本文選題：CuNiAlSi合金　切入點(diǎn)：等溫處理　出處：《中國有色金屬學(xué)報》2015年06期 　論文類型：期刊論文

【摘要】：通過等溫淬火方法獲得Cu-6.5Ni-1Al-1Si-0.15Mg-0.15Ce合金的TTP曲線。采用硬度、電導(dǎo)率測試和透射電鏡(TEM)觀察等方法研究了等溫溫度和等溫時間對合金性能和顯微組織的影響。結(jié)果表明:合金TTP曲線的鼻尖溫度約為675℃,淬火敏感區(qū)域為625~725℃;合金在650℃附近進(jìn)行等溫處理,δ-Ni2Si和共格的Ni3Al析出相的形核率和長大速率均很高;隨著等溫時間的延長,晶內(nèi)析出的δ-Ni2Si和Ni3Al急劇粗化,同時,晶界處發(fā)生δ-Ni2Si的不連續(xù)析出,并形成無襯度析出帶,導(dǎo)致合金經(jīng)等溫時效處理后硬度急劇下降,并且在鼻尖區(qū)具有很高的淬火敏感性。
[Abstract]:The TTP curves of Cu-6.5Ni-1Al-1Si-0.15Mg-0.15Ce alloy were obtained by isothermal quenching. The effects of isothermal temperature and isothermal time on the properties and microstructure of the alloy were studied by means of conductivity measurement and TEM observation. The results show that the nose tip temperature of the TTP curve of the alloy is about 675 鈩，