本文選題：金剛石　切入點(diǎn)：化學(xué)鍍鎳　出處：《電鍍與涂飾》2017年16期

【摘要】：先對(duì)金剛石進(jìn)行化學(xué)鍍鎳,得到增重率分別為5%、10%、20%、30%、45%和60%的鍍鎳金剛石。隨后以直徑120μm的鍍銅圓柱形琴鋼絲作為基體,采用氨基磺酸鎳為主鹽的鍍液(由80 g/L Ni(NH_2SO_3)2·4H_2O、30 g/L NiCl_2·6H_2O、3 g/L H_3BO_3和0.1 g/L十二烷基硫酸鈉組成)依次進(jìn)行預(yù)鍍(1μm)、上砂鍍(6μm)和加厚鍍(6μm)。其中上砂鍍是采用鍍鎳金剛石作為第二相進(jìn)行鎳-金剛石復(fù)合電鍍。結(jié)果表明,選用增重率為30%的金剛石磨粒進(jìn)行上砂鍍時(shí),所得金剛石線鋸的表面形貌最佳,磨粒的沉積密度最高,切割性能最優(yōu)。
[Abstract]:After electroless nickel plating on diamond, a nickel plated diamond with a weight gain of 5% 10% 20% and 30% 45% and 60% respectively was obtained, and then the 120 渭 m copper plated cylindrical piano wire was used as the substrate. Nickel aminosulfonic acid plating solution (consisting of 80 g / L Ni(NH_2SO_3)2 4H _ 2O _ 3 g / L NiCl_2 _ 6H _ 2O _ 3 g / L H_3BO_3 and 0.1 g / L sodium dodecyl sulfate) was used for pre-plating (1 渭 m), sand plating (6 渭 m) and thickening plating (6 渭 m), in which nickel coated diamond was used as the second phase. Ni-diamond composite electroplating. The results show that, When the diamond abrasive with weight gain of 30% is sand-plated, the diamond wire saw has the best surface morphology, the highest deposition density and the best cutting performance.
【作者單位】： 江西省核工業(yè)地質(zhì)局測(cè)試研究中心;
【分類號(hào)】：TB306;TQ153.12

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 張國(guó)青;黃輝;徐西鵬;;釬焊金剛石線鋸切割單晶硅材料時(shí)的斷裂行為研究[J];金剛石與磨料磨具工程;2014年04期

2 中川平三郎;蔣修治;;用金剛石線鋸高速高精度切割加工天然大理石[J];超硬材料工程;2006年06期

3 石川憲一;金剛石電沉積絞合線鋸的開發(fā)[J];珠寶科技;2004年02期

4 畢玉超;葛培琪;高玉飛;;KDP晶體金剛石線鋸切入方向的研究[J];硅酸鹽通報(bào);2013年06期

相關(guān)碩士學(xué)位論文 前6條

1 馬倩;樹脂結(jié)合劑金剛石線鋸的研究[D];河南工業(yè)大學(xué);2016年

2 鄭路;樹脂結(jié)合劑金剛石線鋸絲制造實(shí)驗(yàn)研究[D];山東大學(xué);2016年

3 劉宇龍;硅片線鋸廢料中硅的回收技術(shù)研究[D];南昌大學(xué);2013年

4 孟磊;碳化硅的線鋸切片技術(shù)與加工機(jī)理研究[D];山東大學(xué);2011年

5 張景濤;電鍍金剛石線鋸制造工藝及其性能的研究[D];青島科技大學(xué);2013年

6 賀歡歡;硅片線鋸廢砂漿中硅與碳化硅分離技術(shù)研究[D];南昌大學(xué);2012年

，

本文編號(hào)：1696009