【摘要】：采用光學(xué)顯微鏡、掃描電鏡、拉伸試驗(yàn)和沖擊試驗(yàn)等方法研究了鐵塔用Q420B大規(guī)格角鋼的組織和性能。結(jié)果表明,Q420B角鋼組織為鐵素體+珠光體,晶粒尺寸細(xì)小、均勻。3種不同肢厚25~#Q420B角鋼的屈服強(qiáng)度為471~496 MPa,抗拉強(qiáng)度為617~627 MPa,伸長(zhǎng)率為23%~29%,沖擊韌性均達(dá)到國(guó)家標(biāo)準(zhǔn)規(guī)定的D級(jí)。
[Abstract]:The microstructure and properties of Q420B angle steel for iron tower were studied by means of optical microscope, scanning electron microscope, tensile test and impact test. The results show that the microstructure of Q420B angle steel is ferrite + pearlite with fine grain size and uniformity. The length is 23%~29%, and the impact toughness is up to D grade stipulated by the national standard.
【作者單位】： 華北理工大學(xué)冶金與能源學(xué)院;唐山鋼鐵有限公司技術(shù)中心;
【基金】：國(guó)家自然科學(xué)基金資助項(xiàng)目(51474092) 河北省高等學(xué)校創(chuàng)新團(tuán)隊(duì)領(lǐng)軍人才培育計(jì)劃(LJRC007) 河北省科技廳資助項(xiàng)目(E2013209228、12212122D) 唐山市科技計(jì)劃資助項(xiàng)目(14110201A)
【分類號(hào)】：TG142.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前2條

1 王德寶;王越;陳聯(lián)滿;崔磊;;Q420B角鋼腿部裂紋形態(tài)分析及成因探討[J];軋鋼;2010年01期

2 ;[J];;年期

相關(guān)會(huì)議論文 前1條

1 李永祥;李斌;張杰新;;Q420B角鋼釩氮微合金化工藝研究與開發(fā)[A];2012年全國(guó)煉鋼—連鑄生產(chǎn)技術(shù)會(huì)論文集（上）[C];2012年

，

本文編號(hào)：2210089