【摘要】：研究了由不同摻量有機(jī)蛭石(OEVMT)和納米氧化鋅(Nano-ZnO)組成的多尺度納米材料對(duì)再生瀝青長(zhǎng)期熱氧和光氧老化性能的影響。利用薄膜烘箱對(duì)普通基質(zhì)瀝青進(jìn)行老化以制得老化瀝青,采用熔融共混方法,先將老化瀝青、普通基質(zhì)瀝青以及再生劑按照一定的比例混合以制得再生瀝青,再將多尺度納米材料加入到再生瀝青中制得多尺度納米材料改性再生瀝青。采用壓力老化箱老化(PAV)和加速紫外光老化(UV)分別模擬再生瀝青的長(zhǎng)期熱氧老化和光氧老化條件。通過傳統(tǒng)物理性能試驗(yàn)和動(dòng)態(tài)剪切流變?cè)囼?yàn)評(píng)價(jià)了再生瀝青的老化性能。結(jié)果表明:添加多尺度納米材料提高了再生瀝青老化前的高溫穩(wěn)定性、剪切變形抵抗力和彈性行為,但一定程度上削弱了其低溫塑性變形能力;多尺度納米材料有效改善了再生瀝青長(zhǎng)期熱氧和光氧老化抵抗力;綜合考慮長(zhǎng)期老化性能數(shù)據(jù),多尺度納米材料的推薦摻量(質(zhì)量分?jǐn)?shù))為1%OEVMT+3%Nano-ZnO。
[Abstract]:The effects of multi-scale nano-materials composed of organic vermiculite (OEVMT) and nano-zinc oxide (Nano-ZnO) on the long-term thermal and photo-oxygen aging properties of recycled asphalt were studied. The aging asphalt was prepared by using the film oven to aging the common base asphalt. The asphalt was prepared by melt blending, and the aging asphalt, the ordinary base asphalt and the regenerating agent were mixed in a certain proportion to produce the recycled asphalt. Then the multi-scale nano-materials were added to the recycled asphalt to prepare the multi-scale nano-materials modified recycled asphalt. The aging conditions of regenerated asphalt were simulated by aging (PAV) in pressure aging chamber and accelerated UV aging (UV), respectively. The aging performance of recycled asphalt was evaluated by traditional physical property test and dynamic shear rheological test. The results show that the addition of multi-scale nano-materials can improve the high temperature stability, shear deformation resistance and elastic behavior of recycled asphalt before aging, but weaken its low temperature plastic deformation ability to some extent. Multi-scale nano-materials can effectively improve the resistance of regenerated asphalt to long-term thermal oxygen and photo-oxygen aging, and considering the long-term aging performance data, the recommended content (mass fraction) of multi-scale nano-materials is 1%OEVMT _ 3Nano-ZnO.
【作者單位】： 湖南大學(xué)土木工程學(xué)院;
【基金】：國(guó)家自然科學(xué)基金項(xiàng)目(51308203) 湖南省自然科學(xué)基金項(xiàng)目(2017JJ3015) 湖南省交通科技進(jìn)步與創(chuàng)新計(jì)劃項(xiàng)目(201307) 湖南省科技計(jì)劃重點(diǎn)項(xiàng)目(2015SK2063-1)
【分類號(hào)】：U414

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 韓基一;王永剛;楊光;劉九林;;再生瀝青的化學(xué)組成與結(jié)構(gòu)研究[J];蘭州石化職業(yè)技術(shù)學(xué)院學(xué)報(bào);2009年03期

2 安中華,楊彥海,徐雅峰,孔國(guó)永;灰色關(guān)聯(lián)分析法評(píng)價(jià)再生瀝青的性能關(guān)系[J];遼寧交通科技;2003年06期

3 王洋;廖克儉;王洪國(guó);陸偉強(qiáng);;鞍山千山公路再生瀝青老化研究[J];化工科技;2012年02期

4 ;江西省公路管理局召開舊路再生瀝青養(yǎng)護(hù)新技術(shù)現(xiàn)場(chǎng)觀摩會(huì)[J];石油瀝青;2013年04期

5 李波;;道路再生瀝青與混凝土配比研究[J];內(nèi)蒙古公路與運(yùn)輸;2014年01期

6 陳義兵;;再生瀝青混合料配合比設(shè)計(jì)技術(shù)[J];安徽建筑;2007年05期

7 李進(jìn);張玉貞;;工廠熱拌再生瀝青混凝土技術(shù)綜述[J];石油瀝青;2008年01期

8 丁湛;栗培龍;;再生瀝青的黏度復(fù)合模型研究[J];新型建筑材料;2008年05期

9 楊秋浩;;再生瀝青混凝土質(zhì)量控制因素研究[J];科技創(chuàng)新導(dǎo)報(bào);2011年12期

10 周彬;連瑞雪;;再生瀝青養(yǎng)護(hù)法在公路養(yǎng)護(hù)中的作用分析[J];科技信息;2012年09期

相關(guān)會(huì)議論文 前2條

1 徐f，

本文編號(hào)：2399621