【摘要】：以木炭作為載體,固載水合氧化鐵,采用抽真空旋轉(zhuǎn)蒸發(fā)法制備鐵炭復(fù)合材料,通過比較不同制備條件下復(fù)合材料對水體中磺胺類抗生素的去除效果,對制備條件進(jìn)行優(yōu)化。并采用批量平衡試驗,研究了鐵炭復(fù)合材料對磺胺類抗生素的吸附去除特性。結(jié)果表明:以Fe(NO3)3溶液浸漬,鐵炭質(zhì)量比為0.224∶1,固化9 h條件下去除水體中磺胺類抗生素效果最佳;鐵炭復(fù)合材料對磺胺和磺胺吡啶的去除效果明顯優(yōu)于單一炭材料,鐵炭復(fù)合材料對磺胺和磺胺吡啶的去除率隨抗生素初始濃度增加而降低,酸性條件下磺胺和磺胺吡啶去除率高于中性和堿性條件,溶液中背景離子強(qiáng)度變化對磺胺和磺胺吡啶的去除影響較小;鐵炭復(fù)合材料對磺胺和磺胺吡啶的去除符合一級動力學(xué)模型,為物理化學(xué)吸附和化學(xué)降解的協(xié)同作用,且在反應(yīng)過程中生成中間產(chǎn)物。
[Abstract]:The iron-carbon composite was prepared by vacuum rotation evaporation with charcoal as carrier and supported on hydrated ferric oxide. By comparing the removal efficiency of sulfanilamide antibiotics in water under different preparation conditions, the preparation conditions were optimized. The adsorption and removal of sulfanilamide antibiotics by iron carbon composites were studied by batch equilibrium test. The results show that when Fe (NO3) 3 solution is impregnated, the ratio of iron to carbon is 0.224: 1, and the curing time is 9 h, the removal efficiency of sulfanilamide and sulfamyridine in water is the best, and the removal efficiency of iron carbon composite is better than that of single carbon material. The removal rate of sulfanilamide and sulfampyridine decreased with the increase of the initial concentration of antibiotics, and the removal rate of sulfaniline and sulfamyridine in acidic condition was higher than that in neutral and alkaline condition. The removal of sulfanilamide and sulfampyridine by iron-carbon composites was in accordance with the first-order kinetic model, which was the synergistic effect of physicochemical adsorption and chemical degradation. And the intermediate product is formed in the reaction process.
【作者單位】： 安徽農(nóng)業(yè)大學(xué)資源與環(huán)境學(xué)院;安徽農(nóng)業(yè)大學(xué)生物技術(shù)中心;農(nóng)田生態(tài)保育與污染防控安徽省重點實驗室;
【基金】：國家自然科學(xué)基金(41471405) 農(nóng)田生態(tài)保育與污染防控安徽省重點實驗室開放基金資助項目(FECPP201705)
【分類號】：TQ424;X52

【相似文獻(xiàn)】

相關(guān)期刊論文 前4條

1 孫鴻;張穩(wěn)嬋;王紅霞;崔杏雨;;煤矸石制備沸石-活性炭復(fù)合材料的吸附性能研究[J];應(yīng)用化工;2008年06期

2 于捷;新洗滌劑“SAS”[J];化學(xué)世界;1963年11期

3 松岡秀男;金郁靜;;表面活性劑SAS的技術(shù)發(fā)展[J];日用化學(xué)品科學(xué);1990年06期

4 曹愛麗;黃積濤;王憲;楊裴;高偉;王彥;;丙烯酸(AA)——丙稀磺酸鹽(SAS)共聚物吸水劑的研制[J];天津理工學(xué)院學(xué)報;1991年02期

相關(guān)會議論文 前1條

1 孫鴻;張穩(wěn)嬋;王紅霞;馬靜紅;梁海天;李瑞豐;;沸石-活性炭復(fù)合材料的吸附性能研究[A];第十三屆全國催化學(xué)術(shù)會議論文集[C];2006年

相關(guān)碩士學(xué)位論文 前3條

1 謝非;功能活性炭復(fù)合材料的制備及水處理應(yīng)用[D];合肥工業(yè)大學(xué);2016年

2 葉先鋒;活性氧化鋁/活性炭復(fù)合材料的研制[D];福州大學(xué);2011年

3 譚建冬;由煤矸石和瀝青為原料制備FAU沸石/活性炭復(fù)合材料[D];太原理工大學(xué);2010年

，

本文編號：2181394