本文選題：混凝土　切入點：鹽漬土　出處：《應(yīng)用基礎(chǔ)與工程科學(xué)學(xué)報》2017年04期 　論文類型：期刊論文

【摘要】：對不同組混凝土試件在多種情況下進行了耐久性試驗,結(jié)合試驗數(shù)據(jù)選取試件的相對質(zhì)量評價參數(shù)和相對動彈性模量評價參數(shù)作為評價指標(biāo),探究了混凝土的表觀損傷特征、相對質(zhì)量及相對動彈性模量的變化規(guī)律,同時對不同組混凝土試件取樣進行電鏡掃描、EDS能譜分析及化學(xué)成分測定,以揭示混凝土的微觀結(jié)構(gòu)及損傷劣化機理.研究結(jié)果表明,相對質(zhì)量評價參數(shù)和相對動彈性模量評價參數(shù)能直觀地表征混凝土的劣化過程;西寧鹽漬土地區(qū)混凝土的破壞形式為鹽分的化學(xué)腐蝕和物理結(jié)晶,化學(xué)腐蝕對混凝土劣化具有加速效應(yīng),二者相互作用使混凝土發(fā)生了嚴(yán)重的破壞,主要的腐蝕產(chǎn)物有石膏、碳酸鈣及硅灰石膏,特別地在西寧鹽漬土地區(qū)混凝土發(fā)現(xiàn)了更為危害的硅灰石膏型硫酸鹽侵蝕;西寧地區(qū)現(xiàn)場暴露混凝土已經(jīng)受到鹽漬土的侵蝕,其評價參數(shù)波動性變化,經(jīng)過1 230d的試驗還處于劣化初期.
[Abstract]:In this paper, durability tests of concrete specimens of different groups are carried out under various conditions. According to the test data, the relative quality evaluation parameters and the relative dynamic elastic modulus evaluation parameters of the specimens are selected as the evaluation indexes, and the apparent damage characteristics of concrete are explored. The changes of relative mass and relative dynamic modulus of elasticity were analyzed by scanning electron microscope (SEM) EDS spectrum analysis and chemical composition analysis to reveal the microstructure of concrete and the mechanism of damage deterioration. The relative quality evaluation parameters and the relative dynamic elastic modulus evaluation parameters can directly characterize the deterioration process of concrete, and the failure forms of concrete in Xining saline soil area are chemical corrosion of salt and physical crystallization. Chemical corrosion has an accelerated effect on the deterioration of concrete, and the interaction of the two causes serious damage to concrete. The main corrosion products are gypsum, calcium carbonate and wollastonite paste, the main corrosion products of which are gypsum, calcium carbonate and wollastonite paste. In particular, more harmful wollastonite gypsum sulfate erosion has been found in concrete in Xining saline soil area, and the field exposed concrete in Xining area has been eroded by saline soil, and its evaluation parameters fluctuate. After 1 230 days of test, it is still in the initial stage of deterioration.
【作者單位】： 蘭州理工大學(xué)甘肅省土木工程防災(zāi)減災(zāi)重點實驗室;西部土木工程防災(zāi)減災(zāi)教育部工程研究中心;
【基金】：國家自然科學(xué)基金項目(51168031,51468039)
【分類號】：TU528

【相似文獻】

相關(guān)期刊論文 前6條

1 楊仲元;王建林;;大氣曝露混凝土劣化試驗分析[J];山西建筑;2006年15期

2 侯云芬;吳越愷;;多因素耦合作用下混凝土劣化機理研究現(xiàn)狀[J];北京建筑工程學(xué)院學(xué)報;2013年01期

3 劉運華;;混凝土劣化與滲透性相關(guān)性研究[J];鐵道科學(xué)與工程學(xué)報;2006年01期

4 王國英;;混凝土劣化分析與提高耐久性措施[J];科技創(chuàng)業(yè)家;2013年04期

5 胡毅;鞠成;;粉煤灰細度對混凝土劣化性能的影響[J];混凝土;2012年04期

6 李士彬;孫偉;;疲勞、碳化和氯鹽作用下混凝土劣化的研究進展[J];硅酸鹽學(xué)報;2013年11期

相關(guān)碩士學(xué)位論文 前1條

1 劉鑫;高原環(huán)境下混凝土劣化機理及施工質(zhì)量對其影響[D];西南交通大學(xué);2017年

，

本文編號：1643282