本文選題：建材放射性 + 樣品粒徑　； 參考：《核電子學(xué)與探測技術(shù)》2015年10期

【摘要】：為提高檢測建筑材料中放射性核素~(232)Th、~(226)Ra、~(40)K含量的準(zhǔn)確性,利用低本底NaI(TI)γ譜儀就樣品的粒徑、含水量、封樣時間對檢測結(jié)果的影響進行了實驗研究。結(jié)果表明:樣品粒徑、含水量、封樣時間影響建材中放射性核素含量和內(nèi)、外照射系數(shù)測量數(shù)據(jù),且內(nèi)、外照射系數(shù)隨樣品條件變化呈現(xiàn)一定變化的規(guī)律;當(dāng)樣品滿足粒徑小于0.16 mm、含水量0%、封樣時間不小于10 d的條件時,測量的結(jié)果能夠較好地反映建材的放射性;如果不滿足條件,則應(yīng)該對測量的數(shù)據(jù)進行相應(yīng)的修正。
[Abstract]:In order to improve the accuracy of detecting the content of radionuclide 232T 226K in building materials, the effect of sample size, water content and sealing time on the detection results was studied by using a low background NaII-TI 緯 spectrometer. The results show that the particle size, water content and sealing time of the samples affect the radionuclide content and the internal and external radiation coefficients of building materials, and the internal and external radiation coefficients vary with the sample condition to a certain extent. When the size of the sample is less than 0.16 mm, the water content is 0 and the sealing time is not less than 10 days, the measured results can well reflect the radioactivity of the building materials; if the conditions are not satisfied, the measured data should be corrected accordingly.
【作者單位】： 南華大學(xué)核科學(xué)技術(shù)學(xué)院;
【基金】：國家級大學(xué)生創(chuàng)新創(chuàng)業(yè)訓(xùn)練計劃項目(201410555009)資助
【分類號】：TU502

【相似文獻】

相關(guān)期刊論文 前1條

1 段志剛;李清玉;王曉艷;曾凌云;;Sol-gel法不同工藝路線制備TiO_2的實驗研究[J];實驗室科學(xué);2013年02期

相關(guān)碩士學(xué)位論文 前1條

1 呂林林;納米氧化鋅的制備、摻雜及性能研究[D];中南大學(xué);2009年

，

本文編號：1890595