Foamed glass-ceramics were prepared via a single-step sintering method using high-titanium blast furnace slag and waste glass as the main raw materials The influence of sintering temperature（900–1060℃） on the microstructure and properties of foamed glass-ceramics was studied. The results show that the crystal shape changed from grainy to rod-shaped and finally turned to multiple shapes as the sintering temperature was increased from 900 to 1060℃. With increasing sintering temperature, the averag... 

【文章來源】：International Journal of Minerals Metallurgy and Materials. 2017,24(08)

【文章頁數(shù)】：6 頁

【文章目錄】：
1. Introduction
2. Experimental
3. Results and discussion
    3.1. Thermal analysis of the mixture
    3.2. Effect of sintering temperature on the microstruc-ture of foamed glass-ceramics
    3.3. Effect of sintering temperature on the properties of foamed glass-ceramics
4. Conclusions


【參考文獻】：
期刊論文
[1]Effects of sphere size on the microstructure and mechanical properties of ductile iron–steel hollow sphere syntactic foams[J]. Hamid Sazegaran,Ali-Reza Kiani-Rashid,Jalil Vahdati Khaki.  International Journal of Minerals Metallurgy and Materials. 2016(06)
[2]Influence of aluminium nitride as a foaming agent on the preparation of foam glass-ceramics from high-titanium blast furnace slag[J]. Huan Shi,Ke-qin Feng,Hai-bo Wang,Chang-hong Chen,Hong-ling Zhou.  International Journal of Minerals Metallurgy and Materials. 2016(05)
[3]Effect of cooling rate on the crystallization behavior of perovskite in high titanium-bearing blast furnace slag[J]. Lu Liu,Mei-long Hu,Chen-guang Bai,Xue-wei Lü,Yu-zhou Xu,Qing-yu Deng.  International Journal of Minerals Metallurgy and Materials. 2014(11)
[4]Dissolution and diffusion of TiO2 in the CaO-Al2O3-SiO2 slag[J]. Zhong-shan Ren,Xiao-jun Hu,Xin-mei Hou,Xiang-xin Xue,Kuo-chih Chou.  International Journal of Minerals Metallurgy and Materials. 2014(04)
[5]Fabrication and properties of foam geopolymer using circulating fluidized bed combustion fly ash[J]. Ze Liu,Ning-ning Shao,Dong-min Wang,Jun-feng Qin,Tian-yong Huang,Wei Song,Mu-xi Lin,Jin-sha Yuan,Zhen Wang.  International Journal of Minerals Metallurgy and Materials. 2014(01)



本文編號：2976676