本文選題：電暈放電 + 印刷特性��； 參考：《包裝工程》2016年15期

【摘要】：目的確定SiO_x阻隔材料的電暈特性與印刷特性,研究其電暈處理規(guī)律以及印刷色彩再現(xiàn)的能力。方法采用磁控共濺射方法在PET表面制備不同含量SiO_x的復(fù)合阻隔材料,并采用電暈放電進(jìn)行處理,利用接觸角表征電暈放電后表面狀態(tài)的變化;采用彩色噴墨打印方式,對處理后的復(fù)合薄膜表面進(jìn)行印刷測試。結(jié)果 SiO_x質(zhì)量分?jǐn)?shù)較小時不具備抗電暈特性,當(dāng)SiO_x質(zhì)量分?jǐn)?shù)達(dá)到50%左右時,即產(chǎn)生了抗電暈?zāi)芰�。結(jié)論印刷測試結(jié)果表明,經(jīng)過電暈處理的復(fù)合薄膜色彩再現(xiàn)良好,可直接進(jìn)行印刷。
[Abstract]:Objective to determine the corona characteristics and printing characteristics of SiO_x barrier material, and to study its corona treatment law and printing color reproduction ability.Methods the composite barrier materials with different contents of SiO_x were prepared on the surface of PET by magnetron co-sputtering, and treated by corona discharge. The change of surface state after corona discharge was characterized by contact angle, and color inkjet printing was used.The surface of the treated composite film was printed and tested.Results when the mass fraction of SiO_x was small, the corona resistance was not found. When the mass fraction of SiO_x was about 50%, the ability of anti-corona was produced.Conclusion the results of printing test show that the color reproduction of the composite film after corona treatment is good and can be directly printed.
【作者單位】： 廣州科技職業(yè)技術(shù)學(xué)院;哈爾濱商業(yè)大學(xué);
【基金】：國家自然科學(xué)基金青年科學(xué)基金(51302054) 黑龍江省青年科學(xué)基金(QC2012C008) 黑龍江省自然科學(xué)基金(E201356) 哈爾濱商業(yè)大學(xué)創(chuàng)新項(xiàng)目(201510240113)
【分類號】：TB484

【相似文獻(xiàn)】

相關(guān)期刊論文 前6條

1 陳雁;葉建斌;謝劍翔;;紫外檢測技術(shù)在電暈放電檢測中的應(yīng)用[J];廣東電力;2008年09期

2 劉強(qiáng),翁明,詹偉;電暈風(fēng)干燥實(shí)驗(yàn)的研究[J];真空電子技術(shù);2004年01期

3 金明劍,孫鷂鴻;不同參數(shù)條件下水中脈沖放電的電學(xué)特性研究[J];高電壓技術(shù);2004年07期

4 李學(xué)文;李義鵬;孫立富;張婷婷;;粉體同軸柱形電極放電性能分析[J];廣東工業(yè)大學(xué)學(xué)報;2011年03期

5 張欽芝;新型日間電暈探測照相機(jī)[J];國際電力;2001年02期

6 ;[J];;年期

，

本文編號：1773761