【摘要】：冷拌超薄瀝青混合料是一種新型路面材料。為驗(yàn)證其可行性,選用兩種乳化劑和3種常用超薄層級(jí)配來(lái)測(cè)試其路用性能。首先采用修正馬歇爾方法進(jìn)行了3種級(jí)配的配合比設(shè)計(jì),得到了最佳瀝青摻量。然后按照規(guī)范規(guī)定方法,測(cè)定了不同組合的高溫穩(wěn)定性、低溫穩(wěn)定性、水穩(wěn)定性和表面抗滑性能。測(cè)試結(jié)果顯示,只有A種乳化劑和SMA-10組合才能滿足規(guī)范規(guī)定的各項(xiàng)指標(biāo),滿足工程可行性。限制冷拌超薄瀝青混合料功能的不是高溫性能和表面抗滑性能,而是水穩(wěn)定性能和低溫性能,此領(lǐng)域尚待深入研究。
[Abstract]:Cold-mixed ultra-thin asphalt mixture is a new type of pavement material. In order to verify its feasibility, two kinds of emulsifiers and three kinds of commonly used ultra-thin layers were selected to test their road performance. At first, the modified Marshall method was used to design the mixture ratio of three grades, and the optimum asphalt content was obtained. The stability of high temperature, low temperature, water and surface skid resistance of different combinations were determined according to the standard method. The test results show that only the combination of A emulsifier and SMA-10 can meet the specifications and meet the engineering feasibility. The function of cold mix ultra-thin asphalt mixture is not limited by high temperature performance and surface skid resistance, but by water stability and low temperature performance.
【作者單位】： 湖北職業(yè)技術(shù)學(xué)院;武漢工程大學(xué)交通研究中心;
【基金】：湖北省自然科學(xué)基金青年項(xiàng)目,項(xiàng)目編號(hào)2014CFB772 武漢工程大學(xué)科學(xué)研究基金,項(xiàng)目編號(hào)K201408
【分類號(hào)】：U414

【參考文獻(xiàn)】

相關(guān)期刊論文 前3條

1 譚憶秋;姚李;王海朋;邊鑫;齊宇翔;;超薄磨耗層瀝青混合料評(píng)價(jià)指標(biāo)[J];哈爾濱工業(yè)大學(xué)學(xué)報(bào);2012年12期

2 張永明;宋曉燕;王婷;劉蒸;朱涵;;溫拌瀝青混合料超薄罩面在道路養(yǎng)護(hù)中的應(yīng)用技術(shù)[J];公路;2011年01期

3 李安,鄭南翔;冷拌瀝青混合料磨耗層[J];中外公路;2005年04期

相關(guān)碩士學(xué)位論文 前1條

1 李萍;慢裂乳化瀝青的研究開發(fā)和應(yīng)用[D];東南大學(xué);2005年

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 陳磊;余浩;;溫拌瀝青混合料超薄罩面技術(shù)分析[J];科技經(jīng)濟(jì)市場(chǎng);2017年07期

2 龔小波;張波;高成倫;;SMC改性瀝青超薄罩面在達(dá)陜高速公路養(yǎng)護(hù)中的應(yīng)用[J];低碳世界;2017年13期

3 何y腜，

本文編號(hào)：2325852