本文關(guān)鍵詞： 無機(jī)聚合物 珊瑚礁砂 正交試驗(yàn) 力學(xué)性能　出處：《武漢理工大學(xué)學(xué)報(bào)》2016年11期 　論文類型：期刊論文

【摘要】：利用珊瑚礁砂為細(xì)骨料,無機(jī)聚合物為膠凝材料,試配出無機(jī)聚合物珊瑚礁砂混凝土(IPCSC);考慮水膠比、膠凝材料用量、砂率以及溫度4項(xiàng)因素,進(jìn)行正交試驗(yàn),優(yōu)選出強(qiáng)度等效于C40且工作性能優(yōu)良的配比;根據(jù)標(biāo)準(zhǔn)方法測試了基本力學(xué)性能,各項(xiàng)指標(biāo)與對照的水泥珊瑚礁砂混凝土(CSC)進(jìn)行了對比。結(jié)果表明:相對于對照組,同強(qiáng)度等級時(shí),IPCSC劈裂抗拉強(qiáng)度提高62%,試樣拉壓強(qiáng)度比增加,靜力彈性模量略有提高。
[Abstract]:Using coral reef sand as fine aggregate and inorganic polymer as cementitious material, inorganic polymer coral reef sand concrete was prepared. The orthogonal test was carried out considering four factors: water / binder ratio, amount of cementitious material, sand ratio and temperature. The ratio of strength equivalent to C40 and excellent working performance was selected, and the basic mechanical properties were tested according to the standard method, and the indexes were compared with the control CSCs. The results showed that: compared with the control group, At the same strength grade, the splitting tensile strength of IPCSC increases by 62%, the tensile strength ratio increases, and the static modulus of elasticity increases slightly.
【作者單位】： 武漢理工大學(xué)設(shè)計(jì)研究院;武漢理工大學(xué)土木工程與建筑學(xué)院;
【基金】：國家科技支撐計(jì)劃(2014BAB15B01)
【分類號】：TU528

【相似文獻(xiàn)】

中國期刊全文數(shù)據(jù)庫 前4條

1 ;新的無機(jī)聚合物氯化磷腈首次投產(chǎn)[J];化工新型材料科技資料;1979年10期

2 吳永根;付亞偉;蔡良才;劉洋;王碩太;徐波;;無機(jī)聚合物快速修補(bǔ)混凝土研究[J];混凝土;2008年09期

3 梁磊;李曉;牛晚揚(yáng);孟瑞晉;;雙氧水發(fā)泡體系對無機(jī)聚合物發(fā)泡混凝土硬化性能的影響研究[J];混凝土;2014年01期

4 ;[J];;年期

中國碩士學(xué)位論文全文數(shù)據(jù)庫 前2條

1 游純子;無機(jī)聚合物混凝土溫度-應(yīng)力試驗(yàn)研究[D];武漢理工大學(xué);2014年

2 劉驊;無機(jī)聚合物混凝土耐久性能試驗(yàn)研究[D];武漢理工大學(xué);2011年

，

本文編號：1554725