本文關(guān)鍵詞： 秸稈菱鎂混凝土 創(chuàng)新型工藝 物理力學(xué)性能 擬靜力試驗　出處：《山東農(nóng)業(yè)大學(xué)》2017年碩士論文　論文類型：學(xué)位論文

【摘要】：秸稈菱鎂混凝土是以秸稈纖維為加筋材料,以菱鎂水泥作為膠結(jié)材料,摻加適當(dāng)比例的礦物填料和添加劑,加水制成的具有一定強(qiáng)度、保溫性能和較好穩(wěn)定性的新型環(huán)保節(jié)能材料。旨在突破傳統(tǒng)秸稈類建材秸稈摻量低、強(qiáng)度低等缺點(diǎn),并充分利用秸稈的保溫性能在農(nóng)村建房,打造綠色生態(tài)建筑。本文對傳統(tǒng)秸稈類混凝土的研究現(xiàn)狀和不能大規(guī)模推廣的原因進(jìn)行了分析。自行設(shè)計了秸稈混凝土的專用制作裝置來研制新型秸稈混凝土。確定了新型秸稈混凝土的原材料組成,并探索性的對秸稈的處理和選材、鹵水的制作和濃度的取值、膠凝材料的制備和配比取值、氯氧鎂水泥的性能等進(jìn)行了研究。形成了一套完善的秸稈混凝土試件的制作工藝技術(shù)。試驗設(shè)計了600 Kg/m3、800 Kg/m3、1000 Kg/m3三個等級的秸稈菱鎂混凝土正交試驗組,研究秸稈摻量、膠凝材料配比和砂摻量對秸稈混凝土抗壓強(qiáng)度、彈性模量、干密度的影響規(guī)律。并對正交試驗結(jié)果進(jìn)行了系統(tǒng)的分析,包括極差分析、點(diǎn)圖分析、方差分析。試驗確定了三個密度等級的秸稈混凝土的最優(yōu)配合比。并根據(jù)試驗結(jié)果研究低密度秸稈混凝土抗壓強(qiáng)度數(shù)據(jù)規(guī)律,設(shè)計1600 Kg/m3、1800 Kg/m3兩個密度等級的秸稈混凝土,使其達(dá)到承重砌塊強(qiáng)度的要求。然后對秸稈菱鎂混凝土立方體試件的受壓破壞形態(tài)進(jìn)行分析,并繪制應(yīng)力-應(yīng)變曲線,計算彈性模量。對不同密度秸稈菱鎂混凝土試件的應(yīng)力-應(yīng)變曲線進(jìn)行綜合性分析,研究其受壓變形規(guī)律。然后將不同密度等級的秸稈菱鎂混凝土與其它幾種混凝土的抗壓強(qiáng)度、彈性模量和干密度進(jìn)行了系統(tǒng)性對比,證明了秸稈菱鎂混凝土性能的優(yōu)越。本文對不同密度等級的秸稈菱鎂混凝土的導(dǎo)熱系數(shù)和軟化系數(shù)進(jìn)行了測試。證明了秸稈混凝土其優(yōu)良的保溫性能,并針對秸稈菱鎂混凝土的耐水性能差的缺點(diǎn)提出了改進(jìn)方案。而且應(yīng)用設(shè)計了秸稈菱鎂混凝土預(yù)制中型砌塊和輕鋼骨架-秸稈混凝土混合結(jié)構(gòu)墻體,并針對墻體的抗震性能進(jìn)行了擬靜力試驗,充分證明了秸稈菱鎂混凝土砌塊建造墻體的優(yōu)越的抗震性能。
[Abstract]:Straw magnesite concrete is made of straw fiber as reinforcement material, magnesium magnesite cement as cementing material, with appropriate proportion of mineral fillers and additives, and water has a certain strength. The aim of this paper is to break through the disadvantages of low mixing amount and low strength of traditional straw building materials, and make full use of the thermal insulation property of straw to build houses in rural areas. In this paper, the research status of traditional straw concrete and the reasons why it can not be popularized on a large scale are analyzed. A special production device of straw concrete is designed to develop new straw concrete. The raw material composition of new straw concrete was determined. And explore the treatment and selection of straw, brine production and concentration of the value, the preparation of cementitious materials and the ratio of values. The properties of magnesium oxychloride cement were studied. A set of perfect processing technology of straw concrete specimen was formed. The 600 kg / m ~ (3 +) ~ (800) Kg/m3 was designed. The compressive strength and elastic modulus of straw concrete with three grades of 1000 Kg/m3 were studied in the orthogonal test group, including the content of straw, the proportion of cementing material and the amount of sand. The effects of dry density on the results of orthogonal test are analyzed systematically, including range analysis and point diagram analysis. Variance analysis. The optimum mix ratio of straw concrete with three density grades was determined. According to the experimental results, the compressive strength data of low density straw concrete was studied, and the design was made at 1600 Kg/m3. Two density grades of straw concrete at 1800 Kg/m3 made it meet the requirements of bearing block strength. Then the compressive failure pattern of cubic specimen of straw magnesite concrete was analyzed. The stress-strain curve was drawn and the elastic modulus was calculated. The stress-strain curves of different density straw magnesite concrete specimens were comprehensively analyzed. Then, the compressive strength, elastic modulus and dry density of straw magnesite concrete with different density grades were systematically compared with other concrete. In this paper, the thermal conductivity and softening coefficient of straw magnesite concrete with different density grades were tested, and the excellent thermal insulation performance of straw magnesite concrete was proved. According to the shortcoming of poor water resistance of straw magnesite concrete, the improvement scheme is put forward, and the precast medium block of straw magnesite concrete and the mixed structure wall of light steel skeleton and straw concrete are designed. The quasi static test on the seismic behavior of the wall is carried out, which fully proves the excellent seismic performance of the wall constructed by the straw magnesite concrete block.
【學(xué)位授予單位】：山東農(nóng)業(yè)大學(xué)
【學(xué)位級別】：碩士
【學(xué)位授予年份】：2017
【分類號】：TU528

【參考文獻(xiàn)】

相關(guān)期刊論文 前10條

1 張強(qiáng);李耀莊;劉保華;徐志勝;;秸稈灰混凝土力學(xué)性能試驗及強(qiáng)度預(yù)測[J];農(nóng)業(yè)工程學(xué)報;2017年02期

2 項雅麗;鄧世輝;夏明明;;秸稈資源制作農(nóng)村墻體理論研究與發(fā)展趨勢探討[J];科技創(chuàng)業(yè)月刊;2016年23期

3 王永維;朱磊;關(guān)博文;劉偉;李鋒;;用于配制鎂水泥膠凝材料鹵水的波美度研究[J];公路;2016年05期

4 譚曦;蘇有文;;稻草纖維混凝土物理力學(xué)性能試驗研究[J];混凝土與水泥制品;2016年05期

5 朱立平;丁晴;侯鵬;張劍紅;;外墻用巖棉板導(dǎo)熱系數(shù)與溫度及含水率的關(guān)系[J];建筑節(jié)能;2016年04期

6 錢坤;賈光輝;夏天;;秸稈混凝土砌塊的力學(xué)性能試驗研究[J];建筑節(jié)能;2015年11期

7 馬慧;關(guān)博文;王永維;郁亞蕓;劉開平;張紀(jì)陽;;氯氧鎂水泥膠凝材料的研究進(jìn)展[J];材料導(dǎo)報;2015年15期

8 張偉平;童菲;邢益善;顧祥林;;混凝土導(dǎo)熱系數(shù)的試驗研究與預(yù)測模型[J];建筑材料學(xué)報;2015年02期

9 張強(qiáng);李耀莊;劉保華;;秸稈資源在混凝土中應(yīng)用的研究進(jìn)展[J];硅酸鹽通報;2015年04期

10 李輝;;均勻設(shè)計在混凝土膠凝材料強(qiáng)度確定中的應(yīng)用[J];廣東建材;2015年03期

相關(guān)會議論文 前1條

1 文俊強(qiáng);陳益民;張洪滔;唐潤榮;董剛;吳明慧;;我國無機(jī)膠凝材料基秸稈建材發(fā)展現(xiàn)狀[A];第十屆全國水泥和混凝土化學(xué)及應(yīng)用技術(shù)會議論文摘要集[C];2007年

相關(guān)博士學(xué)位論文 前1條

1 鄭妮娜;裝配式構(gòu)造柱約束砌體結(jié)構(gòu)抗震性能研究[D];重慶大學(xué);2010年

相關(guān)碩士學(xué)位論文 前10條

1 彭立磊;農(nóng)作物秸稈再生保溫磚砌體基本物理力學(xué)性能試驗研究[D];鄭州大學(xué);2016年

2 齊瑋;泡沫混凝土物理力學(xué)性能與孔隙特征的研究[D];沈陽建筑大學(xué);2016年

3 徐翔波;再生混凝土配合比設(shè)計及其物理力學(xué)性能研究[D];廣西科技大學(xué);2015年

4 張慧瑾;混凝土夾心秸稈砌塊試點(diǎn)建筑保溫性能研究[D];山東農(nóng)業(yè)大學(xué);2015年

5 宋梓寧;秸稈混凝土力學(xué)和保溫性能的室內(nèi)試驗與數(shù)值模擬研究[D];吉林大學(xué);2015年

6 姜榮鵬;秸稈禁燒與秸稈處理處置問題研究[D];山東大學(xué);2013年

7 王皓;組合結(jié)構(gòu)體系承載力及變形性能研究[D];吉林建筑工程學(xué)院;2012年

8 丁美;農(nóng)作物秸稈資源潛力與開發(fā)可持續(xù)評價體系研究[D];南京農(nóng)業(yè)大學(xué);2011年

9 馬飛;混凝土夾心秸稈塊砌塊干燥工藝與力學(xué)性能研究[D];山東農(nóng)業(yè)大學(xué);2011年

10 殷園園;芯柱式構(gòu)造柱約束砌體結(jié)構(gòu)抗震性能評價[D];重慶大學(xué);2011年

，

本文編號：1458547