本文選題：瓦特鎳 + 硫酸鎳�。� 參考：《電鍍與精飾》2014年11期

【摘要】：通過赫爾槽試驗、偏轉法、安時法等多種方法,測試了國內外市場上6種品牌硫酸鎳所得鍍鎳層外觀、內應力,鍍液的電流效率、分散能力、整平能力及覆蓋能力等性能,并進行對比。結果顯示,金柯生產硫酸鎳產生的針孔少于其它品牌,配制鍍液無需預處理即可進行直接生產,其瓦特鎳液獲取鍍層內應力最小,鍍液分散能力、整平能力、覆蓋能力和電流效率稍優(yōu)于其它品牌硫酸鎳。
[Abstract]:By means of Hull tank test, deflection method and amperometric method, the appearance, internal stress, current efficiency, dispersion ability, leveling ability and covering ability of nickel plating layer obtained from six brands of nickel sulfate in domestic and foreign markets were tested. And compare it. The results show that the pinholes produced by Jinke nickel sulfate production are less than those produced by other brands, and the nickel bath can be produced directly without pretreatment. The nickel Watt solution can obtain the minimum internal stress, the dispersion ability and the leveling ability of the plating solution. Coverage and current efficiency are slightly better than other brands of nickel sulfate.
【作者單位】： 金柯有色金屬有限公司;
【基金】：高校合作項目(項目編號2012-01-060)
【分類號】：TQ153.12

【共引文獻】

相關期刊論文 前10條

1 梁劍濤;劉祥萱;王煊軍;;鋁活化塑料表面化學鍍銅新工藝研究[J];工程塑料應用;2007年01期

2 沈藝程;續(xù)振林;趙雄超;辜志俊;;激光表面處理對陶瓷基底化學鍍銅層結合力的影響[J];中國表面工程;2006年04期

3 肖發(fā)新;曹島;孟志廣;毛建偉;楊滌心;申曉妮;;添加劑對PCB酸性銅鍍層質量及鍍液性能影響[J];中國表面工程;2011年02期

4 吳贛紅;李德良;董坤;曹t，

本文編號：1971144