本文關(guān)鍵詞：金納米通道制備及催化性能研究　出處：《光譜學與光譜分析》2016年S1期 　論文類型：期刊論文

  更多相關(guān)文章： 金納米通道 層-層自組裝 催化性能

【摘要】：以聚碳酸酯超濾膜(PC膜)為模板,采用層-層自組裝技術(shù)將聚乙烯亞胺(PEI)陽離子聚合物和檸檬酸根穩(wěn)定的金納米粒子(AuNPs)交替吸附在PC膜孔內(nèi)制備了金納米通道,并采用SEM對其進行了表征。以紫外-可見吸收光譜作為分析手段研究了金納米通道對對硝基苯酚(4-NP)還原反應(yīng)的催化性能。結(jié)果表明,金納米通道具有良好的催化活性,催化效率隨組裝層數(shù)的增多出現(xiàn)先增大后降低的現(xiàn)象,PEI/AuNPs為三層時,金納米通道具有較高的催化性能,且催化效率隨4-NP+NaBH4混合溶液體系在金納米通道內(nèi)的流速增大而減小。
[Abstract]:Using polycarbonate ultrafiltration membrane (PC membrane) as template, the gold nanochannels were prepared by layer to layer self assembly technology, and the gold nanoparticles were alternately adsorbed on the PC membrane hole by alternating adsorption of polyethylenimine (PEI) cationic polymer and citric acid stabilized gold nanoparticles (AuNPs), and their appearance was characterized by SEM. The catalytic properties of the gold nano channel on the reduction of p-nitrophenol (4-NP) were studied by UV visible absorption spectroscopy. The results show that the gold nano channel has good catalytic activity, catalytic efficiency with increasing the number of the layers increase first and then decrease, PEI/AuNPs for the three layer, the catalytic performance of gold nano channel has high catalytic efficiency, and with 4-NP+NaBH4 mixed solution on gold nano channel velocity increases.
【作者單位】： 西北大學化學與材料科學學院;
【基金】：陜西省自然科學基金項目(2014JM2050)資助
【分類號】：O643.36;TB383.1
【正文快照】： 金納米通道的制備及表征結(jié)果:將PC膜放到膜過濾器里,與裝有組裝液的注射器連接好一并安置到注射泵上。利用注射泵控制流速,將10 mL 0.5 mg·L-1的PEI溶液以0.25mL·min-1的速度濾過裝有PC膜的過濾器,再用10mL的超純水以1mL·min-1的速度濾過,洗去與PC膜結(jié)合不牢固的PEI分子,用

【相似文獻】

相關(guān)期刊論文 前4條

1 翟尚儒,鄭均林,吳東,孫予罕;NaAlO_2改性AlMCM-41:鋁分布、酸量及催化性能的有效調(diào)控[J];無機化學學報;2004年09期

2 高志賢,程昌瑞,譚長瑜;Ga－Al－Si－ZSM－5 的合成、表征與催化性能[J];石油學報(石油加工);1996年01期

3 李新柱;張記市;;Co取代介孔磷鋁分子篩的合成、表征及催化性能[J];中國有色金屬學報;2009年11期

4 ;[J];;年期

相關(guān)會議論文 前1條

1 景曉燕;;球形Co_3O_4的合成與性能研究[A];中國化學會第28屆學術(shù)年會第5分會場摘要集[C];2012年

，

本文編號：1346289