【摘要】：選用5種不同的時效溫度對擠壓成型的6082鋁合金殼體進(jìn)行了熱處理,并進(jìn)行了室溫條件下的力學(xué)試驗和磨損試驗。結(jié)果表明:隨時效溫度從130℃增至190℃,殼體力學(xué)性能和耐磨損性能均先提高后下降;與130℃時效相比,經(jīng)180℃時效使6082鋁合金殼體的抗拉強度提高17%,屈服強度提高25%,磨損體積減小47%,斷后伸長率從12.7%下降至9.6%。6082鋁合金殼體的時效溫度優(yōu)選為180℃。
[Abstract]:The extruded 6082 aluminum alloy shell was heat treated with 5 different aging temperatures, and the mechanical and wear tests were carried out at room temperature. The results showed that the temperature of instant effect increased from 130鈩，

本文編號：2513136