本文選題：可降解鎂合金支架 + 腹主動脈�。� 參考：《介入放射學(xué)雜志》2017年05期

【摘要】：目的觀察新型可降解鎂合金支架——MPM植入兔腹主動脈后降解時間及血管內(nèi)膜增生。方法 24只新西蘭大白兔隨機分為4組,每組6只,分別于距左腎動脈水平下1 cm腹主動脈處植入MPM支架各1枚。術(shù)后30、60、90、180 d分別復(fù)查腹主動脈造影,分離支架段血管進行觀察。采用SPSS20.0軟件對數(shù)據(jù)進行分析。結(jié)果 24只實驗兔在隨訪期間存活良好。植入支架逐漸降解,180 d時基本降解;血管內(nèi)膜增生,90 d時達峰值,整個降解過程血管通暢。結(jié)論可降解鎂合金支架MPM完全降解時間為182 d,可滿足血管正性重塑。
[Abstract]:Objective to observe the degradation time and intimal hyperplasia of new degradable magnesium alloy scaffolds (MPM) implanted into rabbit abdominal aorta. Methods Twenty-four New Zealand white rabbits were randomly divided into 4 groups with 6 rabbits in each group. MPM stents were implanted at the abdominal aorta 1 cm below the left renal artery level in each group. Abdominal aortography was performed 30 days after operation and stent segments were separated for observation. SPSS 20.0 software was used to analyze the data. Results 24 rabbits survived well during follow-up. The stents degraded basically at 180 d and reached the peak at 90 d after intimal hyperplasia. The whole degradation process was smooth. Conclusion MPM degradation time of degradable magnesium alloy scaffold is 182 d, which can satisfy positive vascular remodeling.
【作者單位】： 上海交通大學(xué)附屬第六人民醫(yī)院南院介入科;浙江省嘉興市第一醫(yī)院放射科;
【基金】：上海市科委醫(yī)學(xué)引導(dǎo)類項目(124119b1200) 上海市衛(wèi)生局科研項目(20124175)
【分類號】：R654.3

【相似文獻】

相關(guān)期刊論文 前8條

1 余匯洋;;損傷血管內(nèi)膜增生的研究[J];局解手術(shù)學(xué)雜志;2006年03期

2 王民生,陳中偉;生長因子與血管內(nèi)膜增生[J];中華創(chuàng)傷雜志;1994年05期

3 李濟宇;血管內(nèi)膜增生的治療進展[J];國外醫(yī)學(xué).外科學(xué)分冊;1998年04期

4 錢濟先,錢兆奇,黃耀添,李桂云,王劍波,胡佩珍,王軍,呂榮;含β射線的軟性血管外模型對移植血管內(nèi)膜增生及平滑肌增殖的抑制作用[J];中華醫(yī)學(xué)雜志;1999年01期

5 曲樂豐;反義技術(shù)治療血管內(nèi)膜增生的研究[J];國外醫(yī)學(xué)(創(chuàng)傷與外科基本問題分冊);2000年01期

6 裴斐;李俊彥;張莉;何蕊;;內(nèi)皮型一氧化氮合酶基因轉(zhuǎn)染對移植人工血管內(nèi)膜增生的作用(英文)[J];中國組織工程研究與臨床康復(fù);2008年40期

7 李超,李桂媛,張強,段志泉;一氧化氮對人培養(yǎng)血管內(nèi)膜增生的抑制作用[J];中華實驗外科雜志;2000年03期

8 ;[J];;年期

相關(guān)碩士學(xué)位論文 前1條

1 巢雄杰;金粉蕨素對大鼠頸動脈損傷后狹窄的早期預(yù)防作用的研究[D];南華大學(xué);2016年

，

本文編號：2053345