【摘要】：為了研究Mg-Gd-Y鎂合金在高應(yīng)變速率下的動態(tài)拉伸性能及失效機制,采用分離式Hopkinson拉桿(SHTB)裝置在室溫下且應(yīng)變速率為1 400~3 000 s-1范圍內(nèi)對其進行了動態(tài)拉伸實驗,并利用光學(xué)顯微鏡和掃描電子顯微鏡對動態(tài)拉伸后的鎂合金試樣進行了分析.結(jié)果表明,在動態(tài)拉伸載荷作用下,Mg-Gd-Y鎂合金沿ED方向呈現(xiàn)連續(xù)屈服現(xiàn)象.應(yīng)變速率增大后,Mg-Gd-Y鎂合金具有正應(yīng)變速率效應(yīng).在動態(tài)拉伸載荷作用下,Mg-Gd-Y鎂合金的斷口形貌呈解理斷裂特征,鎂合金的變形方式為孿生和滑移,且滑移為主要變形方式.
[Abstract]:In order to study the dynamic tensile properties and failure mechanism of Mg-Gd-Y magnesium alloy at high strain rate, the dynamic tensile tests were carried out at room temperature with a strain rate of 1 400 ~ 3 000 s ~ (-1) in a split Hopkinson tension bar (SHTB) device. The dynamic tensile magnesium alloy samples were analyzed by optical microscope and scanning electron microscope. The results show that Mg-Gd-Y magnesium alloy exhibits continuous yield along Ed direction under dynamic tensile loading. Mg-Gd-Y magnesium alloy has positive strain rate effect when strain rate increases. The fracture morphology of Mg-Gd-Y magnesium alloy under dynamic tensile loading shows cleavage fracture characteristics. The deformation mode of Mg-Gd-Y magnesium alloy is twinning and slip, and slip is the main deformation mode.
【作者單位】： 沈陽工業(yè)大學(xué)材料科學(xué)與工程學(xué)院;
【基金】：國家重點基礎(chǔ)研究發(fā)展計劃(973計劃)資助項目(2013CB632205) 遼寧省科技攻關(guān)計劃資助項目(2013201018)
【分類號】：TG146.22

【相似文獻】

相關(guān)期刊論文 前3條

1 毛萍莉;于金程;劉正;董陽;席通;;擠壓態(tài)Mg-Gd-Y鎂合金動態(tài)壓縮力學(xué)性能與失效行為[J];中國有色金屬學(xué)報;2013年04期

2 桑英明;郭永春;李建平;段洪波;;Mg-Gd-Y系合金400℃平衡相圖的計算與驗證[J];熱加工工藝;2012年18期

3 ;[J];;年期

相關(guān)博士學(xué)位論文 前1條

1 姚素娟;Mg-Gd-Y（Sc）合金的制備技術(shù)和高溫性能研究[D];中南大學(xué);2009年

相關(guān)碩士學(xué)位論文 前3條

1 洪敏;Mg-Gd-Y系高強鎂合金熱機械加工工藝、組織及性能研究[D];沈陽航空航天大學(xué);2015年

2 周陽;表面激冷對Mg-Gd-Y合金的組織、力學(xué)和腐蝕性能的影響[D];上海交通大學(xué);2008年

3 梁曉鋒;Mg-Gd-Y基高強鎂合金組織及性能控制的基礎(chǔ)研究[D];重慶理工大學(xué);2012年

，

本文編號：2001121