發(fā)布時間：2019-02-12 20:02

【摘要】：以加氫半焦為原料,利用下落床和固定床裝置,高溫水蒸氣活化直接制得廉價的活性焦,并對其進行高濃度和低濃度氣化廢水處理實驗.在優(yōu)化的制備條件下,分別考察了活化時間對活性焦吸附指標和廢水吸附性能的影響.結果表明:隨著活化時間由5s增加到120min,所制備活性焦的苯酚吸附值和碘值先增加后略微下降,總比表面和總孔容增加.未活化的加氫半焦吸附指標較低且廢水吸附效果較差.采用下落床活化,活化時間為5s時,活性焦吸附性能提高不明顯;而采用固定床活化,活性焦吸附性能明顯提高.當活化時間為90min時,活性焦的苯酚吸附值和碘值達到最大值,分別為97mg/L和588mg/L,總比表面積和總孔容分別可達675.53m2/g和0.631 2cm3/g.當活化時間30min時,自制活性焦對高低濃度氣化廢水中COD、總磷、TOC的去除率和吸附容量與市售活性焦相近,而活化時間在30min~120min范圍內(nèi)變動導致COD、總磷、TOC的去除率和吸附容量變化范圍均5%,活化時間對高低濃度氣化廢水中COD、總磷、TOC的去除率和吸附容量均影響不大.
[Abstract]:Low cost active coke was prepared from hydrogenated semi-coke by using falling bed and fixed bed device. The treatment of high concentration and low concentration gasification wastewater was carried out. Under the optimized preparation conditions, the effects of activation time on the adsorption index of activated coke and adsorption performance of wastewater were investigated. The results showed that with the increase of activation time from 5 s to 120 min, the phenol adsorption value and iodine value of the prepared active coke firstly increased and then decreased slightly, and the total specific surface and total pore volume increased. The adsorption index of unactivated hydrogenated semi-coke is low and the adsorption efficiency of wastewater is poor. When activated by falling bed, the adsorbability of activated coke was not improved obviously when activation time was 5 s, but that of activated coke with fixed bed was improved obviously. When the activation time is 90min, the phenol adsorption value and iodine value of activated coke reach the maximum value, which are 97mg/L and 588mg / L, respectively. The total specific surface area and total pore volume are up to 675.53m2/g and 0.631 cm ~ 3 / g, respectively. When the activation time is 30min, the removal rate and adsorption capacity of COD, in high and low concentration gasification wastewater from activated coke are similar to those of commercial activated coke. However, the change of activation time in the range of 30min~120min leads to the total phosphorus of COD,. The range of TOC removal rate and adsorption capacity is 5, and activation time has little effect on COD, total phosphorus, TOC removal rate and adsorption capacity in high and low concentration gasification wastewater.
【作者單位】： 新奧科技發(fā)展有限公司 煤基低碳能源國家重點實驗室;山東大學燃煤污染物減排國家工程實驗室;
【基金】：國家高技術研究發(fā)展計劃(863)項目(2011AA05A201)
【分類號】：O647.3;X784

【相似文獻】

相關期刊論文 前8條

1 王劍秋;王賢清;;顆粒頁巖半焦燃燒反應模型的研究[J];石油學報(石油加工);1987年03期

2 王賢清;王劍秋;錢家麟;朱亞杰;;油頁巖半焦燃燒中灰分層的擴散動力學研究[J];石油學報(石油加工);1987年04期

3 喬晉紅,趙煒,謝克昌;煤半焦吸附性的實驗研究[J];太原理工大學學報;2003年06期

4 王黎;木質(zhì)半焦的非催化及催化氣化[J];應用化學;1987年03期

5 易其國;張永光;齊方杰;肖波;李方華;;木質(zhì)生物燃料與其半焦的混燃實驗研究[J];環(huán)境科學學報;2014年09期

6 趙輝;周勁松;曹小偉;段玉燕;駱仲泱;岑可法;;生物質(zhì)半焦高溫水蒸汽氣化反應動力學的研究[J];動力工程;2008年03期

7 林民;王賢清;錢家麟;朱亞杰;;顆粒油頁巖半焦燃燒過程有效系數(shù)的研究[J];石油學報(石油加工);1990年01期

8 謝志平;權變利;;半焦催化甲烷轉化過程的動力學分析[J];天然氣化工(C1化學與化工);2009年04期

相關會議論文 前1條

1 張亞婷;云卉;王露;劉濤;周安寧;;神木半焦改性及其光催化性能的研究[A];中國化學會第29屆學術年會摘要集——第12分會：催化化學[C];2014年

相關博士學位論文 前1條

1 胡沔;半焦載Fe-Ni催化劑的制備及其對生物質(zhì)催化熱解的機理研究[D];華中科技大學;2015年

相關碩士學位論文 前4條

1 董珍;活性半焦負載Fe基氧化物催化還原NO的實驗研究[D];遼寧科技大學;2016年

2 云卉;神木半焦改性及其在CO_2光催化轉化過程中的應用研究[D];西安科技大學;2016年

3 李玉潔;半焦催化甲烷轉化過程中主要反應的熱力學和動力學分析[D];太原理工大學;2007年

4 張文華;生物質(zhì)焦油在半焦基催化劑下水蒸氣重整的研究[D];大連理工大學;2014年

，

本文編號：2420742