　　Ultrasonic vibration with different powers from 0 k W to 1.6 k W was applied during the tungsten inert gas welding-brazing of Mg/Ti.The microstructures,mechanical properties and corrosion resistance of the ultrasonic assisted tungsten inert gas（U-TIG） welded-brazed Mg/Ti joint were characterized.The results showed that,without being subjected to ultrasonic vibration,coarse columnar α-Mg grains occurred in the fusion zone of Mg/Ti joint.However,with ultrasonic power of 1.2 k W,the average grain s... 

【文章來源】：Journal of Materials Science & Technology. 2016,32(12)EISCICSCD

【文章頁數(shù)】：7 頁

【文章目錄】：
1. Introduction
2. Materials and Methods
3. Results and Discussion
    3.1. Microstructures of brazing zone
    3.2. Microstructures of fusion welding zone
    3.3. Mechanical properties
    3.4. Corrosion behaviors
4. Conclusions


【參考文獻(xiàn)】：
期刊論文
[1]TC4鈦/5052鋁異種金屬激光點(diǎn)焊工藝特性研究[J]. 孫逸銘,張澤群,檀財(cái)旺,趙曉葉,陳波,宋曉國,馮吉才.  激光與光電子學(xué)進(jìn)展. 2019(03)
[2]超聲振動(dòng)對高氮鋼激光-電弧復(fù)合焊接接頭組織與性能的影響研究[J]. 劉佳,白陳明,崔博,石巖,李忠,張宏.  機(jī)械工程學(xué)報(bào). 2018(16)
[3]熱輸入對鎂合金對焊接頭微觀組織和力學(xué)性能的影響（英文）[J]. 楊方洲,周杰,熊逸博.  Journal of Central South University. 2018(06)
[4]AZ31B/TC4填鎳夾層激光-電弧對接熔化焊特性[J]. 段旭,宋剛,劉黎明.  焊接技術(shù). 2018(04)
[5]鎂/鈦異種合金焊接的研究現(xiàn)狀與展望[J]. 張澤群,張凱平,檀財(cái)旺,周利,周珍珍.  焊接. 2017(11)

博士論文
[1]ZE41鎂合金薄壁鑄件集成計(jì)算及制備工藝研究[D]. 付玉.大連理工大學(xué) 2019

碩士論文
[1]面向散熱結(jié)構(gòu)的鎂/銅、鎂/鋁、鋁/鋁特種焊接工藝研究[D]. 牛田星.天津理工大學(xué) 2021
[2]復(fù)合微合金化及超聲處理對ZL101鋁合金組織與耐腐蝕性能的影響[D]. 董布克.合肥工業(yè)大學(xué) 2021
[3]Mg、Cu及Mg/Cu異種金屬超聲輔助釬焊工藝和機(jī)理研究[D]. 郎強(qiáng).天津理工大學(xué) 2020
[4]振動(dòng)處理工藝對鑄、焊件機(jī)械性能影響研究[D]. 孟祥旗.山東大學(xué) 2018
[5]高能噴丸對同種及異種金屬材料的TIG焊接接頭的組織和性能的影響[D]. 孫永強(qiáng).重慶大學(xué) 2018



本文編號：3626117