳志剛;王欣;;核電廠二回路管道流動(dòng)加速腐蝕管理[A];壓力容器先進(jìn)技術(shù)——第七屆全國(guó)壓力容器學(xué)術(shù)會(huì)議論文集[C];2009年

4 鐘志民;李勁松;鄭會(huì);;核電廠二回路汽水管道壁厚管理實(shí)踐與思考[A];中國(guó)核科學(xué)技術(shù)進(jìn)展報(bào)告（第二卷）——中國(guó)核學(xué)會(huì)2011年學(xué)術(shù)年會(huì)論文集第3冊(cè)（核能動(dòng)力分卷（下））[C];2011年

相關(guān)重要報(bào)紙文章 前1條

1 本報(bào)記者 張德斌;張國(guó)寶：我國(guó)核電項(xiàng)目安全性能有保證[N];中國(guó)證券報(bào);2011年

相關(guān)碩士學(xué)位論文 前1條

1 伊成龍;核電廠二回路管道流動(dòng)加速腐蝕性能研究[D];上海交通大學(xué);2012年

，

本文編號(hào)：2204180