本文選題：苯扎氯銨 + 度米芬��； 參考：《鄭州大學》2017年碩士論文

【摘要】：本文的主要研究內(nèi)容分為以下三個部分:第一部分,以表面活性離子液體[C16MIm]Br(十六烷基三甲基咪唑溴鹽)對HZSM-5A型沸石進行負載,得到改性沸石SMZ。以此改性分子篩為載體,DOP為增塑劑制備了PVC膜磷酸一氫根(HPO42-)選擇性電極,最佳膜組成為w(增塑劑)w:(PVC):w(載體)=65:30:5,膜電極對HPO42-表現(xiàn)出良好的響應性。電極的響應范圍為1.0×10-2~1.0×10-9 mol/L,響應斜率為-24.7 mV/decade,檢測下限為4.09×10-10 mol/L。電極具有選擇性好、檢測限低的優(yōu)點,在使用過程中也表現(xiàn)出了良好的可行性。所研制的電極可以成功的應用于湖水、池塘水和自來水中磷的檢測。第二部分,以亞胺(C8H16-CH=NH,C10H20-CH=NH)為負載物來改性HZSM-5A型沸石,得到兩種改性分子篩SMZ-C8和SMZ-C10。以改性分子篩為載體,DOP為增塑劑制備了Pb2+選擇性電極,在w(增塑劑):w(PVC):w(載體)=65:30:5的配比下的膜電極的響應性能最好。膜電極對Pb2+的響應范圍分別為:1.0×10-2~1.0×10-6和1.0×10-3~1.0×10-8mol/L,響應斜率分別為25.89和28.57mV/decade,檢測下限分別為5.89×10-7和6.08×10-9 mol/L,電極對大部分的金屬陽離子具有抗干擾能力,可在一定的pH范圍內(nèi)使用。所研制的兩種電極可以成功地應用于湖水、池塘水和自來水中鉛離子含量的測定及土壤、化妝水、白酒和茶葉中鉛的含量的測定。第三部分,以苯扎氯銨(BKC)、度米芬(DB)為原料分別與四氟硼酸鈉(NaBF4)、四苯硼鈉(NaTPB)合成了兩種締合物[BK][BF4]和[DB][TPB],并以它們?yōu)檩d體,分別以DOP、DBP為增塑劑,研制了一種新的PVC膜[BK]、[DB]選擇性電極,最佳膜組成為:w(增塑劑):w(PVC):w(載體)=66:33:1。所制備的兩種膜電極對BKC、DB的響應范圍分別為:1.0×10-2~1.0×10-6mol/L、1.0×10-3~1.0×10-6mol/L,響應斜率分別為:55.74 mV/decade、53.49 mV/decade,檢測下限分別為:5.38×10-7 mol/L、4.39×10-7 mol/L。這兩種膜電極選擇性好,抗干擾能力強,且可在一定的pH范圍內(nèi)使用。所研制的電極可以成功的應用于紙巾、牛奶及眼藥水中BKC的檢測和度米芬含片中度米芬含量的測定。
[Abstract]:The main research contents of this paper are as follows: in the first part, the modified zeolite SMZZ was obtained by loading HZSM-5A zeolite with surfactant ionic liquid [C16MIm] Br( cetyltrimethyl imidazolium bromide salt). The modified molecular sieve was used as the carrier of DOP as plasticizer to prepare PVC membrane HPO _ 42-selective electrode. The optimum membrane composition was w (plasticizer w / PVC / w). The membrane electrode showed a good response to HPO _ 42-. The response range of the electrode is 1.0 脳 10-9 mol / L, the response slope is -24.7 MV / L, and the detection limit is 4.09 脳 10-10 mol / L. The electrode has the advantages of good selectivity and low detection limit. The electrode can be successfully applied to the determination of phosphorus in lake water, pond water and tap water. In the second part, two kinds of modified molecular sieves SMZ-C8 and SMZ-C10 were obtained by modifying HZSM-5A zeolites with imine C8H16-CHN NH (NH). The PB2 selective electrode was prepared with modified molecular sieve as the carrier and DOP as the plasticizer. The membrane electrode has the best response performance under the ratio of w (plasticizer w / w) PVC / w (carrier = 65: 30: 5). The response range of the membrane electrode to PB2 is 1.0 脳 10-2 (1.0 脳 10-6) and 1.0 脳 10-8 mol / L respectively, the response slope is 25.89 and 28.57 MV / L, the detection limits are 5.89 脳 10-7 and 6.08 脳 10-9 mol / L, respectively. The electrode has anti-interference ability to most metal cations and can be used in a certain pH range. The two kinds of electrodes can be successfully applied to the determination of lead ion content in lake water, pond water and tap water, as well as in soil, make-up water, liquor and tea. In the third part, two kinds of association complexes [BK] [BF4] and [DB] [TPB] were synthesized with sodium tetrafluoroborate (NaBF4) and sodium tetraphenylborate (NaBF4), respectively, using benzalkonium chloride (BKCX) and Dumifen (DBB) as raw materials. A new PVC membrane [BK], [DB] selective electrode was prepared using DOPN-DBP as plasticizer, respectively. The best membrane composition is: 1: 6: 33: 1. The response range of the two kinds of membrane electrodes to BKCnDB is 1.0 脳 10-6 mol / L = 1.0 脳 10-6 mol / L respectively, and the response slope is 55.74 MV / L / L, 53.49 MV / L / L, respectively, and the detection limit is: 5.38 脳 10 ~ (-7) mol / L ~ (4.39) 脳 10 ~ (-7) mol 路L ~ (-1), and the detection limit is: 5.38 脳 10 ~ (-7) mol / L ~ (-1) = 4.39 脳 10 ~ (-7) mol 路L ~ (-1), respectively. These two kinds of membrane electrodes have good selectivity, strong anti-interference ability and can be used in a certain pH range. The electrode can be successfully used for the determination of BKC in tissue, milk and eye drops and the determination of moderate mifen content in Dumifen buccal tablets.
【學位授予單位】：鄭州大學
【學位級別】：碩士
【學位授予年份】：2017
【分類號】：O657.1

【相似文獻】

相關(guān)期刊論文 前10條

1 焦曉娟;電極法測定水中氟化物的幾點體會[J];中國環(huán)境監(jiān)測;2002年05期

2 王樹藩;;電極事故分析及防斷方法[J];鐵合金;1988年03期

3 王延齡,王琦,張仕定;關(guān)于加罩電極罩作用機理的討論[J];光譜學與光譜分析;2003年06期

4 沈國勵,韓梅,劉虹,俞汝勤;維生素B_6選擇性電極的研究[J];高等學�；瘜W學報;1985年10期

5 潘玲;電極法測定糧食中氟的若干問題探討[J];江蘇環(huán)境科技;1994年01期

6 杜寶中,魯國民,薛力;以銻電極作參比電極測定廢水中硫化物[J];分析試驗室;2002年01期

7 王莉;于壽進;;水中氟化物電極法測定的改進[J];江蘇預防醫(yī)學;2007年03期

8 楊伯宇;李春塘;宦國禾;;賴氨酸細菌電極的研制和應用[J];離子選擇電極通訊;1984年04期

9 徐芬,沈國勵,俞汝勤,謝錦云,張梅芬;動物組織膜L-維生素C電極的研究[J];藥學學報;1990年05期

10 孫長清;許宏鼎;高茜;王成順;周慧;;雙酶麥芽糖電極的研制與應用[J];化學傳感器;1990年01期

相關(guān)會議論文 前9條

1 于海忠;;電極法測定氯離子濃度在大連地區(qū)的正常分布[A];中國輸血協(xié)會第四屆輸血大會論文集[C];2006年

2 張會剛;朱慶山;;改進的締合物模型優(yōu)化模擬KCl-MgCl_2,KCl-FeCl_2熔鹽體系[A];2004年全國冶金物理化學學術(shù)會議專輯[C];2004年

3 王雙強;白向茹;劉瑞麗;顏振寧;;以(4-溴-3-甲氧基苯)肼為載體的鉻離子選擇性電極的研制與應用[A];河南省化學會2012年學術(shù)年會論文摘要集[C];2012年

4 郭小麗;郭敏;王新東;;適用于深海研究的硫離子選擇性電極[A];第十三次全國電化學會議論文摘要集（下集）[C];2005年

5 屠月弦;;開發(fā)醫(yī)用離子選擇性電極為醫(yī)學生物學服務[A];首屆中國儀器儀表學會醫(yī)療儀器分會學術(shù)會議論文集[C];1993年

6 張楠;牛利;;一種安培式離子選擇性電極作為水相中鎘離子傳感器[A];中國化學會第28屆學術(shù)年會第10分會場摘要集[C];2012年

7 趙中一;姚宗江;方銳;趙麗華;;固相反射散射分光光度法測定碲[A];中國化學會第八屆多元絡(luò)合物會議論文[C];2002年

8 郭小麗;郭敏;王新東;;適用于深海探測的硫離子選擇性電極的制備及性能研究[A];2006年全國冶金物理化學學術(shù)會議論文集[C];2006年

9 張淼;林建涵;張彥娥;;基于離子選擇性電極的土壤硝態(tài)氮快速檢測方法研究[A];2007年中國農(nóng)業(yè)工程學會學術(shù)年會論文摘要集[C];2007年

相關(guān)博士學位論文 前10條

1 盧強;涂層鈦電極的制備及其降解廢水中硝基苯的研究[D];南京理工大學;2011年

2 畢強;電化學處理有機廢水電極材料的制備與性能研究[D];西安建筑科技大學;2014年

3 劉sチ，

本文編號：2012315