本文關鍵詞：電液顫振對6061鋁合金反擠壓成形過程的影響（英文）　出處：《Transactions of Nonferrous Metals Society of China》2015年09期 　論文類型：期刊論文

  更多相關文章： 鋁合金 傳統(tǒng)反擠壓 電液顫振輔助反擠壓 有限元分析 材料流動 應變分布

【摘要】：研究電液顫振技術在冷擠壓成形中應用的可行性。在室溫下對6061鋁合金坯料進行傳統(tǒng)反擠壓和電液顫振輔助反擠壓。實驗結果表明,給凹模施加頻率為100 Hz、幅值為0.013 mm的顫振,可使最大擠壓力下降5.65%。采用有限元軟件Deform模擬反擠壓過程,結果表明,在反擠壓過程中,顫振可使坯料與模具之間的摩擦因數(shù)從0.2下降為0.1,改變材料流動的方向及提高材料流動的瞬時速度,同時使坯料承受較小的最大塑性應變,其應變分布較傳統(tǒng)反擠壓更均勻。
[Abstract]:Study of electro-hydraulic flutter in the cold extrusion forming feasibility application. At room temperature for 6061 Aluminum Alloy billet extrusion and traditional electro-hydraulic flutter assisted extrusion. The experimental results show that the die is applied to a frequency of 100 Hz, 0.013 mm for flutter amplitude, the maximum pressure drop of 5.65%. finite element software Deform to simulate the process of backward extrusion. The results showed that in the backward extrusion process, flutter can make the friction coefficient between billet and die decreased from 0.2 to 0.1, changing the material flow direction and improve the instantaneous speed of material flow, while the blank for the maximum plastic strain is smaller, the strain distribution compared with the traditional anti extrusion more uniform.

【作者單位】： 浙江工業(yè)大學特種裝備制造與先進加工技術教育部/浙江省重點實驗室;金華職業(yè)技術學院機電工程學院;
【基金】：Project(51275475)supported by the National Natural Science Foundation of China Project(2014BY001)supported by the Department of Education in Zhejiang Province,China Project(2014EP0110)supported by the Key Laboratory of Special Purpose Equipment and Advanced Manufacturing Technology,Ministry of Education and Zhejiang Province,China
【分類號】：TG379
【正文快照】： 1 IntroductionVibration assisted metal forming is one of the mostrecent and beneficial process improvements in whichvibration is applied on the billet or the die to improveforming process because of the lower forming load,better surface qualities and hig

【參考文獻】

相關期刊論文 前3條

1 蔡改貧;姜志宏;;振動擺動輾壓成形實驗分析[J];中國機械工程;2010年14期

2 王志恒;楊慶華;胡新華;阮健;;顫振激勵下金屬冷擠壓成形降載特性[J];浙江大學學報(工學版);2014年11期

3 Ali KHOSRAVIFARD;Mohammad JAHEDI;Amir Hossein YAGHTIN;;1050鋁合金扭轉(zhuǎn)擠壓加工的3D有限元分析(英文)[J];Transactions of Nonferrous Metals Society of China;2012年11期

【共引文獻】

相關期刊論文 前10條

1 張勤儉;王會英;徐文勝;韓連江;劉成讓;;超聲擠壓強化技術的研究現(xiàn)狀及發(fā)展前景[J];電加工與模具;2013年06期

2 許忠斌;劉雨;鄭素霞;蘇良瑤;沈雪明;劉國林;;塑料振動加工與樣品成型一體化試驗機的研制[J];高分子材料科學與工程;2015年02期

3 劉暢;蘇言杰;王楠;趙波;劉璇;張亞非;;金剛石顆粒與硅基底的超聲焊接及場發(fā)射性能（英文）[J];微納電子技術;2015年02期

4 鄭建新;羅傲梅;;6061-T6鋁合金縱-扭復合振動超聲深滾加工試驗研究[J];稀有金屬材料與工程;2015年03期

5 牛榮軍;李文灑;康乃正;鄧四二;;汽車輪轂軸承單元軸端鉚合有限元分析[J];軸承;2015年04期

6 楊程;張敏娜;湯丹妮;張U，

本文編號：1441150