本文選題：自密實 + 全輕混凝土��； 參考：《華北水利水電大學》2017年碩士論文

【摘要】：對于自密實輕骨料混凝土,鋼纖維的加入,使自密實輕骨料混凝土在輕質高強的性能上又增加了其抗裂性、韌性,使之更能符合新型建筑材料的要求。本文對目前國內外的有關研究成果進行了較為系統(tǒng)的總結。并通過自密實混凝土的研究方法的絕對體積法,參考輕骨料混凝土的配合比設計方法并采用鋼纖維替代粗骨料的計算方法對自密輕骨料混凝土進行配合比設計和相關的試驗研究。本文采用試驗的方法配制出滿足自密實性能的自密實鋼纖維全輕混凝土,并研究了鋼纖維體積率、骨料粒徑等因素對混凝土拌合物工作性能的影響,及骨料粒徑對鋼纖維分布規(guī)律的影響。其中鋼纖維分布規(guī)律是本文研究的重點。本試驗主要研究內容與結果如下:1、按照《自密實混凝土應用技術規(guī)程》(JGJ/T283-2012)中混凝土拌合物工作性能的測試方法,分別測試自密實鋼纖維全輕混凝土拌合物的填充性、間隙通過性和抗離析性,并分析各因素對混凝土拌合物工作性能的影響規(guī)律,確定所拌制混凝土的適用范圍。結果表明,骨料粒徑和鋼纖維摻量對工作性能的影響先降低后增加。所配置的自密實鋼纖維全輕混凝土基本全部滿足工作性能要求。2、以水膠比為0.31,波浪形鋼纖維為基準,研究鋼纖維體積分數為0%、0.8%、1.2%、1.6%是對自密實鋼纖維全輕混凝土骨料最大粒徑分別為M10、M16、M20工作性能的影響。結果表明:鋼纖維體積率1.2%,骨料粒徑為M10時,工作性能最好。3、以水膠比為0.31,波浪形鋼纖維為基準,研究鋼纖維體積分數為1.2%時骨料粒徑M19,M16,M20對鋼纖維分布規(guī)律的影響。研究結果表明:M10分布規(guī)律最均勻,M16和M20近似相同。
[Abstract]:For self-compacting lightweight aggregate concrete, the addition of steel fiber can increase the crack resistance and toughness of self-compacting lightweight aggregate concrete in light and high strength, so that it can meet the requirements of new building materials. In this paper, the research results at home and abroad are systematically summarized. And through the absolute volume method of self-compacting concrete research, According to the design method of mix ratio of lightweight aggregate concrete and the calculation method of replacing coarse aggregate with steel fiber, the mix ratio design and related experimental study of self-compacting lightweight aggregate concrete are carried out. In this paper, the self-compacting steel fiber all-light concrete is prepared by means of experiment. The effects of the volume ratio of steel fiber and the particle size of aggregate on the working performance of concrete mixture are studied. And the effect of aggregate particle size on the distribution of steel fiber. The distribution of steel fiber is the focus of this paper. The main contents and results of this experiment are as follows: 1. According to the test method of the performance of the concrete mixture in JGJ / T283-2012), the filling properties of the self-compacting steel fiber total light concrete mixture are tested respectively. The effects of various factors on the performance of concrete mixture were analyzed and the applicable range of concrete was determined. The results show that the effect of aggregate particle size and steel fiber content on the working properties decreases first and then increases. The fully lightweight self-compacting steel fiber concrete has basically met the working performance requirement of 0.2.The reference is the water-binder ratio of 0.31 and the wavy steel fiber. The effect of steel fiber volume fraction of 0 and 0.8% and 1.6% on the working performance of self-compacting steel fiber whole light concrete aggregate with maximum particle size of M10 / M16 / M20 was studied. The results show that when the volume ratio of steel fiber is 1.2 and the aggregate particle size is M10, the working performance is the best. The effect of aggregate size M19 M16 / M20 on the distribution of steel fiber is studied on the basis of water / binder ratio of 0.31 and wavy steel fiber as the reference point, when the volume fraction of steel fiber is 1.2, the effect of aggregate size M19 / M16 / M20 on the distribution of steel fiber is studied. The results show that the distribution law of M10 is approximately the same as M16 and M20.
【學位授予單位】：華北水利水電大學
【學位級別】：碩士
【學位授予年份】：2017
【分類號】：TU528

【參考文獻】

相關期刊論文 前10條

1 潘麗云;徐文曉;陳彥磊;李長永;;鋼纖維全輕混凝土基本性能試驗研究[J];華北水利水電大學學報(自然科學版);2015年02期

2 李曉克;沈澤;陳梅華;趙明爽;;鋼纖維輕骨料粉煤灰砼抗壓性能試驗研究[J];廣西大學學報(自然科學版);2015年01期

3 劉喜;呂貝貝;劉全威;吳濤;;高強輕骨料陶粒混凝土配合比及強度影響因素試驗研究[J];硅酸鹽通報;2014年04期

4 高英力;劉赫;張海倫;唐斌璨;;高強輕骨料混凝土拌合物性能及影響因素試驗研究[J];硅酸鹽通報;2013年04期

5 王玉梅;劉錫軍;;自密實輕骨料混凝土配合比設計及基本力學性能試驗[J];混凝土;2012年06期

6 譚一明;李海深;;自密實輕骨料混凝土配合比設計[J];湖南工程學院學報(自然科學版);2011年04期

7 張春曉;丁慶軍;;鋼纖維輕集料自密實混凝土的配制及其在鋼橋面鋪裝中的應用[J];混凝土;2011年03期

8 吳智敏;張小云;張云國;;自密實輕骨料混凝土配合比設計及基本力學性能試驗[J];建筑科學與工程學報;2008年04期

9 劉漢勇;王立成;宋玉普;王海濤;;鋼纖維高強輕骨料混凝土力學性能的試驗研究[J];建筑結構學報;2007年05期

10 辛全倉;張殿明;王振軍;何廷樹;;自密實輕骨料混凝土配合比設計研究[J];公路;2007年05期

相關博士學位論文 前3條

1 李長永;鋼纖維輕骨料混凝土性能與疊澆梁受彎性能研究[D];鄭州大學;2014年

2 張云國;自密實輕骨料混凝土性能研究[D];大連理工大學;2009年

3 曾志興;鋼纖維輕骨料混凝土力學性能的試驗研究及損傷斷裂分析[D];天津大學;2003年

相關碩士學位論文 前6條

1 楊慧;鋼纖維全輕混凝土無腹筋梁抗剪性能試驗研究[D];華北水利水電大學;2014年

2 程領;LC50輕骨料混凝土配合比設計及性能研究[D];長沙理工大學;2013年

3 王大強;自密實纖維輕骨料混凝土耐久性及微觀結構研究[D];大連交通大學;2011年

4 蘭憲鋼;自密實纖維輕骨料混凝土工作及力學性能研究[D];大連交通大學;2011年

5 張小云;自密實輕骨料混凝土試驗研究[D];大連理工大學;2009年

6 曹剛;高強輕骨料混凝土試驗研究[D];西北工業(yè)大學;2004年

，

本文編號：1842718