【摘要】：在組織工程支架表面沉積含有生長因子的絲蛋白層,通過絲蛋白β構(gòu)象轉(zhuǎn)變,固定生長因子于支架表面。研究此種生長因子負(fù)載方法對明膠多孔支架性能的影響,結(jié)果表明,因子負(fù)載前后支架的孔隙率皆達(dá)到90%以上,吸水量皆為干燥時支架質(zhì)量的18倍左右;力學(xué)測試表明,因子負(fù)載后支架的壓縮模量增加至26.1kPa;Elisa檢測表明,在各取樣時間點,每毫克支架緩釋活性EGF的量約在0.3~0.5ng之間,4周累積釋放活性EGF達(dá)到3.473ng;MTT實驗與SEM觀察表明,用此種方法負(fù)載因子于支架中,可以有效促進(jìn)支架中細(xì)胞的生長。
[Abstract]:The silk protein layer containing the growth factor is deposited on the surface of the tissue engineering scaffold, and the growth factor is fixed on the surface of the support through the conformational change of the silk protein. The effect of the loading method of the growth factor on the performance of the gelatin porous scaffold was studied. The results showed that the porosity of the support before and after the loading of the factor was over 90%, and the amount of water absorption was about 18 times the mass of the support at the time of drying; the mechanical tests showed that, The compressive modulus of the support after the factor loading was increased to 26.1 kPa; the Elisa test showed that, at each sampling time point, the amount of the sustained-release active EGF per mg of the stent was about 0.3 to 0.5 ng, and the cumulative release activity of EGF at 4 weeks reached 3.473 ng; and the MTT assay and the SEM observation showed that the loading factor of this method was in the stent, The growth of cells in the stent can be effectively promoted.
【作者單位】： 廣州醫(yī)科大學(xué)基礎(chǔ)學(xué)院生物醫(yī)學(xué)工程系;
【基金】：國家自然科學(xué)基金資助項目(50872099) 廣東省重大科技專項基金資助項目(2012A080203002) 廣州醫(yī)科大學(xué)博士人員科研資助項目(2012C17)
【分類號】：R318.08

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 王芋驍;孔志杰;黃溪;馬林;;交聯(lián)改性絲素蛋白材料制備和醫(yī)學(xué)應(yīng)用[J];現(xiàn)代絲綢科學(xué)與技術(shù);2013年05期

2 黃君霆;;家蠶基因組序列解讀10周年[J];蠶業(yè)科學(xué);2013年05期

3 胡戈亮;馬永剛;姚遙;王善文;;明膠-白芨膠/丹參多孔材料與大鼠組織相容性研究[J];湖北中醫(yī)藥大學(xué)學(xué)報;2013年06期

4 ZHANG LuZhong;ZHOU YouLang;LI GuiCai;ZHAO YaHong;GU XiaoSong;YANG YuMin;;Nanoparticle mediated controlled delivery of dual growth factors[J];Science China(Life Sciences);2014年02期

5 朱繼翔;陳曉明;彭曄;陽范文;田秀梅;何福坡;;負(fù)載絲裂霉素C的明膠多孔支架制備及釋放[J];合成材料老化與應(yīng)用;2014年02期

6 辛林偉;唐際存;李朝旭;李強;王黎明;;不同途徑注射鼠神經(jīng)生長因子對斷指再植術(shù)后感覺恢復(fù)的療效評估[J];實用醫(yī)學(xué)雜志;2013年19期

7 Huawei Liu;Weisheng Wen;Min Hu;Wenting Bi;Lijie Chen;Sanxia Liu;Peng Chen;Xinying Tan;;Chitosan conduits combined with nerve growth factor microspheres repair facial nerve defects[J];Neural Regeneration Research;2013年33期

8 LIU Bingjie;WANG Dongfeng;YU Guangli;MENG Xianghong;;Adsorption of Heavy Metal Ions,Dyes and Proteins by Chitosan Composites and Derivatives-A Review[J];Journal of Ocean University of China;2013年03期

9 陳格飛;賈小娜;鄭翔宇;孟清;;重組蜘蛛絲蛋白MiSp NT結(jié)構(gòu)域在不同pH環(huán)境下的Trp熒光光譜及圓二色譜分析[J];中國生物化學(xué)與分子生物學(xué)報;2014年01期

10 金洹宇;劉星;銀華;安艷;;絲素蛋白在生物醫(yī)用領(lǐng)域中的應(yīng)用[J];生物醫(yī)學(xué)工程學(xué)雜志;2014年01期

相關(guān)會議論文 前1條

1 蘇歡歡;孫華燕;高旭鵬;王鑫;徐風(fēng)華;;腦源性神經(jīng)營養(yǎng)因子復(fù)合導(dǎo)管對大鼠坐骨神經(jīng)損傷修復(fù)的研究[A];2013年中國藥學(xué)大會暨第十三屆中國藥師周論文集[C];2013年

相關(guān)博士學(xué)位論文 前2條

1 王宇清;PFTBA水凝膠促進(jìn)周圍神經(jīng)再生的效能及機制研究[D];第四軍醫(yī)大學(xué);2013年

2 楊小元;絲滌混構(gòu)小口徑人造血管的成型及性能研究[D];東華大學(xué);2014年

相關(guān)碩士學(xué)位論文 前10條

1 向杰;可吸收誘導(dǎo)神經(jīng)修復(fù)材料用于周圍神經(jīng)缺損的實驗研究及初步臨床應(yīng)用[D];南方醫(yī)科大學(xué);2012年

2 王寧;木材/羥基磷灰石骨替代復(fù)合材料的制備及研究[D];安徽大學(xué);2013年

3 張海衛(wèi);雷帕霉素、FK506對大鼠雪旺細(xì)胞增殖、遷移及相關(guān)蛋白表達(dá)影響的對比研究[D];南華大學(xué);2013年

4 李陽;殼聚糖復(fù)合膜上及移植部位黑素細(xì)胞的實驗研究[D];安徽醫(yī)科大學(xué);2013年

5 趙鵬程;低強度超聲對iPSCs源性神經(jīng)嵴干細(xì)胞增殖和分化的影響[D];重慶大學(xué);2013年

6 曾佳佳;赤泥改性及其與殼聚糖復(fù)合吸附Cr（Ⅵ）的研究[D];廣西大學(xué);2013年

7 胡輝;新型神經(jīng)導(dǎo)管復(fù)合材料與骨髓間充質(zhì)干細(xì)胞用于周圍神經(jīng)缺損的基礎(chǔ)研究[D];南方醫(yī)科大學(xué);2013年

8 張敏;丙氨瑞林PLGA微球緩釋給藥系統(tǒng)的研究[D];第二軍醫(yī)大學(xué);2013年

9 馬驍;靜電紡絲制備PLGA三維組織工程支架的研究[D];大連醫(yī)科大學(xué);2013年

10 蘇歡歡;腦源性神經(jīng)營養(yǎng)因子復(fù)合導(dǎo)管對大鼠坐骨神經(jīng)損傷修復(fù)的影響[D];河北北方學(xué)院;2013年

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 李U，

本文編號：2452745