本文選題：B　切入點：H　出處：《稀有金屬材料與工程》2015年09期 　論文類型：期刊論文

【摘要】：采用光學(xué)顯微鏡、掃描電鏡、顯微硬度計等手段,研究了617B和740H管道氬弧焊接頭微觀組織和顯微硬度。結(jié)果表明:617B焊件焊縫晶粒外延生長明顯,焊縫主要存在Mo、Ti元素偏析,枝晶間分布著不連續(xù)顆粒狀碳化物M6C,焊縫硬度略高于母材。740H焊件焊縫主要存在Nb、Ti元素偏析,枝晶間有較多不規(guī)則顆粒狀碳化物MC,沒有觀察到γ-γ′共晶相;熱影響區(qū)晶粒稍有長大,晶內(nèi)強化相γ′減少,晶界碳化物M23C6和MC發(fā)生回溶,焊縫硬度明顯低于母材。
[Abstract]:The microstructure and microhardness of argon arc welding joints of 617B and 740H pipes were studied by means of optical microscope, scanning electron microscope and microhardness meter. There are discontinuous granular carbides M 6C distributed between dendrites, the hardness of weld is slightly higher than that of base metal. 740H welds are mainly segregated by NB Ti element, there are more irregular granular carbides MCs between dendrites, no 緯-緯 'eutectic phase is observed, and the grains in the heat affected zone grow slightly. With the decrease of 緯', the carbide M23C6 and MC of grain boundary are redissolved, and the hardness of weld is obviously lower than that of base metal.
【作者單位】： 北京科技大學(xué);
【基金】：國家高技術(shù)研究發(fā)展計劃(“863”計劃)(2012AA03A501)
【分類號】：TG407

【參考文獻】

相關(guān)期刊論文 前3條

1 毛健雄;;700℃超超臨界機組高溫材料研發(fā)的最新進展[J];電力建設(shè);2013年08期

2 王玨;吳峗;董建新;張麥倉;謝錫善;徐芳泓;;700℃超超臨界鍋爐材料GH4700合金鑄態(tài)組織及均勻化工藝[J];稀有金屬材料與工程;2013年09期

3 江河;董建新;張麥倉;姚志浩;;700℃超超臨界鍋爐材料617B合金鑄態(tài)組織及均勻化工藝[J];北京科技大學(xué)學(xué)報;2014年06期

【共引文獻】

相關(guān)期刊論文 前10條

1 柳郁;;超超臨界機組鍋爐高溫材料的選擇和應(yīng)用[J];科技創(chuàng)新與應(yīng)用;2014年20期

2 L.O.Osoba;A.K.Khan;S.O.Adeosun;;Cracking Susceptibility After Post-Weld Heat Treatment in Haynes 282 Nickel Based Superalloy[J];Acta Metallurgica Sinica(English Letters);2013年06期

3 朱朝暉;;大厚度比鎳基高溫合金構(gòu)件的焊接工藝[J];金屬功能材料;2013年06期

4 王東雷;;700℃高效超超臨界發(fā)電技術(shù)的研發(fā)現(xiàn)狀及建議[J];科技視界;2014年36期

5 吳，

本文編號：1640333