本文選題：無砂透水混凝土 + 荷葉疏水劑�。� 參考：《北華大學(xué)》2017年碩士論文

【摘要】：隨著城市化的推進(jìn),大面積的不透水性材料被應(yīng)用于城市的建設(shè),對生態(tài)環(huán)境造成嚴(yán)重危害。如熱島效應(yīng)、城市內(nèi)澇、地下水資源短缺、地面沉降和地表徑流污染等。透水混凝土是一種生態(tài)型環(huán)保混凝土,國外一些發(fā)達(dá)國家對其研究和應(yīng)用較早,在市政工程和園林工程中取得了良好的生態(tài)效益和社會效益。近年來,我國對透水混凝土的研究與應(yīng)用勢頭正熱,但是仍處于起步階段。本文將一種新型建筑涂料改性劑(荷葉疏水劑)引入到透水混凝土的研制之中。研究的主要內(nèi)容和成果如下:(1)應(yīng)用體積法進(jìn)行內(nèi)疏水透水混凝土配合比設(shè)計較為合適。(2)本研究采用經(jīng)驗(yàn)法與維勃稠度法相結(jié)合的方法,能較為準(zhǔn)確的對透水混凝土工作性進(jìn)行評價。(3)添加荷葉疏水劑后,透水混凝土強(qiáng)度有一定提高,最多可提高38%。(4)依據(jù)孔隙率、水灰比、疏水劑摻量和骨料類型對透水混凝土的強(qiáng)度和透水系數(shù)兩方面的影響規(guī)律,推薦內(nèi)疏水透水混凝土的目標(biāo)孔隙率為20%,水灰比在0.24~0.28之間,荷葉疏水劑摻量為4%,骨料粒徑為9.5~11.5mm。(5)制備出了抗壓強(qiáng)度為28.7Mpa,透水系數(shù)為4.11mm/s,抗折強(qiáng)度為4.47Mpa的內(nèi)疏水透水混凝土。(6)利用自制的透水儀對透水系數(shù)進(jìn)行了測試,建立了透水系數(shù)與有效孔隙率的關(guān)系式,并推導(dǎo)出當(dāng)有效孔隙率大于23.8%后,內(nèi)疏水透水混凝土的透水系數(shù)將超過未添加疏水劑的透水混凝土。(7)內(nèi)疏水透水混凝土微觀結(jié)構(gòu)更加致密,并且具有均勻的蠟質(zhì)小凸起,形成荷葉疏水效果,與本文理論研究相一致。
[Abstract]:With the development of urbanization, a large area of impermeable materials have been used in urban construction, causing serious harm to the ecological environment. Such as heat island effect, urban waterlogging, groundwater shortage, land subsidence and surface runoff pollution. Permeable concrete is an ecotypic environment-friendly concrete, which has been studied and applied earlier in some developed countries, and has achieved good ecological and social benefits in municipal engineering and garden engineering. In recent years, the research and application of permeable concrete in China is hot, but it is still in its infancy. In this paper, a new architectural coating modifier (lotus leaf hydrophobic agent) is introduced into the development of permeable concrete. The main contents and results of the study are as follows: (1) the volume method is suitable for the design of internal hydrophobic permeable concrete mixture ratio. After adding lotus leaf hydrophobic agent, the strength of permeable concrete can be improved to a certain extent, and the maximum value can be increased by 38. 4) according to porosity and water / cement ratio, The effect of hydrophobic agent content and aggregate type on the strength and permeability coefficient of permeable concrete is studied. It is recommended that the target porosity of internal hydrophobic permeable concrete is 20 and the water-cement ratio is between 0.24 and 0.28. The internal hydrophobic and permeable concrete with a compressive strength of 28.7 Mpas, a permeability coefficient of 4.11mm / s and a flexural strength of 4.47Mpa were prepared. The relationship between the permeability coefficient and the effective porosity is established, and it is deduced that when the effective porosity is greater than 23.8%, The permeability coefficient of internal hydrophobic permeable concrete will be higher than that of impervious concrete without hydrophobic agent. (7) the microstructure of internal hydrophobic permeable concrete will be more compact, and it will have uniform waxy small protrusions to form the hydrophobic effect of lotus leaf. It is consistent with the theoretical study in this paper.
【學(xué)位授予單位】：北華大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2017
【分類號】：TU528

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 徐紅;;透水混凝土系統(tǒng)應(yīng)用探索[J];南通紡織職業(yè)技術(shù)學(xué)院學(xué)報;2008年04期

2 王軍;;彩色透水混凝土在工程中的應(yīng)用研究[J];現(xiàn)代商貿(mào)工業(yè);2011年05期

3 王鵬;陳堅鋼;徐亦冬;;透水混凝土綜合效益簡析[J];山西建筑;2013年22期

4 何兆芳;張浩;王紅;;新型透水混凝土研究與應(yīng)用[J];住宅產(chǎn)業(yè);2014年01期

5 許漢平;徐芬蓮;;中建商砼成都公司成功實(shí)現(xiàn)露骨透水混凝土技術(shù)成果轉(zhuǎn)化[J];商品混凝土;2014年02期

6 王瓊夏;沈明興;佘國華;;無砂大孔透水混凝土實(shí)驗(yàn)研究[J];城市道橋與防洪;2006年06期

7 張朝輝;楊江金;王沁芳;楊娟;;透水混凝土制備工藝研究[J];新型建筑材料;2008年09期

8 劉翠萍;石云興;屈鐵軍;付培江;戢文占;霍亮;;透水混凝土收縮的試驗(yàn)研究[J];混凝土;2009年01期

9 徐寶華;趙榮明;孫明杰;;透水混凝土在奧運(yùn)羽毛球場館室外鋪裝工程中的應(yīng)用[J];混凝土;2009年01期

10 付立彬;付曉彥;付培江;劉明堂;;透水混凝土物理力學(xué)性能試驗(yàn)研究[J];四川建筑科學(xué)研究;2010年06期

相關(guān)會議論文 前8條

1 周占秋;周陽;徐俊峰;;透水混凝土施工工藝[A];土木建筑學(xué)術(shù)文庫（第7卷）[C];2007年

2 石云興;宋中南;霍亮;戢文占;華成謀;史海龍;;透水混凝土試驗(yàn)研究及其在奧運(yùn)工程中的應(yīng)用[A];“全國特種混凝土技術(shù)及工程應(yīng)用”學(xué)術(shù)交流會暨2008年混凝土質(zhì)量專業(yè)委員會年會論文集[C];2008年

3 梁海區(qū);李青川;黃崇奕;潘仁愛;唐明;;彩色透水混凝土在首屆廣西園博園工程中的應(yīng)用[A];特種混凝土與瀝青混凝土新技術(shù)及工程應(yīng)用[C];2012年

4 張燕剛;石云興;屈鐵軍;李艷穩(wěn);劉偉;;火山渣透水混凝土與普通透水混凝土強(qiáng)度影響因素探討[A];2013年混凝土與水泥制品學(xué)術(shù)討論會論文集[C];2013年

5 朱效榮;;高強(qiáng)度透水混凝土的研究與應(yīng)用[A];2009'中國商品混凝土可持續(xù)發(fā)展論壇暨第六屆全國商品混凝土技術(shù)與管理交流大會論文集[C];2009年

6 _5朝，

本文編號：2009151