【摘要】：為提高納米纖維神經(jīng)移植物的接觸引導(dǎo),設(shè)計(jì)了一種含有取向納米纖維束的"芯鞘"型神經(jīng)移植物,它利用靜電紡高取向納米纖維膜,兩次卷繞形成"芯"和"鞘",最后通過(guò)靜電紡絲噴覆而成。利用掃描電鏡觀察并表征了纖維及其移植物形態(tài),測(cè)試了力學(xué)性能,將此移植物用于大鼠10mm坐骨神經(jīng)缺損,術(shù)后兩月通過(guò)體外刺激和組織學(xué)觀察了修復(fù)效果。結(jié)果表明:通過(guò)調(diào)整靜電紡收集轉(zhuǎn)輥轉(zhuǎn)速可獲得高取向聚乳酸納米纖維,納米纖維膜工程應(yīng)力和伸長(zhǎng)率達(dá)到(49.32±14.83)MPa和17.71%±0.06%,利用該膜構(gòu)建的神經(jīng)移植物縫合強(qiáng)力達(dá)到(1.18±0.40)N/針,能支持與保護(hù)神經(jīng)再生,移植兩月后,大鼠能夠感知熱與外力刺激,組織學(xué)觀察發(fā)現(xiàn),有神經(jīng)纖維和血旺細(xì)胞長(zhǎng)入神經(jīng)移植物,證明了該構(gòu)建技術(shù)的可行性,并有可能為神經(jīng)修復(fù)提供一種新的移植材料。
[Abstract]:In order to improve the contact guidance of nanofiber nerve graft, a "core sheath" type nerve graft containing orientation nanofiber bundles was designed. It spun the high orientation nanofiber membrane by electrostatic spinning and formed the "core" and "sheath" two times. Finally, it was spout by electrostatic spinning. The fiber and its graft morphology were observed and characterized by scanning electron microscope. The mechanical properties were tested and the graft was applied to the 10mm sciatic nerve defect in rats. The effect was observed by the external stimulation and histology two months after the operation. The results showed that the high orientation polylactic acid nanofibers could be obtained by adjusting the rotational speed of the rotor spinning, and the stress and elongation of the nanofiber membrane can reach (49.32 + 14.83) MPa and 17.71. It is% + 0.06%. The suture of the nerve graft constructed by this membrane can reach (1.18 + 0.40) N/ needle and can support and protect the nerve regeneration. After two months of transplantation, the rat can perceive the heat and external stimulation. The histological observation found that the nerve fibers and blood cells grow into the nerve graft, which proves the feasibility of the construction and may be the nerve. The repair provides a new type of graft material.
【作者單位】： 江蘇工程職業(yè)技術(shù)學(xué)院紡染工程學(xué)院;卑詩(shī)哥倫比亞大學(xué)材料工程系先進(jìn)纖維材料實(shí)驗(yàn)室;卑詩(shī)哥倫比亞大學(xué)醫(yī)學(xué)院動(dòng)物與外科學(xué)系;
【基金】：江蘇高校品牌專業(yè)建設(shè)工程(PPZY2015A093) 江蘇省先進(jìn)紡織工程技術(shù)中心項(xiàng)目(蘇政辦發(fā)2014[22]號(hào)) 江蘇高校優(yōu)秀中青年教師境外研修項(xiàng)目(蘇教師[2012]6號(hào)) 南通市新型纖維材料重點(diǎn)實(shí)驗(yàn)室項(xiàng)目資助(CP12014003)
【分類號(hào)】：R651;TQ340.64

【相似文獻(xiàn)】

相關(guān)博士學(xué)位論文 前6條

1 任勃;鎳鈷基氧化物納米纖維的靜電紡絲法制備及電化學(xué)性能研究[D];哈爾濱工程大學(xué);2014年

2 劉方;納米顆粒改性環(huán)氧樹(shù)脂及其復(fù)合材料力學(xué)性能研究[D];哈爾濱工程大學(xué);2014年

3 邵韋;稀土摻雜氟化物多層核殼納米晶上轉(zhuǎn)換和量子剪裁的研究[D];哈爾濱工業(yè)大學(xué);2017年

4 李大龍;介孔磷灰石基納米藥物控制釋放體系的構(gòu)建與生物學(xué)評(píng)價(jià)[D];哈爾濱工業(yè)大學(xué);2017年

5 楊桂欣;幾種納米功能材料的合成及成像、腫瘤治療性能研究[D];哈爾濱工程大學(xué);2015年

6 仲崇娜;核殼結(jié)構(gòu)上轉(zhuǎn)換稀土化合物納米晶的合成、發(fā)光性能及抗腫瘤研究[D];哈爾濱工程大學(xué);2014年

相關(guān)碩士學(xué)位論文 前6條

1 閆貴花;靜電紡制備聚丙烯腈/納米纖維素基多孔碳材料及電學(xué)性能研究[D];鄭州大學(xué);2017年

2 張路f，

本文編號(hào)：2005692