【摘要】：采用淬火法制備聚乳酸(PLA)非晶薄膜,并利用原位顯微紅外光譜在線研究PLA非晶薄膜在不同退火溫度下的結(jié)構(gòu)演化.結(jié)果表明,PLA非晶薄膜存在一個臨界結(jié)晶溫度,當(dāng)退火溫度高于臨界結(jié)晶溫度時,PLA非晶薄膜可以通過分子鏈的局部調(diào)整實現(xiàn)冷結(jié)晶,反之,不能發(fā)生冷結(jié)晶;在冷結(jié)晶過程中先出現(xiàn)中間相,隨后發(fā)生中間相-晶體相的轉(zhuǎn)變;中間相是通過分子鏈的構(gòu)象調(diào)整和分子鏈間的堆砌調(diào)整產(chǎn)生的,退火溫度越高,中間相出現(xiàn)得越早,最終得到的晶體結(jié)構(gòu)越規(guī)整.
[Abstract]:Polylactic acid (PLA) amorphous films were prepared by quenching method. The structure evolution of PLA amorphous films at different annealing temperatures was studied by in situ microinfrared spectroscopy. The results show that there is a critical crystallization temperature in the PLA amorphous film. When the annealing temperature is higher than the critical crystallization temperature, the cold crystallization of the PLA amorphous film can be achieved by local adjustment of molecular chain, whereas cold crystallization cannot occur. In the cold crystallization process, the mesophase appears first, then the mesophase-crystal phase changes. The mesophase is produced by the conformation adjustment of molecular chain and the stacking adjustment between molecular chains. The higher the annealing temperature, the earlier the mesophase appears. The resulting crystal structure is more regular.
【作者單位】： 鄭州大學(xué)力學(xué)與工程科學(xué)學(xué)院;鄭州大學(xué)物理工程學(xué)院;鄭州大學(xué)國家橡塑模具工程研究中心;
【基金】：國家自然科學(xué)基金(批準(zhǔn)號:51573171)和國家自然科學(xué)基金重點項目(批準(zhǔn)號:11432003)資助~~
【分類號】：O633.14

【相似文獻(xiàn)】

相關(guān)期刊論文 前6條

1 熊新向,李軒科,楊棟梁,李清田;水性中間相制備的初步研究[J];炭素技術(shù);1998年02期

2 李同起,王成揚;碳質(zhì)中間相形成機(jī)理研究[J];新型炭材料;2005年03期

3 王茂章;;有機(jī)化合物的液相炭化化學(xué)[J];化學(xué)通報;1990年12期

4 錢樹安;略論炭素科學(xué)的形成和進(jìn)展──Ⅴ.液相炭化機(jī)理研究的歷史和現(xiàn)狀[J];炭素;1996年02期

5 常云峰,李柏齡,錢樹安;中間相的分子結(jié)構(gòu)[J];碳素;1986年03期

6 ;[J];;年期

相關(guān)博士學(xué)位論文 前1條

1 李同起;碳質(zhì)中間相結(jié)構(gòu)的形成及其相關(guān)材料的應(yīng)用研究[D];天津大學(xué);2005年

，

本文編號：1981880