【摘要】：通過蠕變性能測試和組織形貌觀察,研究了高鎢K416B鎳基合金高溫蠕變期間析出相的演化行為.結(jié)果表明,鑄態(tài)合金中g(shù)'相的尺寸不均勻,條狀MC碳化物在枝晶間區(qū)域呈漢字型分布;在施加應(yīng)力的高溫蠕變期間,細(xì)小M6C碳化物可在形變基體中不連續(xù)析出,熱力學(xué)分析認(rèn)為:在應(yīng)力誘導(dǎo)作用下,元素C偏聚在應(yīng)力集中處,與W等碳化物形成元素結(jié)合,促使細(xì)小M6C相自基體中析出;同時(shí),條狀MC碳化物表面形成溝槽,并逐漸分解蛻變成粒狀M6C相,其中,在條狀MC相表面形成的附加應(yīng)力是促使MC相不斷溶解和發(fā)生球化的主要原因.
[Abstract]:The evolution behavior of precipitated phase during high temperature creep during high temperature creep of high tungsten K416B nickel based alloy was studied by the creep properties test and microstructure observation. The results showed that the size of G'phase in the cast alloy was not uniform, the strip MC carbide was in the interdendritic region, and the fine M6C carbides could be in the deformation base during the high temperature creep of the stress. In the case of discontinuous precipitation in the body, the thermodynamic analysis shows that, under the stress induction, the element C is concentrated at the stress concentration and combines with the carbide forming elements such as W to precipitate the fine M6C phase from the matrix. At the same time, the surface of the strip MC carbide forms the groove and gradually decomposes and metamorphic into the granular M6C phase, in which the additional stress formed on the surface of the bar MC phase is formed. Force is the main reason for the continuous dissolution and spheroidization of MC.
【作者單位】： 中國科學(xué)院金屬研究所;
【基金】：國家重點(diǎn)基礎(chǔ)研究發(fā)展計(jì)劃項(xiàng)目2010CB631200和2010CB631206 國家自然科學(xué)基金項(xiàng)目50931004資助~~
【分類號(hào)】：TG132.3

【參考文獻(xiàn)】

相關(guān)期刊論文 前5條

1 何立子,孫曉峰,鄭啟,侯貴臣,張承忠,管恒榮,胡壯麒;高W型Ni基高溫合金M963中碳化物研究[J];材料工程;2004年02期

2 S.M.Seo;I.S.Kim;J.H.Lee;C.Y.Jo;H.Miyahara;K.Ogi;;Microstructural Evolution in Directionally Solidified Ni-Base Superalloy IN792+Hf[J];Journal of Materials Science & Technology;2008年01期

3 鄭亮,谷臣清,曾強(qiáng),侯淑娥;一種低Cr高W型鑄造鎳基高溫合金的顯微組織及其穩(wěn)定性[J];航空材料學(xué)報(bào);2004年01期

4 楊金俠;孫元;金濤;孫曉峰;胡壯麒;;一種細(xì)晶鑄造鎳基高溫合金的組織與力學(xué)性能[J];金屬學(xué)報(bào);2014年07期

5 肖旋;曾超;侯介山;秦學(xué)智;郭建亭;周蘭章;;定向凝固DZ444鎳基高溫合金初生MC碳化物的分解行為[J];金屬學(xué)報(bào);2014年09期

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 ;Effect of oxygen content and heat treatment on carbide precipitation behavior in PM Ni-base superalloys[J];International Journal of Minerals Metallurgy and Materials;2012年09期

2 ;Microstructure of Carbides at Grain Boundaries in Nickel Based Superalloys[J];Journal of Materials Science & Technology;2012年11期

3 趙坦;張健;陳光;樓瑯洪;;Re、Ta對第二代定向柱晶合金中初生碳化物形成與分解的影響[J];稀有金屬材料與工程;2009年06期

4 白坤;胡銳;李金山;周廉;;Ni-Cr-W基高溫合金近液相線細(xì)晶鑄造(英文)[J];稀有金屬材料與工程;2014年01期

5 馬文斌;劉國權(quán);胡本芙;胡鵬輝;張義文;劉建濤;;碳含量對熱等靜壓態(tài)FGH96合金碳化物的影響[J];稀有金屬材料與工程;2014年01期

6 Chuan-hui Chen;Yang Bai;Xu-chu Ye;;Effects of sintering temperature on the microstructural evolution and wear behavior of WCp reinforced Ni-based coatings[J];International Journal of Minerals Metallurgy and Materials;2014年12期

7 T.Liu;J.S.Dong;L.Wang;Z.J.Li;X.T.Zhou;L.H.Lou;J.Zhang;;Effect of Long-term Thermal Exposure on Microstructure and Stress Rupture Properties of GH3535 Superalloy[J];Journal of Materials Science & Technology;2015年03期

8 劉麗榮;金濤;孫曉峰;管恒榮;胡壯麒;;單晶高溫合金中的碳化物演化及其作用的研究[J];航空材料學(xué)報(bào);2007年05期

9 許文勇;李周;袁華;張勇;劉娜;張國慶;;噴射成形GH742y合金的碳化物相[J];航空材料學(xué)報(bào);2010年02期

10 姚志浩;董建新;張麥倉;于秋穎;鄭磊;;固溶溫度對GH864合金組織性能的影響[J];材料熱處理學(xué)報(bào);2011年07期

相關(guān)會(huì)議論文 前1條

1 W. Sun;X.Z. Qin;W. Wang;T.T. Wang;Y.A Guo;J.T. Guo;L.H Lou;L.Z. Zhou;;Effects of Nb/Ti Ratio on the Microstructures of Two Experimental Ni-based Cast Superalloys[A];中國材料大會(huì)2012第19分會(huì)場：高溫合金論文集[C];2012年

相關(guān)博士學(xué)位論文 前8條

1 肖旋;兩種高溫合金及NiAl共晶合金的顯微組織和力學(xué)性能[D];沈陽工業(yè)大學(xué);2007年

2 陳偉;高推重比航空發(fā)動(dòng)機(jī)整體精鑄燃燒室機(jī)匣用高強(qiáng)度高溫合金研究[D];南京理工大學(xué);2007年

3 趙坦;第二代定向柱晶高溫合金DZ59研究[D];南京理工大學(xué);2009年

4 吳文平;鎳基單晶高溫合金的界面微結(jié)構(gòu)及定向粗化行為分析[D];北京交通大學(xué);2010年

5 玄偉東;高溫合金定向凝固雜晶形成規(guī)律及其控制研究[D];上海大學(xué);2013年

6 彭黎;基于生態(tài)設(shè)計(jì)理念的鎳基單晶高溫合金中跡量摻雜元素的危害作用分析[D];湖南大學(xué);2012年

7 孫飛;鎳基單晶高溫合金中相界面的電子顯微學(xué)與第一性原理研究[D];山東大學(xué);2014年

8 田寧;長壽命服役條件下DZ125合金的蠕變行為及影響因素[D];沈陽工業(yè)大學(xué);2014年

相關(guān)碩士學(xué)位論文 前10條

1 趙永芹;類K445鎳基合金的制備及組織與性能研究[D];西安理工大學(xué);2007年

2 于忠鋒;高強(qiáng)抗熱腐蝕航空渦輪葉片材料（DZ68）的初步研制[D];大連理工大學(xué);2007年

3 趙唯;Ni基高溫合金的等離子體直接成型及其結(jié)構(gòu)、抗熱腐蝕性能研究[D];華中科技大學(xué);2006年

4 寧禮奎;四種鎳基高溫合金的抗熱腐蝕性能研究[D];大連理工大學(xué);2009年

5 趙卓;DZ792合金的恒溫氧化行為研究[D];東北大學(xué);2009年

6 王中原;GH5188合金組織與熱疲勞性能研究[D];沈陽理工大學(xué);2012年

7 楊光;Fe-15Al-10Nb自生復(fù)合材料及Ni-Cr-Mo基TiC增強(qiáng)復(fù)合熔覆層的組織與性能研究[D];華北電力大學(xué);2013年

8 王志國;精密鑄造K444高溫合金葉片鑄態(tài)組織及熱處理優(yōu)化研究[D];哈爾濱工業(yè)大學(xué);2013年

9 孔濤;鎳包覆Y_2O_3顆粒彌散強(qiáng)化鎳基高溫合金的制備及熱腐蝕行為研究[D];華中科技大學(xué);2013年

10 董亞嶺;渦輪增壓器傳動(dòng)軸摩擦焊界面特征與質(zhì)量控制[D];重慶大學(xué);2014年

【二級參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 金文中;李軍;李廷舉;殷國茂;;電磁場和表面孕育劑作用下K417高溫合金的晶粒細(xì)化[J];稀有金屬材料與工程;2008年06期

2 趙惠田,師昌緒;CoO孕育劑促進(jìn)鑄造鎳基高溫合金晶粒細(xì)化的研究[J];金屬學(xué)報(bào);1981年02期

3 鄭建邦,丁浩,郭益平,劉林,柳偉,李行健;Ni_xAl_yTi_z添加劑對K4169高溫合金鑄態(tài)晶粒組織的影響[J];金屬學(xué)報(bào);1998年04期

4 熊玉華,柳偉,楊愛民,張蓉,劉林;Ni-Al-Ti細(xì)化劑對K4169高溫合金鑄態(tài)組織及性能的影響[J];金屬學(xué)報(bào);1999年07期

5 彭志方,任遙遙,駱宇時(shí),燕平,趙京晨,王延慶;鎳基單晶合金CMSX-2高溫蠕變后的顯微組織及合金元素分布特征[J];金屬學(xué)報(bào);2002年02期

6 鄭運(yùn)榮,韓雅芳;燃?xì)鉁u輪用單晶高溫合金的成本因素[J];金屬學(xué)報(bào);2002年11期

7 秦學(xué)智;郭建亭;袁超;侯介山;周蘭章;葉恒強(qiáng);;兩種鑄造鎳基高溫合金在長期時(shí)效期間的微觀組織和力學(xué)性能演變[J];金屬學(xué)報(bào);2010年02期

8 桂忠樓;鎳基高溫合金B(yǎng)TOP工藝的發(fā)展[J];航空制造工程;1995年04期

9 邱華,錢翰城,Samir H Awad,吳仕明;K418高溫合金用鋁酸鈷晶粒細(xì)化劑的研制及應(yīng)用[J];鑄造技術(shù);2004年04期

10 周俊;謝發(fā)勤;吳向清;張軍;;DZ125高溫合金過冷凝固晶粒細(xì)化機(jī)制研究[J];鑄造;2009年07期

，

本文編號(hào)：2128902