【摘要】：采用離子液體1-烯丙基-3-甲基氯化咪唑(AMI)改性白炭黑(SiO_2)。通過傅里葉紅外光譜(FT-IR),X射線衍射(XRD),X射線光電子能譜(XPS),熱失重分析儀(TGA),掃描電鏡(SEM),接觸角儀,BET比表面積和孔徑分析儀,對改性前后白炭黑的微觀結(jié)構(gòu)以及性能進行表征。結(jié)果表明,經(jīng)AMI改性后,白炭黑粒子間的相互作用明顯減小,團聚傾向減弱,在橡膠復合材料基體中的分散性提高。AMI改性白炭黑疏水性增強,接觸角由12.7°增加到80.5°,比表面積由67.84 cm2/g增加到124.28 cm2/g。改性前后,白炭黑晶型結(jié)構(gòu)變化不大,仍為無定形態(tài)。
[Abstract]:Silica (SiO_2) was modified by ionic liquid 1-allyl-3-methyl imidazole chloride (AMI). The microstructure and properties of silica before and after modification were characterized by Fourier transform infrared (FT-IR) X-ray diffraction (FT-IR) (XRD) X-ray photoelectron spectroscopy (XPS),) thermogravimetric analysis (TGA),) scanning electron microscope (SEM) (SEM), contact angle analyzer (SEM),) surface area and pore size analyzer. The results showed that the interaction between silica particles was obviously decreased and the agglomeration tendency was weakened after modified with AMI. The dispersion of silica modified by AMI was improved and the hydrophobicity of modified silica was enhanced. The contact angle increased from 12.7 擄to 80.5 擄, and the specific surface area increased from 67.84 cm2/g to 124.28 cm ~ 2 / g. Before and after modification, the crystal structure of silica changed little and remained amorphous.
【作者單位】： 貴州大學材料與冶金學院;貴州大學貴州省橡膠復合材料工程實驗室;
【基金】：國家自然科學基金(51663003) 貴州大學研究生教育創(chuàng)新基地(CXJD[2014]008)
【分類號】：TQ127.2

【相似文獻】

相關(guān)期刊論文 前7條

1 杜偉坊;杜海清;;高鋁質(zhì)電瓷材料的強度分散性研究[J];電瓷避雷器;1990年06期

2 余政厚;;泥漿細度瓷質(zhì)機械強度及其分散性與瓷質(zhì)顯微結(jié)構(gòu)的關(guān)系[J];電瓷避雷器;1991年03期

3 王平;;磁性氧化鐵懸浮體分散性的檢驗方法[J];實驗技術(shù)與管理;1990年03期

4 趙雪霞;李勇;宋靜靜;楊永珍;劉旭光;;氧化碳微球在溶液中分散性的pH值響應[J];化工新型材料;2013年02期

5 楊路;姜淑文;龐佳妮;王志強;林海;;商用聚羧酸類分散劑作用下Al_2O_3膠體的分散性表征與評價[J];中國陶瓷;2014年07期

6 趙多;孫本良;;不同分散劑對水熱法制備氧化鋯顆粒分散性的影響[J];遼寧科技大學學報;2014年02期

7 李永紅;;短纖維在水泥中的分散性[J];公路交通科技(應用技術(shù)版);2012年11期

相關(guān)碩士學位論文 前2條

1 劉明;鹵水制備阻燃級氫氧化鎂新工藝研究[D];北京化工大學;2016年

2 趙多;水熱合成法制備氧化鋯及分散性的研究[D];遼寧科技大學;2014年

，

本文編號：2169851