本文關(guān)鍵詞：納米偏高嶺土砂漿氯離子滲透性的試驗研究　出處：《廣西大學(xué)學(xué)報(自然科學(xué)版)》2017年04期 　論文類型：期刊論文

  更多相關(guān)文章： 納米偏高嶺土砂漿 正交試驗 電阻率 孔隙率 氯離子擴散系數(shù)

【摘要】：為研究不同水膠比(0.4、0.5、0.6)、養(yǎng)護(hù)方式(水養(yǎng)護(hù)、飽和Ca(OH)2溶液養(yǎng)護(hù)、水與飽和Ca(OH)2溶液交替養(yǎng)護(hù))、礦物摻合料(礦粉、粉煤灰、凹凸棒粘土)對納米偏高嶺土砂漿氯離子滲透性的影響,采用正交試驗設(shè)計9組納米偏高嶺土砂漿配合比,分析其對納米偏高嶺土砂漿物理性能(電阻率、孔隙率)、力學(xué)性能(抗折強度、抗壓強度)、氯離子滲透性的影響規(guī)律;探討納米偏高嶺土砂漿氯離子滲透性與其電阻率、孔隙率之間的關(guān)系。研究結(jié)果表明,水膠比是影響納米偏高嶺土砂漿電阻率、孔隙率的重要因素;礦物摻合料是影響納米偏高嶺土砂漿抗折強度、抗壓強度、氯離子擴散系數(shù)的重要因素,摻30%粉煤灰、3%凹凸棒粘土?xí)r納米偏高嶺土砂漿氯離子擴散系數(shù)較摻30%礦粉的分別提高2.74倍、3.43倍;養(yǎng)護(hù)齡期為28 d時,納米偏高嶺土砂漿氯離子擴散系數(shù)與電阻率、氣孔含量分別呈反比、正比關(guān)系。
[Abstract]:In order to study the effects of water binder ratio (0.4,0.5,0.6), conservation methods (water conservation, saturated Ca (OH) 2 solution of conservation, water and saturated Ca (OH) 2 solution alternating curing), mineral admixtures (slag, fly ash, nano attapulgite clay) of metakaolin mortar chloride ion permeability effect and by orthogonal design 9 groups of nano metakaolin cement mortar, the analysis on the physical properties of nano metakaolin mortar (resistivity, porosity), mechanical properties (flexural strength, compressive strength, chloride ion permeability) the influence of nano metakaolin mortar; chloride ion permeability and resistivity, the relationship between between the porosity. The results showed that water binder ratio is the effect of nano metakaolin mortar resistivity, an important factor of porosity; mineral admixture is the flexural strength, the effect of nano metakaolin compressive strength of mortar, the important factors of chloride diffusion coefficient, with 30% fly ash, 3 The chloride diffusivity of nano metakaolin mortar increased by 2.74 times and 3.43 times respectively compared with 30% mineral powder when the attapulgite clay was used. When the curing age was 28 d, the chloride diffusivity of the nano metakaolin soil mortar was inverse proportional to the resistivity and the porosity content.

【作者單位】： 大連海事大學(xué)道路與橋梁工程研究所;
【基金】：國家自然科學(xué)基金資助項目(51578099) 中央高校基本科研業(yè)務(wù)費專項資金資助項目(3132014326)
【分類號】：U414
【正文快照】： 0引言為保證冬季道路交通安全運行,需噴灑大量除冰鹽以除去道路、橋梁上的積雪。因目前國內(nèi)外采用的除冰鹽的成分主要是氯鹽,這導(dǎo)致許多道路、橋梁結(jié)構(gòu)處于氯鹽環(huán)境中,而氯離子侵入混凝土?xí)䦟?dǎo)致鋼筋銹蝕,從而造成混凝土結(jié)構(gòu)耐久性失效破壞。資料[1]顯示,美國因大量使用冰除鹽