　　Composite films of different contents were prepared by Fe_73.5Cu₁Nb₃Si_13.5B₉ powder as compound phase and silicone rubber as matrix phase.The thickness of film is 200 um.Values of impedance,Z,under pressure stress were measured by TH2816 LCR digital bridge.LYYL-500 N high-grade-type microcomputer control pressure testing machine was used to conduct program control loading with a speed of 0.1 mm·min^-1.The results show that composite...