文獻名稱：氣流攪拌鎂合金半固態(tài)鑄造新技術(shù)

    前言：提出了吹氣鼓泡方式下產(chǎn)生的強對流、弱攪拌而獲得AZ91D鎂合金半固態(tài)組織的新工藝。研究了在不用攪拌溫度和冷卻介質(zhì)下吹氣鼓泡方式對半固態(tài)組織的影響。結(jié)果表明,吹氣攪拌溫度在600℃～610℃時,能夠獲得不同程度的半固態(tài)組織。對吹氣鼓泡方式下獲得鎂合金組織的機理作了初步分析,為進一步擴充研究該方法提供基礎(chǔ)。
    The new technique for agitating semi-solid magnesium alloy AZ91D slurry by gas blowing which create strong convection and weak agitation during solidification was put forward in this article.The effects of different agitating temperatures and molten Mg alloy cooling media on semi-solid microstructure were discussed.The results showed that AZ91D semi-solid microstructure by introducing Ar gas bubbles could be obtained at an agitating temperature between 600 ℃~610 ℃,and the mechanism of obtaining semi-solid M...

文獻名稱 氣流攪拌鎂合金半固態(tài)鑄造新技術(shù)

Article Name
英文(英語)翻譯 A New Casting Technique of Agitating Semi-Solid Magnesium Alloy Using a Gas Blowing Method;

作者 鄒瑩; 董選普; 張潔; 樊自田; 王愛華;

Author ZOU Ying;DONG Xuan-pu;ZHANG Jie;FAN Zi-tian;WANG Ai-hua（State Key Laboratory of Material Processing and Die & Mould Technology;Huazhong University of Science and Technology;Wuhan 430074;Hubei;China）;

作者單位
Author Agencies 華中科技大學材料成型及模具技術(shù)國家重點實驗室; 華中科技大學材料成型及模具技術(shù)國家重點實驗室 湖北武漢; 湖北武漢;

文獻出處
Article From 中國科學院上海冶金研究所; 材料物理與化學(專業(yè)) 博士論文 2000年度

關(guān)鍵詞 AZ91D鎂合金; 半固態(tài); 氣流攪拌法; 微觀組織;

Keywords AZ91D magnesium alloy;semi-solid;gas bubble method;microstructure;

AZ91D鎂合金表面機械研磨處理后顯微結(jié)構(gòu)研究
AZ91D鎂合金直接化學鍍鎳工藝研究
AZ91D鎂合金表面化學轉(zhuǎn)化處理及鍍鎳
激光熔覆AZ91D鎂合金的界面特征和耐磨性研究
AZ91D鎂合金表面磷化膜組織結(jié)構(gòu)與性能的研究
Al-8Ti-2C中間合金對AZ91D鎂合金的組織和性能的影響
以錫酸鈉為主鹽的AZ91D鎂合金化學轉(zhuǎn)化處理工藝
等溫熱處理對消失模鑄造AZ91D鎂合金組織與性能的影響
AZ91D鎂合金觸變鑄造件熱處理前后的組織與性能
觸變成形AZ91D鎂合金的組織與二次凝固行為

  本文關(guān)鍵詞：氣流攪拌鎂合金半固態(tài)鑄造新技術(shù)，由筆耕文化傳播整理發(fā)布。