本文選題：激光技術(shù)　切入點(diǎn)：超疏水表面　出處：《激光與光電子學(xué)進(jìn)展》2017年09期

【摘要】：提出了一種利用納秒光纖激光快速制備超疏水鋁板表面的方法,對樣品表面的接觸角和粗糙度進(jìn)行了測量。烘烤處理激光加工后的樣品,得到了一系列具有不同潤濕性能的鋁板表面,增加激光能量密度可得到超疏水表面。研究結(jié)果表明,增加激光能量密度除了能提高鋁板表面的粗糙度,還會形成明顯的微納二級結(jié)構(gòu);空氣占鋁板超疏水復(fù)合接觸面總面積的90%以上;納秒激光誘導(dǎo)鋁板超疏水表面是微納結(jié)構(gòu)和化學(xué)成分共同作用的結(jié)果。
[Abstract]:A method for rapid preparation of superhydrophobic aluminum plate surface using nanosecond fiber laser was proposed. The contact angle and roughness of the surface of the sample were measured.A series of aluminum plate surfaces with different wetting properties were obtained by baking the samples processed by laser, and superhydrophobic surfaces were obtained by increasing the laser energy density.The results show that the increase of laser energy density can not only improve the surface roughness of aluminum plate, but also form an obvious micro-nano secondary structure, and the air accounts for more than 90% of the total area of superhydrophobic composite contact surface of aluminum plate.Nanosecond laser induced superhydrophobic surface of aluminum plate is the result of the interaction of micro-nano structure and chemical composition.
【作者單位】： 湖北工業(yè)大學(xué)機(jī)械工程學(xué)院;
【基金】：國家科技支撐計劃(2015BAF20B03) 國家自然科學(xué)基金(51405141) 湖北省科技支撐計劃(2015BAA066) 湖北省教育廳項目(Q20151404,T201405,D20161406) 湖北工業(yè)大學(xué)科研啟動金項目(337028)
【分類號】：TG665;TN249

【相似文獻(xiàn)】

相關(guān)期刊論文 前1條

1 ;鑿壁消音[J];大科技(科學(xué)之謎);2009年05期

相關(guān)碩士學(xué)位論文 前1條

1 李君神;切向氣流環(huán)境中激光輻照下薄鋁板響應(yīng)初步研究[D];國防科學(xué)技術(shù)大學(xué);2012年

，

本文編號：1723084