  本文選題：圓明園 + 琉璃瓦��； 參考：《硅酸鹽通報》2017年08期

【摘要】：主要利用光學顯微鏡、能量色散(EDXRF)、XPS、SEM、TEM對圓明園出土的部分綠色琉璃瓦釉-綠中泛紅現(xiàn)象進行分析,以研究圓明園出土琉璃瓦的變色機理和燒制過程。通過以上分析表明,琉璃瓦的釉層屬于一種鉛硅系玻璃,其綠色和紅色是由于釉中Cu元素存在價態(tài)與含量不同所致,并且綠色區(qū)域是以Cu~(2+)形式存在,黑紅色和鮮紅色區(qū)域主要以Cu~+和Cu~0并存形式存在,而且黑紅色區(qū)域Cu~0的含量要高于鮮紅色,所以Cu~0對于呈紅色起到主要作用。綠色到紅色轉(zhuǎn)變是釉層中Cu~(2+)被圓明園遭到火燒時產(chǎn)生的C和CO還原為Cu~0和Cu_2O析出富集到表面所致,其本質(zhì)與銅紅釉呈色機理相同。
[Abstract]:In order to study the mechanism of discoloration and firing process of glazed tiles unearthed by Old Summer Palace, the phenomenon of redness in green glaze and glaze of partially green glazed tile unearthed by Old Summer Palace was analyzed by means of optical microscope and energy dispersive EDXRF Old Summer Palace. According to the above analysis, the glaze layer of glazed tile belongs to a kind of lead-silicon glass, its green and red are caused by the existence of different valence and content of Cu in glaze, and the green area is in the form of Cu~(2). The content of Cu~0 in the black red region is higher than that in the bright red region, so Cu~0 plays a major role in the red color. The green to red transition is caused by the reduction of C and CO from the glaze layer by Old Summer Palace to Cu~0 and Cu_2O precipitation and enrichment to the surface, the essence of which is the same as that of the copper red glaze.
【作者單位】： 中國科學院大學化學與化工學院;北京市文物研究所;北京大學考古文博學院;
【基金】：國家社會科學基金(15ZDB057) 國家自然科學基金(51671179)
【分類號】：TQ174.767

【相似文獻】

相關(guān)期刊論文 前10條

1 高雅春,耿謙;釉層龜裂的成因及其預防[J];陶瓷;2003年05期

2 林植勤;邱鎮(zhèn)滬;;釉面龜裂與釉層剝落機理探討[J];陶瓷科學與藝術(shù);2006年Z1期

3 劉翮天;;提高瓷器制品的釉層質(zhì)量[J];陶瓷;1976年04期

4 黃明卿;;瓷磚坯體和釉層同步壓制[J];建材工業(yè)信息;1984年04期

5 羊宏偉;許明方;;釉層結(jié)構(gòu)和鉛污染的關(guān)系[J];江蘇陶瓷;1988年03期

6 肖韶榮;差動傳感測量釉層熱應力[J];中國陶瓷;1995年04期

7 張頌，

本文編號：1871681